Correlation between hydrogen‐bonding interaction and mechanical properties of polyimide fibers

Novel co‐polymerization polyimide (PI) fibers based on 4,4′‐oxydianiline (ODA)‐pyromellitic dianhydride (PMDA) were prepared. 2‐(4‐Aminophenyl)‐5‐aminobenzimidazole (PABZ) containing the N? H group was introduced into the structure of the fibers as the proton donor. The results of Fourier transform infrared (FTIR) and dynamic mechanical analysis (DMA) showed that hydrogen bonding occured between the N? H group and chains, which strongly enhanced interchain interaction. This hydrogen bonding interaction increased the tensile strength and initial modulus of the PI fibers up to 2.5 times and 26 times, respectively, compared to those of homo‐PI PMDA‐ODA fibers with no hydrogen‐bonding interaction because of the absence of proton donors after the imidization process. In the mean time, glass transition temperature (T_g) of the modified PI fibers was found to be 410–440°C, which was higher than that of the homo‐PI PMDA‐ODA fibers. From the result, a novel access to molecular design and manufacture of high performance PI fibers with good properties could be provided. Copyright © 2009 John Wiley & Sons, Ltd.     

Flexible nanocrystalline‐titania/polyimide hybrids with high refractive index and excellent thermal dimensional stability

In this study, a novel synthetic route was developed to prepare polyimide–nanocrystalline–titania hybrid optical films with a relatively high titania content (up to 50 wt %) and thickness (20–30 μm) from soluble polyimides containing hydroxyl groups. Two series of newly soluble polyimides were synthesized from the hydroxy‐substituted diamines with various commercial tetracarboxylic dianhydrides. The hydroxyl groups on the backbone of the polyimides could provide the organic–inorganic bonding and resulted in homogeneous hybrid solutions by controlling the mole ratio of titanium butoxide/hydroxyl group. AFM, SEM, TEM, and XRD results indicated the formation of well‐dispersed nanocrystalline‐titania. The flexible hybrid films could be successfully obtained and revealed relatively good surface planarity, thermal dimensional stability, tunable refractive index, and high optical transparency. A three‐layer antireflection coating based on the hybrid films was prepared and showed a reflectance of less than 0.5% in the visible range indicated its potential optical applications. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 1433–1440, 2010     

Proton conductive polyimide ionomer membranes: Effect of NH,OH, and COOH groups

A new series of sulfonated polyimide (SPI) copolymers containing NH, OH, or COOH groups were synthesized by the polycondensation of 1,4,5,8‐naphthalnetetracarboxylic dianhydride, 3,3′‐bis(sulfopropoxy)‐4,4′‐diaminobiphenyl, and 3‐(4‐aminophenyl)‐5‐(3‐aminophenyl)‐1H‐1,2,4‐triazole (SPI‐8‐m), 3,5‐bis(4‐aminophenyl)‐1H‐1,2,4‐triazole (SPI‐8‐p), 3,6‐diaminocarbazole (SPI‐9), 3,5‐diamino‐1H‐1,2,4‐triazole (SPI‐10), bis(3‐aminopropyl)‐amine (SPI‐11), 2,6‐diaminopurine (SPI‐12), 2,4‐diamino‐6‐hydroxyprymidine (SPI‐13), or 3,5‐bis(4‐aminophenoxy)benzoic acid (SPI‐14). The obtained SPIs were soluble in polar organic solvents and gave tough and flexible membranes by solution casting. The SPI membranes having NH and COOH groups showed high thermal (decomposition temperature ≈200 °C) and mechanical (maximum stress >22 MPa) stability. Introducing NH groups, especially triazole and carbazole groups, was effective in improving proton conductive properties of SPI membranes at low humidity. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 2846–2854, 2010     

Novel soluble fluorinated poly(ether imide)s with different pendant groups: Synthesis,thermal, dielectric,and optical properties

Three types of new bis(ether dianhydride) monomers, [4,4′‐(2‐(3′‐methylphenyl)‐1,4‐phenylenedioxy)‐diphthalic anhydride (4a)], [4,4′‐(2‐(3′‐trifluoromethylphenyl)‐1,4‐phenylenedioxy)‐diphthalic anhydride (4b)], and [4,4′‐(2‐(3′,5′‐ditrifluoromethylphenyl)‐1,4‐phenylenedioxy)‐diphthalic anhydride (4c)] were prepared via a multistep reaction sequence. Three series of soluble poly(ether imide)s (PEIs) were prepared from the obtained dianhydrides by a two‐step chemical imidization method. Experimental results indicated that all the PEIs had glass transition temperature in the range of 200–230 °C and the temperature of 5% weight loss in the range of 520–590 °C under nitrogen. The PEIs showed excellent solubility in a variety of organic solvents due to introduction of the bulky pendant groups and were capable of forming tough films. The casting films of PEIs (80–91 μm in thickness) had tensile strengths in the range from 88 to 117 MPa, tensile modulus from 2.14 to 2.47 GPa, and elongation at break from 15 to 27%. The casting films showed UV‐Vis absorption edges at 357–377 nm, low dielectric constants of 2.73–2.82, and water uptakes lower than 0.66 wt %. The spin‐coated films of PEIs presented a minimum birefringence value as low as 0.0122 at 650 nm and low optical absorption at the optical communication wavelengths of 1310 and 1550 nm. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 3281–3289, 2010     

Synthesis and Properties of Hyperbranched Polyimides Combined with Silica

Summary: The novel hyperbranched polyimide - silica hybrid materials containing theoretically 16 wt% of an inorganic phase were prepared via a sol-gel process. An amine terminated polyimide precursor (hyperbranched polyamic acid) was prepared from commercially available monomers 4,4′,4″-triaminotriphenylmethane and 4,4′-oxydiphthalic anhydride in molar ratio 1:1. Tetramethoxysilane and/or 3-glycidoxypropyltrimethoxysilane (also used as a coupling agent) were used as silica precursors. During thermal exposition the polyimide precursor was transformed to hyperbranched polyimide and hydrolyzed alkoxy groups reacted mutually to form silica. The final products were self-standing films, whose structure was characterized by using IR and ¹³C and ²⁹Si solid state NMR spectroscopy. The influence of the amount of silica and/or coupling agent on their structure and thermal properties was described.     

