Ring‐opening grafting polymerization of cyclic monomers onto human hair

Natural human hair was successfully modified by the graft polymerization of trimethylene carbonate, β‐propiolactone, ε‐caprolactone, glycidol, ε‐caprolactam, and 5,5‐dimethyl‐1,3‐dioxane‐2‐thione. In contrast, we could not modify natural human hair by the graft polymerization of oxetane under similar conditions. The model reaction suggested that the main initiating species in these polymerizations were the amino, thiol, and hydroxyl groups in hair, which could induce ring‐opening polymerization. Among the tested monomers, β‐propiolactone was most effective for hair modification with its graft polymer, whose concentration was as high as 0.5 g/g of hair though polymerization under mild conditions. The effects of the hair pretreatment and polymerization temperature on the weight ratio of the grafted polymers were also investigated. Hair modified by grafted polymers was characterized with scanning electron microscopy and Fourier transform infrared measurements. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 736–744, 2007     

Investigation on crosslinking behaviors of NBR/PVC filled with anhydrous copper sulfate particles by dynamic mechanical analysis

Crosslinking behaviors of acrylonitrile butadiene rubber (NBR)/poly (vinyl chloride) (PVC) alloy, filled with anhydrous copper sulfate (CuSO₄) particles, were investigated for the first time by dynamic mechanical analysis (DMA) under hetero and isothermal modes, respectively. In the heterothermal testing, (NBR/PVC)/CuSO₄ compound showed two marked increases in the storage modulus (E′), corresponding to coordination crosslinking of NBR-CuSO₄ and self-crosslinking of NBR and PVC respectively. During the isothermal testing, a dramatic increase in E′ was found at the initial stage while that of original NBR/PVC alloy was not detected. The marked increase in E′ of (NBR/PVC)/CuSO₄ compound was mainly due to the crosslinking induced by coordination between  CN and Cu²⁺. The increasing extent of E′ increased with the rise of CuSO₄ content, suggesting the formation of a greater number of crosslinks. Moreover, the activation energy (E_a) of crosslinking process was about 139 kJ/mol. In this work, fourier transform infrared spectrum (FT-IR) and equilibrium swelling method were also performed for the characterization of the compound. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 41–51, 2007     

ℙmax variations related to slaloms

We prove the iteration lemmata, which are the key lemmata to show that extensions by Pmax variations satisfy absoluteness for Π₂-statements in the structure 〈H (ω ₂), ∈, NS_{ω 1}, R 〉 for some set R of reals in L (ℝ), for the following statements: (1) The cofinality of the null ideal is ℵ₁. (2) There exists a good basis of the strong measure zero ideal. (© 2006 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim)     

Solvothermal synthesis of TiO2: anatase nanocrystals and rutile nanofibres from TiCl4 in acetone

This work reports a new synthetic approach for single‐phase TiO₂ nanomaterials by solvothermal treatment of titanium tetrachloride in acetone at 80–110 °C. Small, uniform, and yet size‐tunable (5–10 nm) anatase titania nanocrystallites were obtained using a low concentration of TiCl₄ in acetone (i.e., at molar ratios of TiCl₄/acetone ≤ 1:15) in the temperature range of 80–110 °C, while rutile nanofibers were synthesized using a high concentration of TiCl₄ (e.g., TiCl₄/acetone = 1:10) at 110 °C. Copyright © 2007 John Wiley & Sons, Ltd.