Effect of a Nanoclay on the Mechanical,Thermal and Flame Retardant Properties of Rigid Polyurethane Foam

Water blown rigid polyurethane foams (PUF) with organoclay/organically modified nanoclay (ONC) were prepared and their properties such as density, mechanical, morphological, insulation, thermal and flame retardant properties were studied. In this investigation, the ONC content was varied from 1 to 10 parts per hundred of polyol (php) by weight. It was observed that the compressive strength of ONC filled PUF increased up to 3 php of ONC loading and then it decreased. Wide angle X-ray diffraction and transmission electron microscopy studies indicated the exfoliated dispersion of ONC in PUF. The thermal conductivity of ONC filled PUF decreases up to 5 php and then increases. The glass transition temperature (Tg) of PUF decreases on loading of ONC. The TGA analysis shows that there is slight increase in degradation temperature with increase in ONC loading. The flame retardant properties (LOI and flame spread rate) are improved slightly on addition (3 php) of ONC filled PUF.     

Mechanical,Thermal and Morphological Behaviors of Castor Oil Based PU/PS Interpenetrating Polymer Network-Metakaolin Composites

The meta kaolin (MK) clay particulate filler with different weight ratios viz., 0, 5, 10, 20 and 30 wt% were incorporated into castable polyurethane (PU)/polystyrene (PS) (90/10) interpenetrating polymer network (IPN). The effects of MK particulate filler loading on the mechanical and thermal properties of PU/PS (90/10) IPN composites have been studied. From the tensile behavior, it was noticed that a significant improvement in tensile strength and tensile modulus as an increase in MK filler content. Thermogravimetric analysis (TGA) data reveals the marginal improvement in thermal stability after incorporation of MK filler. TGA studies of the IPN composites have been performed in order to establish the thermal stability and their mode of thermal degradation. It was found that degradation of all composites takes place in two steps. Degradation kinetic parameters were obtained for the composites using three mathematical models. Tensile fractured composite specimens were used to analyze the morphology of the composites by scanning electron microscopic (SEM) technique.     

Synthesis and Characterization of Silicone Modified Polyurethane Surfactant Useable at High Temperature

A series of novel silicone modified polyurethane (Si-PU) surfactants were successfully synthesized by using hydroxypropyl-terminated polydimethylsiloxane (HPMS), polyethylene glycol (PEG), dimethylolpropionic acid (DMPA) and isophoronediisocyanate (IPDI). The chemical structure of the surfactant was confirmed by FTIR and ¹H-NMR. TEM photographs showed that the micelles of the Si-PU surfactants dispersed in aqueous solution were spherical with the particle size in the range of 100–400 nm. Surface tension measurements indicated that these surfactants had low surface tension to 29.9 mN·m^?1and a definite critical micelle concentration to, approximately 5.0×10^?4–7.5×10^?4mol·L^?1. When the content of HPMS was 20 wt%, the surfactant's, emulsifying performance was superior to the traditionally available Span80/Tween80 mixed emulsifiers. In addition to that, no phase transition temperature was detected from 20°C to 90°C by fluorescence probe and DSC measurements, confirming the high thermal stability of the micelles.     

Helical Biphenyl Bisazo Polyurethane: Preparation,Characterization and Analysis of Polymeric Thermo-Optic Switch

The bisazo chromophore molecule (CAAPM) and helical biphenyl bisazo polyurethane (HBBPU) were synthesized. The structures of CAAPM and HBBPU were characterized by FT-IR and UV-vis spectroscopic techniques. The measurements of refractive index and thermo-optic coefficient (dn/dT) of HBBPU were demonstrated at different wavelengths and different temperatures by the ATR technique. By using CCD digital imaging devices, transmission loss of the internal waveguide was measured. The refractive index dispersions and Sellmeyer coefficients of HBBPU were obtained by the Sellmeyer equation. A Y-branched switch based on the thermo-optic effect was proposed and the performance of the switch was simulated. With a branching angle of 0.143° and the FD-BPM method, the result showed that the power consumption of the thermo-optic switch could be only 3.6 mW, and the response time of the switch could reach about 8 ms. This is a significant improvement in reducing power consumption compared with the normal Y-branched polymer thermo-optic switch.     

Synthesis and properties of near IR induced self-healable polyurethane/graphene nanocomposites

A series of self-healable polyurethane (SHPU)/modified graphene (MG) nanocomposites were synthesized from poly(tetramethylene glycol) (PTMG) and 4,4′-methylene diphenyl diisocyanate (MDI) with minute amounts (0–1 wt%) of MG which was chemically modified graphene oxide (GO) with phenyl isocyanate and reduced in the presence of phenylhydrazine.     

Properties of Aqueous Polyurethane Dispersion Modified by Epoxide Resin and Their Use as Adhesive

The aqueous polyurethane hybrid dispersion modified by the epoxy resin were synthesized using 1,4-butanediol ( BDO ) and dimethylolpropionic(DMPA) as chain extenders. A kind of automobile interior decoration adhesive was made by the modified hybrid dispersions. Effects of the content and the kinds of epoxide resin on the properties of dispersions and dispersion-cast films such as appearance, pot life, viscosity, particle size, molecular mass, hardness, swelling in water, contact angle, strength of stress, elongation at break, and other mechanical properties were studied. At the same time the effect of the E20 content on the peel strength of the adhesive for several automobile interior decoration substrates such as rubber/wood, poly(vinyl chloride)/wood; leather/wood, sponge/wood was investigated. The experimental results show that when the epoxy resin E20 content was 8%, the modified polyurethane hybrid dispersions possess better properties and the adhesive made by the modified dispersions posses better adhesion for automobile interior decoration substrates. The stress-strain curve of the modified aqueous polyurethane hybrid dispersions films shows the modified aqueous cast films possess better rigidity and toughness.     

