Thermal Stability Of Folic Acid in the solid-state

This study attempts to identify the degradative process which folic acid undergoes in the solid-state under thermal stress. In order to facilitate the process, the various pieces of the chemical structure, namely, p-amino benzoic acid, pterin and glutamic acid as both its d- and l-isomers were investigated as separate entities. These structured solid-state pieces were then compared to the composite solid state folic acid degradative curves in order to identify the peaks seen and provide direction for the interpolation of the degradative mechanism. It was observed that none of the structural pieces could be superimposed as assumed earlier and hence an attempt was made to identify the decomposition products using various analytical techniques such as infrared spectroscopy, mass spectroscopy and X-ray diffraction which suggested that the glutamic acid fragment is lost first as evidenced by acid loss and amide enhancement in the IR spectra. The vitamin was ultimately degrading to carbon fragments and that further identification was not necessary. This revised version was published online in August 2006 with corrections to the Cover Date.     

Comparison of the thermal behavior of three cellulose fibers mercerized or submitted to solar degradation

Comparison of Lyocell, modal and viscose fibers was performed by means of differential scanning calorimetry, thermogravimetry and scanning electron microscopy. Thermal analysis was performed in air atmosphere. Samples were mercerized (21.3 g 100 mL-1) or submitted to solar radiation (seven months). Solar degraded samples presents a higher thermal stability and are initially less degraded. Furthermore, Lyocell fiber is the most stable under thermal degradation conditions. Heating produces a reduction of the fiber diameter (about 50%). This revised version was published online in July 2006 with corrections to the Cover Date.     

Identification of a chemical indicator of the rupture of 1,4-β-glycosidic bonds of cellulose in an oil-impregnated insulating paper system

In this study, headspace gas chromatography/mass spectrometry has been used to assess the volatile by-products generated by the ageing of oil-impregnated paper insulation of power transformers. Sealed-glass ampoules were used to age under oxidative conditions 0.5-g specimens of insulating paper in 9 mL of inhibited mineral oil in a temperature range of 60–120 °C and moisture of 0.5, 1 and 2% (w/w). A linear relationship between one of the oil-soluble degradation by-products, i.e. methanol, and the number of ruptured 1,4-β-glycosidic bonds of cellulose, regardless of the type of paper (ordinary Kraft or thermally-upgraded (TU) Kraft paper), was established for the first time in this field. Ageing at 130 °C of model compounds of the Kraft paper constituents (α-cellulose, hemicellulose and lignin) and two cellulosic breakdown by-products (D-(+)-glucose and 1,6-anhydro-β-d-glucopyranose) confirmed that the α-cellulose degradation was mostly responsible for the presence of this molecule in the system. Furthermore, additional 130 °C-tests with six different papers and pressboard samples under a tight control of initial moisture indicated that at least one molecule of methanol is formed for each rupture of 1,4-β-glucosidic bond of the molecular chains. Stability tests showed that the ageing indicator is stable under the oxygen and temperature conditions of open-breathing transformers. The presence of methanol was detected in 94% of oil samples collected from over than 900 in-service pieces of equipment, confirming the potential for this application. Lastly, the tests have shown that oil-oxidation by-products and TU-nitrogenous agents modify the methanol partitioning coefficients in the paper/oil/air system, which makes their study essential over a range of field conditions encountered by power transformers. Results are presented and discussed in comparison with 2-furfuraldehyde, which is the current reference in the domain.     

Enzymatic degradation of highly phenolic lignin-based polymers (lignophenols)

Enzymatic degradation of two lignin-based polymers (lignophenols), lignocatechol and lignocresol, prepared by selectively grafting catechol and p-cresol to C_α positions of lignin, respectively, were carried out in aqueous organic solvents. Both lignophenols showed high reactivity in the peroxidase-catalyzed oxidation. Structural analyses by NMR spectroscopies revealed that the degraded lignophenols contained aliphatic chain content, which might be mainly formed in the reduction of the intermediate initially generated by the aromatic ring cleavage. Lower amount of aromatic units in the lignophenols after degraded by peroxidase also indicted the cleavage of aromatic rings. Due to the substitution of phenols at C_α positions of lignin, the degraded lignophenols did not have carbonyl structure, which was abundant in the biodegradation products of native lignin. The two lignophenols were also degraded by Rhus vernicifera laccase. But the degree of degradation was lower than that of the degradation by peroxidase, which might be due to the low activity of laccase on the lignin moieties in lignophenols.     

Size exclusion chromatographic characterization of sodium hyaluronate fractions prepared by high energetic sonication

Summary A high molecular weight sodium hyaluronate isolated from rooster combs was degraded by ultrasonication. High-performance size exclusion chromatography allowed rapid and accurate determination of molecular weight parameters (M_z, M_w, M_n) and distributions. The time dependence of hyaluronan ultrasonication to the molecular characteristics of the polymer was investigated. A non-random nature of the degradation process was demonstrated and the reciprocal M_n value was found to be linearly proportional to the time of ultrasonication.     

