Oxygen inhibition in thiol–acrylate photopolymerizations

The overall effects of oxygen on thiol–acrylate photopolymerizations were characterized. Specially, the choice of thiol monomer chemistry, functionality, and concentration on the extent of oxygen inhibition were considered. As thiol concentration was increased, the degree of oxygen inhibition was greatly reduced because of chain transfer from the peroxy radical to the thiol. When comparing the copolymerization of 1,6‐hexanediol diacrylate with the alkane‐based thiol (1,6‐hexane dithiol) to the copolymerization with the propionate thiol (glycol dimercaptopropionate), it was found that the propionate system was much more reactive and polymerized to a greater extent in the presence of oxygen. In addition, the functionality was considered where the glycol dimercaptopropionate was compared to a tetrafunctional propionate of similar chemistry (pentaerythritol tetrakis(mercaptopropionate)). Given the same thiol concentration, the higher functionality thiol imparted a faster polymerization rate, due to the increased polymer system viscosity, which limited oxygen diffusion and decreased the extent of overall oxygen inhibition. Thus, preliminary insight is provided into how thiol monomer choice affects the extent of oxygen inhibition in thiol–acrylate photopolymerization. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 2007–2014, 2006     

Photoinitiated polymerization in bicontinuous microemulsions: Fluorescence monitoring

The photopolymerization of bicontinuous microemulsions was simultaneously monitored with differential scanning calorimetry and fluorescence. The kinetics and mechanism of the reaction were studied throughout the entire photopolymerization reaction. The role played by the surfactant in the kinetics and morphology was studied. The nature of the surfactant changed the autoacceleration process and final conversion. The behavior was explained as a result of the differences in the interfacial properties. Anionic cetyltrimethylammonium bromide (CTAB) gave rise to a more flexible interfacial film than anionic sodium dodecyl sulfate (SDS), resulting in competition between the intramolecular and intermolecular reactions in the former systems. As cyclization did not contribute to the increase in the degree of crosslinking, SDS photopolymerization gave solids with a more rigid microstructure. Fluorescence methodology was applied to monitor bicontinuous microemulsion polymerization and to reveal the microstructure and morphology development during photopolymerization. The microemulsion composition was designed to prepare nanoporous, crosslinked materials. Even though the nanostructure of the precursor microemulsions was not retained because of phase separation during polymerization, mesoporous solids were obtained. Their morphologies depended on the nature of the surfactant, and membranes with open cells were successfully prepared with CTAB, whereas more complex morphologies resulted with SDS. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 5291–5303, 2006     

Phenylene vinylene‐based electroluminescent polymers with electron transport block in the main chain

We report a new route for the design of soluble phenylene vinylene (PV) based electroluminescent polymers bearing electron‐deficient oxadizole (OXD) and triazole (TZ) moieties in the main chains with the aryloxy linkage. Both series of the PV‐based polymers were prepared by Wittig reaction. By properly adjusting the OXD and/or TZ content through copolymerization, we can achieve an enhanced balance of hole‐ and electron injections, such that the device efficiency is significantly improved. Light‐emitting diodes fabricated from P1, P2, P3, P4, P5, P6, and P7 with the configuration of Indium–Tin Oxide (ITO)/Poly (styrene sulfonic acid) doped poly (ethylenedioxythiophene) (PEDOT)/polymer/Ca/Al, emit bright green light with the maximum peak around 500 nm. For the device using the optimal polymer (P4) as emitting layer, a maximum brightness of 1300 cd/m² at 20 V and a maximum luminance efficiency of 0.325 cd/A can be obtained. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 3469–3478, 2006     

Effect of reaction conditions on the molecular weight and polydispersity of linear poly(arylene ether phosphine oxide)s prepared from an AB monomer

A thorough study of the polymerization behavior of 4‐fluoro‐4′‐hydroxytriphenyl‐phosphine oxide, 2 , under nucleophilic aromatic substitution reactions has been carried out. The synthesis of 2 was achieved in excellent yields by the reaction of bis(4‐fluorophenyl)phenylphosphine oxide, 1 , with one equivalent of potassium hydroxide in DMSO/water. The structure and purity of 2 were confirmed via ¹H, ¹³C, and ³¹P NMR spectroscopy along with elemental analysis. Polymerization reactions of 2 in NMP or DMSO at 180 °C provided the corresponding linear poly(arylene ether phosphine oxide)s, PAEPOs, with number average molecular weights, M_n, ranging from 11,700 to 36,500 Da. All of the polymer samples were completely soluble in chloroform, tetrahydrofuran, DMSO, NMP, and DMAc. The polymerization reactions were accompanied by a competing intramolecular process that resulted in the formation of cyclic oligomeric species that were removed via a final precipitation from methanol. Analysis using ³¹P NMR spectroscopy and size exclusion chromatography (SEC) confirmed that the majority of the lower molecular weight cyclic species were removed via this process. The polymer samples formed tough films when chloroform solutions were slowly evaporated on a glass slide. The PAEPO samples prepared in this study exhibited excellent thermal stability with T_d (5%) values between 503 and 542 in air while the glass transition temperatures ranged from 223 to 237 °C. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 2099–2106, 2006     