Synthesis and Properties of New Fluorinated Polyimides Derived from an Unsymmetrical and Noncoplanar Diamine

A new unsymmetrical and noncoplanar diamine containing trifluoromethyl and trimethyl groups, 1,4‐bis(4‐amino‐2‐trifluoromethylphenoxy)‐2,3,5‐trimethylbenzene ( 2 ), was synthesized using 2,3,5‐trimethylhydroquinone and 2‐chloro‐5‐nitrobenzotrifluoride as starting materials. A series of fluorinated poly(ether imide)s (PEIs) ( 4a–4d ) were prepared from diamine 2 with four aromatic dianhydrides via a one‐step high‐temperature polycondensation procedure. The obtained PEIs were readily soluble in most organic solvents and could be solution‐cast into flexible and strong films. The resulting thin films exhibited light color and good optical transparency with a cutoff wavelength of 356–376 nm. They also displayed good thermal stability with glass transition temperatures (T_g) above 281°C, 10% weight loss temperatures in the range of 482–486°C, and the weight residue more than 55% at 800°C in nitrogen. Moreover, they revealed low dielectric constants (2.77–2.93 at 1 MHz) and low moisture absorptions (0.41%–0.57%).     

New Soluble Fluorinated Polyimides

Aromatic polyimides have been widely used in aerospace, electrical and electronic applications due to their outstanding thermal stability, mechanical strength at elevated temperature and electrical properties1-3. However, polyimide materials are usually difficulty to fabricate owing to their insolubility in most organic solvents and infusibility. Besides solubility, low moisture uptake of polyimide is also a major concern for microelectronics and optical applications. The present article descr…     

Organosoluble and transparent polyimides derived from alicyclic dianhydride and aromatic diamines

Organosoluble polyimides were synthesized with the alicyclic dianhydride 1,8‐dimethylbicyclo[2,2,2]oct‐7‐ene‐2,3,5,6‐tetracarboxylic dianhydride and aromatic diamines. The polyimides possessed good solubility both in strong dipolar solvents and in common solvents; the thermal decomposition temperature of the polyimides exceeded 420 °C. Strong and flexible films of the polyimides, with the cutoff of ultraviolet–visible absorption lower than 310–320 nm, exhibited good features as the alignment layers for nematic liquid crystals with pretilt angles of 1.5–2.9°. © 2001 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 40: 110–119, 2002     

Synthesis of photoreactive polyimide having indan structure

Polyimide containing an indan unit and alkyl moiety with a high molecular weight was prepared from 5,7‐diamino‐1,1,4,6‐tetramethylindan and 3,3′,4,4′‐benzophenone tetracarboxylic dianhydride. This polyimide was amorphous and soluble in common organic solvents, such as tetrahydrofuran, chloroform, and cyclopentanone. Thermogravimetry of the polyimide showed good thermal stability, indicating that a 10% weight loss of the polyimide was observed at 500 °C in nitrogen. The glass‐transition temperature of the polyimide was not observed by DSC measurement between room temperature and 400 °C at a heating rate of 10 °C/min (Apparatus: DSC3100 MAC Science Co., Ltd.). Transparency of the polyimide at 365 nm was 80%. The polyimide acted as a photosensitive resist of negative type by UV radiation. The resist had a sensitivity of 31 mJ/cm² and a contrast of 2.3 when it was developed with cyclopentanone at room temperature. © 2001 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 40: 423–428, 2002     

Preparation of novel,high‐modulus,swollen‐ or jungle‐gym‐type polyimide gels end‐crosslinked with 1,3,5‐tris(4‐aminophenyl)benzene

A novel preparation approach for high‐performance polyimide gels that are swollen or have a jungle‐gym‐type structure is proposed. A new rigid and symmetric trifunctional amine, 1,3,5‐tris(4‐aminophenyl)benzene (TAPB), was synthesized as a crosslinker. Three different kinds of amic acid oligomers derived from pyromellitic dianhydride (PMDA), 4,4′‐oxydiphthalic anhydride (ODPA), p‐phenylenediamine (PDA), and 4,4′‐oxydianiline (ODA) were end‐crosslinked with TAPB at a high temperature to make polyimide networks with different structures. Transparent polyimide gels were obtained from the ODPA–ODA/TAPB series with high compression moduli of about 1 MPa at their equilibrium swollen states in N‐methylpyrrolidone. Microscopic phase separation occurred during the gelation–imidization process when polyimide networks were generated from PMDA–PDA/TAPB and PMDA–ODA/TAPB. After these opaque polyimide networks were dried, a jungle‐gym‐like structure was obtained for the PMDA–PDA/TAPB and PMDA–ODA/TAPB series; that is, there was a high void content inside the networks (up to 70%) and little volume shrinkage. These polyimide networks did not expand but absorbed the solvent and showed moduli as high as those of solids. Therefore, using the highly rigid crosslinker TAPB combined with the flexible monomers ODPA and ODA and the rigid monomers PMDA and PDA, we prepared swollen, high‐performance polyimide gels and jungle‐gym‐type polyimide networks, respectively. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 2501–2512, 2002