水相锌二次电池正极材料V2O5/C的电化学性能研究

采用溶胶－凝胶法合成了一种V₂O₅/C复合材料.扫描电镜（SEM）和红外光谱（FTIR）分析表明,这是一种外层V₂O₅胶体包覆内层乙炔分子的多孔复合材料.以V₂O₅/C作正极,锌片为负极,Zn(ClO₄)₂溶液为电解质组成水相锌二次电池,采用循环伏安（CV）和电化学阻抗谱（EIS）等方法研究发现:V₂O₅:C质量比为1:1时电极具有最好的电化学性能,电池开路电压达1.64 V; Zn^2＋能分别在1.01 V和1.26 V处分步嵌入V₂O₅/C结构中A、B两种位置,其嵌入电流密度峰值最高可达70 mA•g^－1,并且具有较好的循环充放电性能;在一定放电深度下,V₂O₅/C电极反应速率受Zn^2＋的扩散过程控制.     

Organic phase conversion of bulk (wurtzite) ZnO to nanophase (wurtzite and zinc blende) ZnO

We describe the all-organic phase conversion of bulk commercial ZnO in the wurtzite modification to sub-30 nm ZnO that we find to be partially in the zinc blende [, a=4.568(3) Å] modification. The conversion involves refluxing ZnO in 2,4-pentanedione (acetylacetone) at 413 K to form the zinc 2,4-pentanedionate, which is decomposed by heating at 573 K in an appropriate high-temperature solvent such as dibenzylether to form nanophase ZnO. This nanophase, partially zinc blende ZnO can also be obtained in a single step by heating commercial zinc 2,4-pentanedionate in refluxing dibenzylether. Thermodiffractometry suggests that the conversion of zinc blende ZnO to wurtzite ZnO commences near 650 K.     

Phase Relations in the Ni–Mn–Ga Ternary System and Aging Effect on Shape Memory Properties of Ferromagnetic Ni<Subscript>2</Subscript>MnGa Sputtered Films

Summary. Isothermal sections of the Ni–Mn–Ga ternary phase diagram at 1073 and 1273 K were investigated over a wide range of alloy compositions. The range of the β-Ni₂MnGa phase, its equilibria with the γ-(Mn, Ni), α′-Ni₃Ga, and γ-Ni₃Ga₂ phases, and the liquidus and solidus lines were determined experimentally. The aging effect on the shape memory effect (SME) of Ni₂MnGa sputtered films was also investigated. The two-way SME of the constraint-aged films was confirmed by the temperature change.     

An efficient route to regioselective opening of N-tosylaziridines with zinc(II) halides

An efficient route for the regio- and stereoselective ring opening of N-tosylaziridines with zinc dihalides (ZnX₂, X = Cl, Br, I) is described. Depending on the solvent and Zn(II) halide, β-halo amines or imidazolines are obtained selectively in good to excellent yields.     

Zinkkomplexe eines neuen N,N, O‐Liganden

Zinc Complexes of a New N, N, O Ligand The tridentate ligand N, N(2‐dimethylaminoethyl)‐3, 5‐di‐tert.‐butyl‐salicylaldimine ( L H) results from the corresponding salicylic aldehyde and N, N‐dimethyl ethylenediamine. With zinc salts it forms the mononuclear halide complexes [ L ZnCl ˙ CH₃OH] ( 1 ) and [ L ZnI ˙ CH₃OH] ( 2 ) and the presumably polymeric acetate [ L ZnOCOCH₃] ( 3 ). With diethyl zinc and diphenylphosphoric acid it yields the phosphate complex [ L Zn‐OPO(OPh)₂ ˙ CH₃OH] ( 4 ). The coordination of the complexes, which is between trigonal bipyramidal and square pyramidal, and the character of the five donors in the phosphate complex represent the transition state of a hydrolytic substrate cleavage in a zinc enzyme.     

Mechanosynthesis of zinc ferrite in hardened steel vials: Influence of ZnO on the appearance of Fe(II)

Nanocrystalline ZnFe₂O₄ spinel powders are synthesized by high-energy ball milling, starting from a powder mixture of hematite (α-Fe₂O₃) and zincite (ZnO). The millings are performed under air using hardened steel vials and balls. X-ray diffraction and Mössbauer spectrometry are used to characterize the powders. A spinel phase begins to appear after 3 h of milling and the synthesis is achieved after 9 h. Phase transformation is accompanied by a contamination due to iron coming from the milling tools. A redox reaction is also observed between Fe(III) and metallic iron during milling, leading to a spinel phase containing some Fe(II). The mechanism for the appearance of this phase is studied: ZnO seems to have a non-negligeable influence on the synthesis, by creating an intermediate wüstite-type phase solid solution with FeO.     

STUDIES ON THE PREPARATION OF ZINC-CONTAINING ACTIVATED CARBON FIBERS AND THEIR ANTIBACTERIAL ACTIVITY

1. INTRODUCTION Microbial pollution will bring about various problems in industry and other vital fields, such as causing decomposing of materials, harming people抯 health. In order to reduce these problems, new antibacterial materials have been demanded. Recently, much attention has been paid to inorganic materials including zinc oxide [1~4]. These inorganic antibacterial materials are now substituting for organic materials to avoid releasing noxious organic molecules harmful to humans;…     

现场表面拉曼光谱研究Fe-Mo合金诱导共沉积

现场表面拉曼光谱结果显示，在0．2mol·L-1Na2MoO4,pH＝4．0的溶液中，电位正于0．5V（vsSCE）时只观察到多钼酸盐的拉曼峰（940、880和450cm-1）．负于-0．5V时，出现中心位于730cm-1的宽峰．同时电极表面有蓝色膜生成．表明混合氧化态（MO（Ⅳ），MO（Ⅴ））氧化膜的形成．730cm-1的峰在-1．9V时仍然存在，说明氧化膜没有被进一步还原．在钼酸钠溶液中同时含有0．1mol·L-1FeSO4和0．2mol·L-1柠檬酸时，中间态氧化膜的拉曼峰的中心移到740cm-1．且峰强度随着电位从-1．3V负移到-1．9V而逐渐减弱并最终消失．电极表面沉积层呈银白色，说明由于Fe2 的存在，钼的中间态氧化膜的结构发生了变化，能够被进一步还原形成Fe－Mo合金，表现出诱导共沉积的特征．     

药物对微量元素锌吸收的影响

综合分析近年来有关的中外文献资料，讨论了临床常用药物对肠道锌吸收的影响及其意义。有十几类药物会对锌吸收产生影响。药物对锌吸收的影响在营养学及其临床上有重要意义，其中对锌吸收的抑制可能是锌缺乏的原因之一。     

Preconcentration and separation of iron, zinc, cadmium and mercury, from waste water using Nile blue a grafted polyurethane foam

The present work describes a novel method for the incorporation of Nile blue A into polyurethane foam matrix. This foam material was found to be very suitable for the extraction of metal ions from aqueous solutions. The characterization of Nile blue A grafted foam and the effect of halide concentration, pH, shaking time, extraction isotherm and capacity have been investigated. This foam material was found to be suitable for the separation and preconcentration of iron (III), zinc (II), cadmium (II) and mercury (II) from waste water. The extraction was accomplished in (15-20) minutes. Iron was separated from acid medium (2-4 M HCl), zinc from (3-5 M HCl), cadmium from (4-6 M HCl) as thiocyanate complexes and mercury was separated from (1-2 M HCl) as chloride.