A scratch-resistant single-layer antireflective coating by a low temperature sol-gel route

A novel quarterwave-thick narrow-bandwidth antireflective coating has been developed for both plastic and vitreous substrates by a sol-gel route. This coating has revealed pronounced scratch- and climatic-resistance under adverse conditions. The single-layer coating consists basically of a composite material made of silica as the discontinuous phase and of a polytetrafluoroethylene-derived (Teflon¹) organic polymer as the continuous phase. This leads to fluorine-containing colloidal silica product, or a so-called Flucosil coating. The coating is applied by spinning or dipping from specific solutions at room temperature followed by a mild and short heat treatment. In addition to remarkable abrasion and environmental resistance properties, such coatings have displayed excellent laser-induced damage threshold levels, surpassing uncoated substrates.We hope such a product might open new perspectives concerning household articles, architectural optical thin-films, ophthalmic uses, and so on.     

Nanoporous TiO2 Coatings for Infrared Detectors

In GaAs based infrared detectors, a considerable part of the incident light will be reflected at the surface, thus it decreases the detectors sensitivity considerably. In this paper, a TiO₂ nanoporous coating was prepared successfully on the GaAs substrate by sol-gel method. The optical parameters of the coating were also controlled successfully. It was proved that the coating could greatly improve the transmittance of the incident light, which agrees with the theoretical results quite well. In the 2.5–6.0 m waveband, the maximum transmittance of GaAs substrate is 56%, while the transmittance of the GaAs substrate coated with a nanostructured TiO₂ coating is about 94%.     

过渡金属离子对HPAsMoVO杂多酸的氧化性能的影响

用H2-TPR方法研究了过渡金属离子及其含量对杂多酸-HxPAs0.2Mo10VOy的氧化性能的影响,并在固定床反应器上考察了M0.2HxPAs0.2Mo10VOy(M=Fe3 、Co2 、N i2 和Cu2 )催化剂对异丁烷选择性氧化的催化性能.研究结果表明用过渡金属离子取代杂多酸中的质子,可以在较大程度上增强杂多酸的低温氧化能力,其中Fe3 对增强杂多酸的催化活性最为明显,而Cu2 却有利于提高目的产物甲基丙烯酸的选择性.     

Wittig-Olefinierung zu neuen donor- und akzeptor-substituierten 3-Vinylindolen: Optimierte Syntheseverfahren

Summary The optimized Wittig reaction of selectively functionalized 3-acylindoles yield new, and for Diels-Alder reactions highly reactive donor- and acceptor substituted 3-vinylindoles, respectively.

     

中空纤维催化膜反应器中环戊二烯的选择加氢反应

将聚乙烯吡咯烷酮（ＰＶＰ）负载钯催化剂（ＰＶＰ－Ｐｄ）镶嵌到三种醋酸纤维（ＣＡ）中空膜（ＣＡ－Ｉ，ＣＡ－Ⅱ，ＣＡ－Ⅲ）内制各中空纤维催化膜，并进一步制成催化膜反应器，在４０℃和０．１ＭＰａ的反应条件下，在催化膜反应器中进行了环戊二烯的选择加氢反应，考察了具有不同氢气渗透率的醋酸纤维丝组成的三种膜反应器对反应的转化率及选择性的影响，并在此基础上考察了各种反应参数对反应的影响，ＣＡ中空纤维催化膜对环戊     