芥子气模拟剂2-氯乙基乙基硫醚的光催化降解

利用连续流动微反、原位红外和GC/MS等手段考察了芥子气模拟剂2-氯乙基乙基硫醚（2-CEES）在P25 TiO2上的光催化降解反应,证实CO2和H2O是这个反应的最终产物.详细的跟踪分析表明,除了CO2和H2O外,在反应的气相混合物中可检测到C2H4、CH3CHO、CH4、CO、HCl和H2S；少量小分子的羧酸、醚和砜；微量C2H5SC2H5、C2H5S2C2H5、C2H5SC2H4Cl和CH2ClCH2Cl等中间产物;在反应后的催化剂表面可检测到C2H5S2C2H5、C2H5SC2H4OH、C4H9S2C2H5和C2H5S2C2H4OH、等物.根据这些结果提出了2-CEES光催化降解的反应机理,推断2-CEES的光催化降解涉及脱氯、C－S键断裂、有机硫化物光聚合和裂解等复杂过程最终转化为CO2和H2O.认为各种硫物种在表面的积聚引起了催化剂的缓慢失活.     

Thermal degradation of wood treated with guanidine compounds in air: Flammability study

Wood has been treated with guanidine phosphate, guanidine nitrate, guanidine carbonate and guanidine chloride to impart flame retardancy. The samples were subjected to differential thermal analysis (DTA) and thermogravimetry (TG) from ambient temperature to 800°C in air to study their thermal behaviors. From the resulting data, kinetic parameters for different stages of thermal degradation were obtained following the method of Broido. For the decomposition of wood and flame retardant wood, the activation energy was found to decrease from 116 to 54 kJ mol^–1; the char yield was found to increase from 5.6 to 34.9%, LOI from 18 to 41.5, which indicated that the flame retardancy of treated wood was improved. Effects of the different compounds on the degradation and flammability of wood have also been proposed.This revised version was published online in November 2005 with corrections to the Cover Date.     

FTIR-ATR技术研究聚氨酯类文物保护材料的光降解

Polyurethanes are one kind of relic protection materials commonly used. During artificial photo-ageing, three polyurethanes, HDI-based polyurethane, MDI-based polyurethane and TDI-based polyurethane, have been considered to undergo UV radiation. Photochemical degradation of the polyurethanes has been monitored by means of Fourier transform infrared spectroscopy with attenuated total reflection accessory （FTIR-ATR）. It was proved that the mechanism of the photochemical degradation of polyurethanes might be the scissions of carbamate （urethane） groups and the re-reactions of radical groups formed in the scission reactions. From the experiment results HDI-based polyurethane, an aliphatic diisocyanate, could be considered to be more suitably used as relic protection materials among these three polyurethanes for its ageing products with less color.     

Study on flame-retardant mechanism of polycarbonate containing sulfonate-silsesquioxane-fluoro retardants by TGA and FTIR

The flame retardancy of bisphenol A polycarbonate (PC) containing potassium diphenylsulfone sulfonate (KSS), poly(aminopropyl/phenylsilsesquioxane) (PAPSQ) and poly(vinylidenefluoride) (PVDF) was measured by limited oxygen index (LOI) and examined according to UL94. A high LOI and UL94 V-0 rating for 1.6 mm thickness samples were obtained by a combined use of equivalent KSS, PAPSQ and PVDF at 0.1-0.3 wt% loading, respectively. The improvement in flame retardancy of PC compositions arose from the synergistic interaction of three additives. Thermogravimetric analysis (TGA) indicated that the combination decreased the activation energy (E) of PC degradation and elevated the thermal degradation rate of PC to ensure the formation of an insulating carbon layer. FTIR analysis showed that the LOI char of PC containing the three additives took on a highly cross-linking aromatic ester and ether structure.     

Thermal characterization and thermal degradation of poly(norbornene-2,3-dicarboxylic acid dialkyl esters) synthesized by vinyl addition polymerization

The thermal properties and degradation behaviors of poly(norbornene-2,3-dicarboxylic acid dialkyl esters) (PNB-dialkyl esters) (alkyl = Me (PNB-Me), Et (PNB-Et), Pr (PNB-Pr), and Bu (PNB-Bu)) were investigated by thermogravimetric analysis (TGA) in dynamic conditions and by infrared (IR) spectroscopy. The PNB-dialkyl esters show good thermal stability up to 350 °C, and the thermal stability decreases in the order Me > Et > Pr > Bu with the increase in size of side chain. The effect of side-chain size on the thermal degradation behaviors of PNB-dialkyl esters is evidenced by one-step thermal degradation profile for PNB-Me while two-step thermal degradation profile for PNB-Et, PNB-Pr, and PNB-Bu. Transformation is deduced to undergo β-hydrogen elimination and formation of anhydride group in the first stage of thermal degradation reaction according to TGA and IR results for PNB-Et, PNB-Pr, and PNB-Bu. The apparent activation energy and thermal degradation model of PNB-dialkyl esters are estimated by means of Ozawa-Flynn-wall method and Phadnis-Deshpande method, respectively.