Novel,biodegradable, functional poly(ester‐carbonate)s by copolymerization of trans‐4‐hydroxy‐L‐proline with cyclic carbonate bearing a pendent carboxylic group

Water‐soluble poly(ester‐carbonate) having pendent amino and carboxylic groups on the main‐chain carbon is reported for the first time. This article describes the melt ring‐opening/condensation reaction of trans‐4‐hydroxy‐N‐benzyloxycarbonyl‐L ‐proline (N‐CBz‐Hpr) with 5‐methyl‐5‐benzyloxycarbonyl‐1,3‐dioxan‐2‐one (MBC) at a wide range of molar fractions. The influence of reaction conditions such as catalyst concentration, polymerization time, and temperature on the number average molecular weight (M_n) and molecular weight distribution (M_w/M_n) of the copolymers was investigated. The polymerizations were carried out in bulk at 110 °C with 3 wt % stannous octoate as a catalyst for 16 h. The poly(ester‐carbonate)s obtained were characterized by Fourier transform infrared spectroscopy, ¹H NMR, differential scanning calorimetry, and gel permeation chromatography. The copolymers synthesized exhibited moderate molecular weights (M_n = 6000–14,700 g mol^?1) with reasonable molecular weight distributions (M_w/M_n = 1.11–2.23). The values of the glass‐transition temperature (T_g) of the copolymers depended on the molar fractions of cyclic carbonate. When the MBC content decreased from 76 to 12 mol %, the T_g increased from 16 to 48 °C. The relationship between the poly(N‐CBz‐Hpr‐co‐MBC) T_g and the compositions was in approximation with the Fox equation. In vitro degradation of these poly(N‐CBz‐Hpr‐co‐MBC)s was evaluated from weight‐loss measurements and the change of M_n and M_w/M_n. Debenzylation of 3 by catalytic hydrogenation led to the corresponding linear poly(ester‐carbonate), 4 , with pendent amino and carboxylic groups. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 2303–2312, 2004     

Synthesis and characterization of oxidized cellulose

Samples of oxidized cellulose (OC) with various carboxyl contents and degrees of crystallinity were obtained by the oxidation of native and mercerized cellulose with a solution of nitrogen(IV) oxide in CCl₄. A detailed characterization of these OC samples was performed. The effect of oxidation conditions (concentration of N₂O₄ in the solution and oxidation time) and starting cellulose material on OC characteristics (carboxyl, carbonyl and nitrogen content, degree of crystallinity and polymerization, surface area and swelling, and acidic properties) was investigated. Reactivity in the oxidation process was higher in mercerized cellulose than in native cellulose. The action of dilute solutions (10–15%) of N₂O₄ did not affect the degree of crystallinity of cellulose samples. Under these conditions, the oxidation took place mainly in amorphous regions and on the surface of crystallites. Oxidation in a concentrated (40%) N₂O₄ solution led to the destruction of crystallites, which increased the surface area and swelling of cellulose in water. The surface area and the swelling of OC samples increased with a decrease in the index of crystallinity. The acidic properties of OC were shown to increase with an increase of swelling in water. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 4785–4791, 2004     

Two‐stage copolycondensation of preformed oligomers with bisphenols by tosyl chloride/dimethylformamide/pyridine from distributions of resulting oligomers determined by a combination of gel permeation chromatography and NMR

A two‐stage co‐oligomerization of the oligomers initially formed from an equimolar mixture of isophthalic acid (IPA) and terephthalic acid (TPA) and 2,2‐bis(4‐hydroxyphenyl)propane (BPA, 50 mol %) with bisphenols (BPs, 20 mol %) was carried out using a tosyl chloride/dimethylformamide/pyridine condensing agent. The distributions of the resulting oligomers (n_x‐mers), which were quenched with methanol, were determined by a combination of gel permeation chromatography (GPC) and NMR. These distributions (presented by molar percentage) were conveniently calculated with the equation n_x (mol %) = n_x (% mol by GPC) × n₀ (mol % by NMR)/n₀ (% mol by GPC), where n_x (% mol) = n_x (wt % by GPC)/its molecular weight. The results showed the distributions of the preformed IPA/TPA‐BPA oligomers to be in fairly good accord with those obtained directly from GPC and to be supported by the NMR results. The calculation was applied to the co‐oligomers prepared up to a reaction of 0.7, at which there was an increase in the number of higher oligomers indivisible by GPC and the distributions could no longer be determined by molar percentage. The calculated distributions are discussed in relation to the results of copolycondensation. The sequence distributions in the resulting co‐oligomers, which were also examined by NMR, are compared with those in the copolymers. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 44–51, 2004     