Crosslinked epoxy materials exhibiting thermal remendablility and removability from multifunctional maleimide and furan compounds

Crosslinked polymeric materials, which exhibit thermal remendability and removability through Diels–Alder (DA) and retro‐DA reactions, were obtained from using multifunctional maleimide and furan compounds as monomers. The synthesized monomers possess low melting points and good solubility in organo solvents to show excellent processing properties. The performance of DA and retro‐DA reactions were demonstrated with DSC and FTIR measurements. High performance of thermal remendablility and removability of the crosslinked materials were observed with SEM and solvent tests. These materials were applicable in advanced encapsulants and structural materials. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 905–913, 2006     

Facile syntheses of surface-functionalized micelles and shell cross-linked nanoparticles

Block copolymer micelles and shell cross-linked nanoparticles (SCKs) presenting Click-reactive functional groups on their surfaces were prepared using two separate synthetic strategies, each employing functionalized initiators for the controlled radical polymerization of acrylate and styrenic monomers to afford amphiphilic block copolymers bearing an alkynyl or azido group at the α-terminus. The first route for the synthesis of the azide-functionalized nanostructures was achieved via sequential nitroxide-mediated radical polymerization (NMP) of tert-butyl acrylate and styrene, originating from a benzylic chloride-functionalized initiator, followed by deprotection of the acrylic acids, supramolecular assembly of the block copolymer in water and conversion of the benzylic chloride to a benzylic azide. In contrast, the second strategy utilized an alkynyl-functionalized reversible addition fragmentation transfer (RAFT) agent directly for the RAFT-based sequential polymerization of tetrahydropyran acrylate and styrene, followed by selective cleavage of the tetrahydropyran esters to give the α-alkynyl-functionalized block copolymers. These Click-functionalized polymers, with the functionality located at the hydrophilic polymer termini, were then self-assembled using a mixed-micelle methodology to afford surface-functionalized “Clickable” micelles in aqueous solutions. The optimum degree of incorporation of the Click-functionalized polymers was investigated and determined to be ca. 25%, which allowed for the synthesis of well-defined surface-functionalized nanoparticles after cross-linking selectively throughout the shell layer using established amidation chemistry. Functionalization of the chain ends was shown to be an efficient process under standard Click conditions and the resulting functional groups revealed a more “solution-like” environment when compared to the functional group randomly inserted into the hydrophilic shell layer. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 5203–5217, 2006     

Synthesis of poly(p‐phenylene sulfide) from bis(4‐bromophenyl) disulfide

Improved reaction conditions for the preparation of poly(p‐phenylene sulfide) (PPS) directly from bis(4‐bromophenyl) disulfide (BBD) have been established. Heating BBD with magnesium metal afforded only a low molecular weight polymer. PPS with a melting temperature around 280 °C was obtained from BBD in the presence of sodium carbonate or zinc metal. The best results were obtained with the addition of a catalytic amount of KI to the zinc–BBD mixture. Polymers prepared by the above methods are semicrystalline and dissolve in 1‐chloronaphthalene and have properties comparable to commercial PPS. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 900–904, 2006     

Synthesis and characterization of model 3‐miktoarm star copolymers of poly(dimethylsiloxane) and poly(2‐vinylpyridine)

3‐Miktoarm star copolymers, 3μ‐D₂V, with two poly(dimethylsiloxane) (PDMS) and one poly(2‐vinylpyridine) (P2VP) arm, were synthesized by using anionic polymerization–high vacuum techniques and (chloromethylphenylethyl)methyl dichlorosilane, heterofunctional linking agent, with two SiCl groups and one CH₂Cl group. The synthetic strategy involves the selective reaction of the two ? SiCl groups with PDMSOLi living chains, followed by reaction of the remaining chloromethyl group with P2VPLi. Combined molecular characterization results (size exclusion chromatography, membrane osmometry, and ¹H NMR spectroscopy) revealed a high degree of structural and compositional homogeneity. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 614–619, 2006     

Effect of stoichiometry on liquid crystalline supramolecular polymers formed with complementary nucleobase pair interactions

We report herein studies on the liquid crystalline behavior of a series of supramolecular materials that contain different ratios of two complementary symmetrically-substituted alkoxy-bis(phenylethynyl)benzene AA- and BB-type monomers. One monomer has thymine units placed at either end of the rigid mesogenic core, while the other has N⁶-(4-methoxybenzoyl)-adenine units placed on the ends. Differential scanning calorimetric and polarized optical microscopy studies have been carried out on these systems. These studies show that the material's behavior is strongly dependent on its thermal history. As a result, the materials can exhibit, on heating, either a liquid crystalline phase, a crystalline phase, or the coexistence of crystalline and liquid crystalline regions. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 5049–5059, 2006