Synthesis and application as polymer electrolyte of hyperbranched polyether made by cationic ring‐opening polymerization of 3‐{2‐[2‐(2‐hydroxyethoxy)ethoxy]ethoxymethyl}‐3′‐methyl‐oxetane

A novel cyclic ether monomer 3‐{2‐[2‐(2‐hydroxyethoxy)ethoxy]ethoxy‐methyl}‐3′‐methyloxetane (HEMO) was prepared from the reaction of 3‐hydroxymethyl‐3′‐methyloxetane tosylate with triethylene glycol. The corresponding hyperbranched polyether (PHEMO) was synthesized using BF₃·Et₂O as initiator through cationic ring‐opening polymerization. The evidence from ¹H and ¹³C NMR analyses revealed that the hyperbranched structure is constructed by the competition between two chain propagation mechanisms, i.e. active chain end and activated monomer mechanism. The terminal structure of PHEMO with a cyclic fragment was definitely detected by MALDI‐TOF measurement. A DSC test implied that the resulting polyether has excellent segment motion performance potentially beneficial for the ion transport of polymer electrolytes. Moreover, a TGA assay showed that this hyperbranched polymer possesses high thermostability as compared to its liquid counterpart. The ion conductivity was measured to reach 5.6 × 10^?5 S/cm at room temperature and 6.3 × 10^?4 S/cm at 80 °C after doped with LiTFSI at a ratio of Li:O = 0.05, presenting the promise to meet the practical requirement of lithium ion batteries for polymer electrolytes. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 3650–3665, 2006     

Preparation and characterization of mesoporous silica thin films from polyethoxysiloxanes

Tetraethoxysilane (TEOS) and polyethoxysiloxanes (PEOSs; prepared by the acid‐catalyzed hydrolytic polycondensation of TEOS) were subjected to the sol–gel process in the presence of cetyltrimethylammonium bromide (CTAB), respectively. The PEOSs with M_w 700–26,000, as prepared by sol–gel coating of TEOS and PEOS under various conditions, were used. Uniform and crack‐free thin films of thickness 276–613 nm were prepared by spin‐coating of a PEOS solution containing CTAB. When the coating films were sintered at 400 °C, the combustion of ethoxy groups and CTAB took place to provide porous silica thin films. The structure of the thin films was found to be dependent on the molecular weight of PEOS and the molar ratio of CTAB/Si: lamellar or hexagonal phase was observed for M_w less than 15,000 and for CTAB/Si molar ratios greater than 0.10. Honeycomb structures were observed for M_w less than 5000 and for CTAB/Si molar ratios of 0.15. The honeycomb structure was also observed by atomic force microscopy and transmission electron microscope. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 2542–2550, 2006     

Evaluation of piezoelectric PVDF polymers for use in space environments. III. Comparison of the effects of vacuum UV and gamma radiation

Films of piezoelectric PVDF and P(VDF‐TrFE) were exposed to vacuum UV (115–300 nm VUV) and γ‐radiation to investigate how these two forms of radiation affect the chemical, morphological, and piezoelectric properties of the polymers. The extent of crosslinking was almost identical in both polymers after γ‐irradiation, but surprisingly, was significantly higher for the TrFE copolymer after VUV‐irradiation. Changes in the melting behavior were also more significant in the TrFE copolymer after VUV‐irradiation due to both surface and bulk crosslinking, compared with only surface crosslinking for the PVDF films. The piezoelectric properties (measured using d₃₃ piezoelectric coefficients and D‐E hysteresis loops) were unchanged in the PVDF homopolymer, while the TrFE copolymer exhibited more narrow D‐E loops after exposure to either γ‐ or VUV‐radiation. The more severe damage to the TrFE copolymer in comparison with the PVDF homopolymer after VUV‐irradiation is explained by different energy deposition characteristics. The short wavelength, highly energetic photons are undoubtedly absorbed in the surface layers of both polymers, and we propose that while the longer wavelength components of the VUV‐radiation are absorbed by the bulk of the TrFE copolymer causing crosslinking, they are transmitted harmlessly in the PVDF homopolymer. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 3253–3264, 2006     

Mechanical endurance of polymer electrolyte membrane and PEM fuel cell durability