Polymerization of 1,3‐dienes with functional groups. III. Free‐radical polymerization of N,N‐diethyl‐2‐methylene‐3‐butenamide

Free‐radical homo‐ and copolymerization behavior of N,N‐diethyl‐2‐methylene‐3‐butenamide (DEA) was investigated. When the monomer was heated in bulk at 60 °C for 25 h without initiator, rubbery, solid gel was formed by the thermal polymerization. No such reaction was observed when the polymerization was carried out in 2 mol/L of benzene solution with with 1 mol % of azobisisobutyronitrile (AIBN) as an initiator. The polymerization rate (R_p) equation was R_p ∝ [DEA]^1.1[AIBN]^0.51, and the overall activation energy of polymerization was calculated 84.1 kJ/mol. The microstructure of the resulting polymer was exclusively a 1,4‐structure where both 1,4‐E and 1,4‐Z structures were included. From the product analysis of the telomerization with tert‐butylmercaptan as a telogen, the modes of monomer addition were estimated to be both 1,4‐ and 4,1‐addition. The copolymerizations of this monomer with styrene and/or chloroprene as comonomers were also carried out in benzene solution at 60 °C. In the copolymerization with styrene, the monomer reactivity ratios obtained were r₁ = 5.83 and r₂ = 0.05, and the Q and e values were Q = 8.4 and e = 0.33, respectively. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 999–1007, 2004     

New 7‐membered diazepanone alkoxyamines for nitroxide‐mediated radical polymerization

The synthesis of new 7‐membered diazepanone alkoxyamines [2,2,7,7‐tetramethyl‐1‐(1‐phenyl‐ethoxy)‐[1,4]diazepan‐5‐one ( 3 ) and 2,7‐diethyl‐2,3,7‐trimethyl‐1‐(1‐phenyl‐ethoxy)‐[1,4]diazepan‐5‐one ( 8 )] through the Beckmann rearrangement of piperidin‐4‐one alkoxyamines was developed. Both 3 and 8 were evaluated as initiators and regulators for the nitroxide‐mediated radical polymerization of styrene and n‐butyl acrylate. 8 , a sterically highly hindered alkoxyamine readily available as a crystalline solid, allowed the fast and controlled polymerization and preparation of polymers with low polydispersity indices (1.2–1.4) up to a degree of polymerization of about 100. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 3332–3341, 2004     

Synthesis and structural characterization of novel,fluorinated poly(phthalazinone ether)s containing perfluorophenylene moieties

The synthesis and structural characterization of a series of novel, fluorinated poly(phthalazinone ether)s containing perfluorophenylene moieties are described. The monomers, 4‐(4′‐hydroxyaryl)phthalazin‐1(2H)‐ones ( 2a – 2d ), were conveniently and efficiently synthesized from phenols and phthalic anhydride in two steps via 2‐(4′‐hydroxybenzoyl)benzoic acids, which were first obtained by the Friedel–Crafts reaction in good yields and with high stereoselectivity and were then converted into 2a – 2d by fusion with hydrazine. All the polymers were prepared by nucleophilic aromatic substitution (S_NAr) polycondensation between the compounds perfluorobiphenyl and 4‐(4′‐hydroxyaryl)phthalazin‐1(2H)‐ones ( 2a ‐ 2d ). The resulting fluorinated polymers were readily soluble in common organic solvents (e.g., CHCl₃, tetrahydrofuran, dimethylformamide, dimethyl sulfoxide, N‐methylpyrrolidone, etc.) at room temperature. Their weight‐average molecular weights and the polydispersities ranged from (7.96–18.25) × 10³ to 1.31–2.71, respectively. Their glass‐transition temperatures varied from 213 to 263 °C. They were all stable up to 390 °C both in air and in argon. The 5% weight‐loss temperatures of these polymers in air and argon ranged from 393–487 to 437–509 °C, respectively. Wide‐angle X‐ray diffraction studies indicated they were all amorphous and could be attributed to the presence of kink nonplanar moiety, phenyl phthalazinone along the polymer backbone. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 925–932, 2004     

