退火时间对MgB_2超导薄膜的影响

在多晶A l2O3衬底上,以B2H6作为硼源,化学气相沉积先驱B薄膜,采用Mg扩散方法,在不同退火时间条件下制备了MgB2超导薄膜。通过电阻-温度曲线测量、X射线衍射分析和扫描电子显微镜形貌观测方法,研究了退火时间对MgB2薄膜的超导特性、晶体结构、表面形貌的影响。     

Tune optimization of the third generation light source storage ring based on Frequency Map Analysis

Tune optimization is necessary to optimize the nonlinearity of the third generation light source storage ring. In this paper we summarize the common strategies for choosing a tune and discuss tune op-timization. Frequency Map Analysis (FMA) is applied as a tune scanning tool to reveal information about nonlinear resonances and guide the tune optimization. The Shanghai Synchrotron Radiation Facility (SSRF) storage ring is taken as a test lattice, and the optimum solutions are presented in this paper. Moreover, the third order regular structural resonances excited by sextupoles are particularly investigated, and it is found that these resonances distort the tune shifts with amplitude and show a stop-band like the linear structural resonances.     

Preparation and characterization of Fe3O4 magnetic composite microspheres covered by a P(MAH-co-MAA) copolymer

A magnetic core–shell-layered polymer microsphere (MPS) was successfully synthesized by a dispersion polymerization route, where the modified Fe₃O₄ nanoparticles (MFN) were used as a core, while poly(maleic anhydride-co-methacrylic acid) P(MAH-co-MAA) as a shell was covered on the surface of the Fe₃O₄ nanoparticles. Environmental scanning electron microscope (ESME) and transmission electron microscope (TEM) measurements indicate that the magnetic P(MAH-co-MAA)/Fe₃O₄ composite microspheres assume sphericity and have a novel core–shell-layered structure. The crystal particle sizes of the unimproved Fe₃O₄ and the MFN samples vary from 8 to 16 nm in diameter, and the average size is about 10.6 nm in diameter. The core–shell magnetic composite microspheres can be adjusted by changing the stirring speed. Since multiple Fe₃O₄ cores were coated with a proper percentage of P(MAH-co-MAA) copolymers, and therefore lower density was acquired for the MPS, which improved sedimentation and dispersion behavior. The saturated magnetization of pure Fe₃O₄ nanoparticles reaches 48.1 emu g⁻¹ and the value for composite nanoparticles was as high as 173.5 emu g⁻¹. The nanoparticles show strong superparamagnetic characteristics and can be expected to be used as a candidate for magnetism-controlled drug release.     

Piezoelectric scattering limited mobility characteristics of a degenerate surface layer in compound semiconductors at low lattice temperatures

The theory is developed for piezoelectric scattering rate of carriers in a degenerate surface layer under the condition of low temperature when the approximations of the well-known traditional theory are not valid. The scattering rates thus obtained are then used to estimate the zero-field mobility characteristics for the surface layers under similar condition of low temperature. The results for the surface layers in GaAs and ZnO show that when one takes into account either the degeneracy of the carrier ensemble or the finite energy of the phonons or both, the energy dependence of the scattering rates changes significantly from what follows for a non-degenerate ensemble or from the traditional theory, where one makes use of the high-temperature approximation and thus assumes equipartition law for the phonon distribution, and neglects the phonon energy in the energy balance equation of the electron–phonon system. It is observed that the zero-field mobility characteristics that follow from these scattering rates are interesting in that they are quite different from what turns out either for a non-degenerate ensemble or in the high-temperature approximations.     

Spin thermoelectricity in dualhydrogenated zigzag silicene nanoribbons with surface adsorptions

The buckled structure of silicene provides a feasible pathway to influence its electric and magnetic properties via surface adsorptions. Here, we investigate the magnetic and spin thermoelectric transport properties of dual-hydrogenated zigzag silicene nanoribbons (ZSiNRs) without/with the hydrogen adsorption. The band gaps for two spin channels in ZSiNRs under the hydrogen adsorption are shifted near the Fermi level, leading to the appearance of spin Seebeck effect. Using a temperature difference, one can derive the carriers with the different spin index to flow in the opposite direction. Moreover, a large rectification ratio close to 10⁵ at room temperature is achieved for the spin current, and the charge current exhibits a remarkable negative differential thermoelectric resistance (NDTR) behavior. The results presented here are fascinating potential applications in the fields of silicon-based spin caloritronic devices.     