The life of proton exchange membrane fuel cells (PEMFC) is currently limited by the mechanical endurance of polymer electrolyte membranes and membrane electrode assemblies (MEAs). In this paper, the authors report recent experimental and modeling work toward understanding the mechanisms of delayed mechanical failures of polymer electrolyte membranes and MEAs under relevant PEMFC operating conditions. Mechanical breach of membranes/MEAs in the form of pinholes and tears has been frequently observed after long‐term or accelerated testing of PEMFC cells/stacks. Catastrophic failure of cell/stack due to rapid gas crossover shortly follows the mechanical breach. Ex situ mechanical characterizations were performed on MEAs after being subjected to the accelerated chemical aging and relative humidity (RH) cycling tests. The results showed significant reduction of MEA ductility manifested as drastically reduced strain‐to‐failure of the chemically aged and RH‐cycled MEAs. Postmortem analysis revealed the formation and growth of mechanical defects such as cracks and crazing in the membranes and MEAs. A finite element model was used to estimate stress/strain states of an edge‐constrained MEA under rapid RH variations. Damage metrics for accelerated testing and life prediction of PEMFCs are discussed. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 2346–2357, 2006     

Characterization and electrical properties of polypyrrole/multiwalled carbon nanotube composites synthesized by in situ chemical oxidative polymerization

This study describes the preparation of polypyrrole (PPy)/multiwalled carbon nanotube (MWNT) composites by in situ chemical oxidative polymerization. Various ratios of MWNTs, which served as hard templates, were first dispersed in aqueous solutions with the surfactant cetyltrimethylammonium bromide to form micelle/MWNT templates and overcome the difficulty of MWNTs dispersing into insoluble solutions of pyrrole monomer, and PPy was then synthesized via in situ chemical oxidative polymerization on the surface of the templates. Raman spectroscopy, Fourier transform infrared (FTIR), field‐emission scanning electron microscopy (FESEM), and high‐resolution transmission electron microscopy (HRTEM) were used to characterize the structure and morphology of the fabricated composites. Structural analysis using FESEM and HRTEM showed that the PPy/MWNT composites were core (MWNT)–shell (PPy) tubular structures. Raman and FTIR spectra of the composites were almost identical to those of PPy, supporting the idea that MWNTs served as the core in the formation of a coaxial nanostructure for the composites. The conductivities of these PPy/MWNT composites were about 150% higher than those of PPy without MWNTs. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 1413–1418, 2006     

Wetting at a polymer gel–vapor interface; a system not influenced by a long-range van der Waals contribution

The exterior of a cross-linked polymer gel resembles a polymer brush. Such gel including its brush can be swollen by a good solvent. The detachment of the solvent–vapor (L–V) interface from the brush is controlled by the adsorption of polymer segments onto this interface and is to a very good approximation not influenced by long-range van der Waals contributions. A wetting transition in this system coincided with the adsorption–desorption transition for chains onto such L–V interface and has various unusual features. There are several indications that in practice this system should feature a second-order wetting transition.     

Combinational simulations of free energy of polymer solution

It is conceptually proposed that the total entropy of polymer solution is contributed from two distinct parts: the positional and the oomformational. The former can be represented analytically, while the latter can be simulated with the random self-avoiding walk model on the simple cubic lattice for multichain systems. The obtained results indicated that both the conformational entropy and the mixing heat are consistent with the scaling laws wry well.     

On the origin of 1.5 μm luminescence in porous silicon coated with sol–gel derived erbium-doped Fe2O3 films

Sol–gel derived Fe₂O₃ films containing about 10 wt% of Er₂O₃ were deposited on porous silicon by dipping or by a spin-on technique followed by thermal processing at 1073 K for 15 min. The samples were characterized by means of PL, SEM and X-ray diffraction analyses. They exhibit strong room-temperature luminescence at 1.5 μm related to erbium in the sol–gel derived host. The luminescence intensity increases by a factor of 1000 when the samples are cooled from 300 to 4.2 K. After complete removal of the erbium-doped film by etching and partial etching the porous silicon, the erbium-related luminescence disappears. Following this, luminescence at 1.5 μm originating from optically active dislocations (“D-lines”) in porous silicon was detected. The influence of the conditions of synthesis on luminescence at 1.5 μm is discussed.