Generation of highly stable amidate anion in anionic polymerization of 3‐(triethylsilyl)propyl isocyanate

To study living anionic polymerization, 3‐(triethylsilyl)propyl isocyanate (TEtSPI) monomer was synthesized by hydrosilylation of allylamine with triethylsilane and treatment of the resulting amine with triphosgene. The polymerization of TEtSPI was performed with sodium naphthalenide (Na‐Naph) as an initiator and in the absence and presence of sodium tetraphenylborate (NaBPh₄) as an additive in tetrahydrofuran (THF) at ?78 and at ?98 °C. A highly stabilized amidate anion for living polymerization of isocyanates was generated for the first time with the combined effect of the bulky substituent and the shielding action of the additive NaBPh₄, extending the living character at least up to 120 min at ?98 °C. Even the anion could exist at ?78 °C for 10 min. A block copolymer, poly(n‐hexyl isocyanate)‐b‐poly[(3‐triethylsilyl)propyl isocyanate]‐b‐poly(n‐hexyl isocyanate), was synthesized with quantitative yields and controlled molecular weights via living anionic polymerization in THF at ?78 °C for TEtSPI and ?98 °C for n‐hexyl isocyanate, respectively, with Na‐Naph with three times of NaBPh₄ as a common ion salt. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 933–940, 2004     

Synthesis and characterization of alt‐bipyridinylene‐phenylene copolymers containing ruthenium(II) complexes

Poly{bis(4,4′‐tert‐butyl‐2,2′‐bipyridine)–(2,2′‐bipyridine‐5,5′‐diyl‐[1,4‐phenylene])–ruthenium(II)bishexafluorophosphate} ( 3a ), poly{bis(4,4′‐tert‐butyl‐2,2′‐bipyridine)–(2,2′‐bipyridine‐4,4′‐diyl‐[1,4‐phenylene])–ruthenium(II)bishexafluorophosphate} ( 3b ), and poly{bis(2,2′‐bipyridine)–(2,2′‐bipyridine‐5,5′‐diyl‐[1,4‐phenylene])–ruthenium(II)bishexafluorophosphate} ( 3c ) were synthesized by the Suzuki coupling reaction. The alternating structure of the copolymers was confirmed by ¹H and ¹³C NMR and elemental analysis. The polymers showed, by ultraviolet–visible, the π–π* absorption of the polymer backbone (320–380 nm) and at a lower energy attributed to the d–π* metal‐to‐ligand charge‐transfer absorption (450 nm for linear 3a and 480 nm for angular 3b ). The polymers were characterized by a monomodal molecular weight distribution. The degree of polymerization was approximately 8 for polymer 3b and 28 for polymer 3d . © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 2911–2919, 2004     

Synthesis and characterization of new segmented polyurethanes with side‐chain,liquid‐crystalline chain extenders

Liquid‐crystalline, segmented polyurethanes with methoxy–biphenyl mesogens pendant on the chain extender were synthesized by the conventional prepolymer technique and esterification reaction. Two, side‐chain, liquid‐crystalline (SCLC) polyurethanes with mesogens having spacers of six and eight methylene units were prepared. The structures of the mesogenic units and SCLC polyurethanes were confirmed by Fourier transform infrared spectroscopy and ¹H NMR. Polymer properties were also examined by solubility tests, water uptakes, and inherent viscosity measurements. Differential scanning calorimetry studies indicated that the transition temperature of the isotropic to the liquid‐crystalline phase decreased with increasing spacer length. Wide‐angle X‐ray diffraction (WAXD) studies revealed the existence of liquid‐crystalline phases for both SCLC polyurethanes. Polarized optical microscopic investigations further confirmed the thermotropic liquid‐crystalline behaviors and nematic mesophases of both samples. Thermogravimetric analysis displayed better thermal stabilities for both SCLC polymers and indicated that the presence of mesogenic side chains may increase the thermal stability of segmented polyurethanes. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 290–302, 2004