丙烯选择氧化铋钼铁复氧化物催化剂组成,结构及性能的研究

采用XRD、Raman、XPS及催化剂性能评价等手段,考察了Bi_3(FeO_4)(MoO_4)_2和Fe_2(MoO_4)_3分别存在及两者共存时对Bi-Mo复氧化物体系催化性能的影响.结果表明,这两种含Fe物种的存在都有助于改善Bi-Mo系复氧化物催化剂对丙烯选择氧化反应的催化性能.但两者在作用机理上有所不同.Fe_2(MoO_4)_3本身无催化活性,但在反应条件下可部分还原为FeMoO_4形成Fe~(3+)/Fe~(2+)氧化还原对;且其地结构上与α-Bi_2(MoO_4)_3相匹配,这些因素都有助于促进催化体系中电子和氧物种的传递及催化剂表面活性中心的再生,从而提高催化性能.Bi_3(FeO_4)(MoO_4)_2在反应条件下也可形成Fe~(3+)/Fe~(2+)氧化还原对,但由于其Fe~(3-)所处的化学环境与Fe_2(MoO_4)_3很不相同,且Fe的含量也不及Fe_2(MoO_4)_3,因此它在促进催化体系中电子和氧物种的传递及催化剂表面活性中心的再生等方面的性能较差,但它对提高催化剂表面的活性中心(Bi-Mo对)数目有贡献.     

A technique for coating capillary columns with a very thick film of cross-linked stationary phase

A method for preparation of capillary columns and traps with a very thick film (up to 100 μm) of stationary phase is described. The principle of this method is based on an immediate fixation of a film of prepolymer, formed during dynamic coating. Thus, the development of film irregularities, such as are caused by Rayleigh instability is avoided. Fixation of the film is conveniently accomplished by heat-accelerated crosslinking as was demonstrated in this work, where a commercially available silicone prepolymer (Sylgard 184, Dow Corning) was employed. The low phase ratio columns which thus can be prepared are interesting both in chromatography with dense mobile phases and as enrichment devices. Examples of the latter application are shown, where trace organic components from air and water were concentrated.     

SYNTHESIS, CROSSLINKING MECHANISM AND PROPERTIES OF A POLYACRYLATE/POLYURETHANE COMPOSITE COATING

A polyacrylate/polyurethane (P(A) / P(U)) composite coating has been prepared bycrosslinking an acetoacetylated polyacrylate with a vinylic group terminated polyurethaneat room temperature. A model Michael reaction between ethyl acetoacetate (EAA) andmethyl acrylate (MA) was designed to study the crosslinking mechanism. It was foundthat the two active hydrogen atoms in acetoacetyl group can both add to vinylic groupsand the yield of mono- and bis-adducts are much affected by the molar ratio of acetoacetylto vinylic groups. Higher crosslinking degree and better properties could be obtained withdecreasing the molar ratio of the two active groups from 1/1 to 0.6/1 in the compositecoatings.     

烯丙基碘和锡与醛的选择加成反应

含活性基团的醛可与烯丙碘和锡粉直接进行亲核加成反应，得到高烯丙基的醇，水的存在不利于此反应的进行，与烯丙基溴相比，烯丙基碘反应活性更强，可在短时间内得较高的产率。     

Preparation of TiO2 Sol Using TiCl4 as a Precursor

A titanium dioxide sol with narrow particle size distribution was synthesized using TiCl₄ as the starting material. The sol was prepared by a process where HCl was added to a gel of hydrated titanium oxide to dissolve it. The resulting aqueous titanic acid solution was heated to form titanium dioxide sol. The effects of preparation parameters were investigated. TiCl₄ was slowly added to distilled water at 5°C. Aqueous solution of sodium hydroxide was added to adjust the pH of the system to 8–12. After aging for a period of time, the peptized sol was filtered and sufficiently washed. The filtered cake was repulped in water. Hydrochloric acid was slowly added to the solution with stirring. After condensation reaction and crystallization, a transparent sol with suspended TiO₂ was formed. XRD results show that the crystalline phase was anatase. The suspended TiO₂ particles were rhombus primary particles with the major axis ca. 20 nm and the minor axis ca. 5 nm. The TiO₂ particles prepared at pH 8 had the largest surface area of 141 cm³/g and it was microporous. The compositions of the solution which yielded the smallest suspended TiO₂ particles were TiO₂:HCl (35% HCl) = 1:1 (molar ratio), concentration of TiO₂ = 10%. Hydroxypropyl cellulose with viscosity of 150–400 cps was added as a dispersant. The sol was excellent in dispersibility and long-term stability. Transparent thin films could be obtained through dip-coating glass substrate in the sol. The dip-coating on glass can be less than three times to have one monolayer TiO₂. The transparent TiO₂ thin film had strong hydrophilicity after being illuminated by UV light.