氟磷共掺杂二氧化硅光纤预制棒的表面晶化

对F、P共掺杂光纤预制棒退火后的表面晶化行为进行了研究.由改进的化学汽相沉淀法制备的氟和磷共掺杂二氧化硅光纤预制棒玻璃样品在6 h的1 150 ℃控温加热处理后,其表面发生晶化.用X-射线衍射仪观测其晶相,主要为α-方石英,可使玻璃具有二阶光学非线性;用光学显微镜观察了其表面形貌并对结晶微粒的大小进行测量,知晶粒大小在十几到几十μm之间,会造成散射损耗的增加.实验结果,还显示氟对结晶过程有很大的影响.     

Wall shear stress and near-wall convective transport: Comparisons with vascular remodelling in a peripheral graft anastomosis

Fluid dynamic properties of blood flow are implicated in cardiovascular diseases. The interaction between the blood flow and the wall occurs through the direct transmission of forces, and through the dominating influence of the flow on convective transport processes. Controlled, in vitro testing in simple geometric configurations has provided much data on the cellular-level responses of the vascular walls to flow, but a complete, mechanistic explanation of the pathogenic process is lacking. In the interim, mapping the association between local haemodynamics and the vascular response is important to improve understanding of the disease process and may be of use for prognosis. Moreover, establishing the haemodynamic environment in the regions of disease provides data on flow conditions to guide investigations of cellular-level responses.     

Meter-long CeO2/YSZ/Y2O3 buffer layers for YBCO coated conductors using DC reactive sputtering

This paper reports CeO₂/YSZ/Y₂O₃ buffer layers deposited on biaxially textured NiW substrates by DC reactive sputtering in a reel-to-reel system. The effect of partial pressure of water vapor (P_H2O) on surface morphology and orientation of the Y₂O₃ films was examined. The obtained CeO₂/YSZ/Y₂O₃ buffer layers exhibit a highly biaxial texture, with in- and out-of-plane FWHM values respectively in the range of 6.0–7.0° and 4.5–5.5°. Crystallographic consistency of CeO₂/YSZ/Y₂O₃ along meter length is excellent. Atomic force microscope observation (AFM) reveals a smooth, continuous and crack-free surface with a Root-mean-square roughness (RMS) lower than 10 nm.     

介质pH对银基上4-甲基-4H-3-巯基-1,2,4-三氮唑成膜结构和缓蚀性能影响的SERS和电化学研究

在不同pH介质中,缓蚀试剂4-甲基-4H-3-巯基-1,2,4-三氮唑(4-MTTL)都能在银基底上形成自组装膜。SERS光谱表明:当pH=3时,4-MTTL分子是以硫醇式,通过两个氮原子为吸附位点,以较平躺方式在银表面构筑自组装膜;当介质为pH=7和pH=11时,4-MTTL以硫醇式,通过氮和硫原子为吸附位点倾斜或垂直方式作用于银表面。由于后者的吸附方式比前者更为垂直于表面,所以形成的膜中分子排列更为致密。电化学极化实验也表明,在pH=3的条件下,形成的4-MTTL单层有更正的腐蚀电位;在pH=11时,构筑的膜缓蚀能力强于pH=7的。并由电化学交流阻抗数据解析了相应的缓蚀机理。     

A Direct Experimental Evidence of Collective Electron Resonance Mechanism of Surface Enhanced Infrared Spectroscopy (Seirs)

Abstract

We report here the preliminary results of the surface enhanced transmission infrared spectra of CH₃(CH₂)₇Azo(CH₂)₃COOH monolayers on CaF₂ substrate which was coated by silver island films with different size and distribution. The larger enhancement of absorbance of v(C=O) in COOH residing between silver island gap and small enhancement of absorbance of vibration mode of COO^? located on the silver islands are observed. It give us a direct experimental evidence of the collective electron resonance mechanism of surface enhance infrared spectroscopy (SEIRS), i.e. the decrease of the electromagnetic (EM) coupling reduces the enhancement factor of SEIRS.