Retention profile of Fe,Mn and Cu onto chemically treated polyurethane with carbon disulfide

Dithiocarbamate modified polyurethane foam (DTC-PUF) was synthesized as a new solid-phase extraction sorbent for the preconcentration and determination of Fe(II), Mn(II) and Cu(II) in environmental samples using flame atomic absorption spectrometry. Maximum extraction of the elements was achieved at pH 5–7 and flow rate 3 mL min^?1. Quantitative desorption was achieved by 10 mL from 1.0 mol L^?1 HCl solution. The capacity of the sorbent was 149.2 ± 0.5, 237.5 ± 0.2, 200.2 ± 0.1 μg g^?1 and the limit of detection was of 0.015, 0.015 and 0.012 μg mL^?1for Fe(II), Mn(II) and Cu(II), respectively. A preconcentration factor of 100 was obtained for all elements. The developed method was successfully applied to the determination of the tested elements in water (tap and lake) and plant (spinach and parsley leaves) samples and showed good recovery values from 98 to 111% with corresponding RSD values ranged from 0.6 to 8.6%.     

磷杂菲改性腰果酚多元醇的合成及阻燃聚氨酯硬泡性能

采用生物质原料腰果酚和9,10-二氢-9-氧杂-10-膦杂菲-10-氧化物(DOPO)为原料, 合成了一种磷杂菲改性腰果酚多元醇(P-Cardanol-Polyol), 并利用核磁共振氢谱和磷谱对其结构进行了表征. 利用P-Cardanol-Polyol对聚氨酯硬泡(RPUF)进行阻燃改性, 得到一系列阻燃聚氨酯硬泡. 考察了P-Cardanol-Polyol的用量对阻燃聚氨酯硬泡的形貌、 密度、 热导率、 压缩性能、 热稳定性以及阻燃性能的影响. 研究结果表明, P-Cardanol-Polyol对聚氨酯硬泡的密度影响可以忽略不计; 随着P-Cardanol-Polyol的加入, 阻燃聚氨酯硬泡的平均孔径逐渐减小, 热导率也逐渐降低. 未改性聚氨酯硬泡的最大热释放速率和总放热量分别为390 kW/m²和31.9 MJ/m², 阻燃聚氨酯硬泡则降低至340 kW/m²和24.6 MJ/m². 此外, 阻燃聚氨酯硬泡的压缩强度比未改性聚氨酯硬泡提升了约13%. 炭层分析结果表明, P-Cardanol-Polyol能够促进聚氨酯硬泡形成连续致密且具有良好抗热氧化性能的炭层, 有利于减少燃烧过程中可燃性气体的逸出, 从而提升阻燃性能.     

Quantitative evaluation on oil diffusion mechanisms in nano‐organic‐montmorillonite modified caster oil‐based polyurethane foam for oil/water separation

To improve the oil absorbency of caster oil‐based polyurethane foam, nano‐organic‐montmorillonite (OMMT) was used for the additives. The aim of this study is to evaluate the oil diffusion mechanism and dispersion uniformity of OMMT modified caster oil‐based polyurethane (MPU) using experiments and molecular dynamic simulation. Molecule movement and molecule trajectory of oil was investigated by molecular dynamic simulation and numerical simulation. According to the quantitative analyzing results, the diffusion model was put forward. The average diffusion coefficient of crude oil in 0, 1, 2 wt%, 4, and 6 wt% MPU is 2.4 × 10^?4 cm²/s, 2.6 × 10^?4 cm²/s, 3.0 × 10^?4 cm²/s, 3.2 × 10^?4 cm²/s, and 3.3 × 10^?4 cm²/s, respectively. It indicated that crude oil appeared gradient in the MPU. The optimal diffusion direction of crude oil is (0, 0, 1) crystal face, and the small particles of crude oil are easy to be adsorbed. The two‐dimensional diffusion trajectory of crude oil is nonlinear. The diffusion model includes the diffusion of crude oil at the interface of oil and polyurethane, surface diffusion and pore diffusion, and pore adsorption. Furthermore, the diffusion model showed that the van der Waals force was the main reason for crude oil diffusion or adsorption. OMMT could improve the ability of oil/water separation of polyurethane.     

一种新型的侧链型聚氨酯高分子钌聚合物的合成

通过分子设计,将带有-OH端基的钌(Ⅱ)联吡啶配合物[Ru(bpy)2L]PF6{L=希夫碱4-[(N甲-基-N羟-乙基)氨基]苯甲醛缩肼基硫代甲酸甲酯}与甲苯-2,4异-氰酸酯、丙烯酸羟乙酯发生共聚合反应,合成了新的侧链型聚氨酯高分子钌聚合物(4)。4的结构经红外光谱和差热分析表征。