晶化温度对中孔分子筛（M41S）结构转变的影响

在低表面活性剂浓度及低表面活性剂与氧化硅比的条件下，研究了十六烷基三甲基溴化铵－硅酸钠体系中晶化温度对中孔分子筛Ｍ４１Ｓ材料结构转变的影响。结果有，晶化温度提高至１３５℃改变了原六方晶相ＭＣＭ－４１的结构，晶化温度提高到１５０℃后，中孔结构六方ＭＣＭ－４１晶格转变为变不稳定的层状相，     

炭黑填充聚乙烯材料电阻—温度特性研究

研究了炭黑／聚乙烯导电复合材料的ＰＴＣ特性及在不同条件下的电阻变化。发现ＰＴＣ特性与体积膨胀及聚乙烯晶相的熔融有许多一致性。认为材料的体积膨胀及聚乙烯晶相熔融时炭黑颗粒均匀化扩散导致了电阻随温度上升。在较高温度下，炭黑颗粒在分子链段热运动的推动下会发生相对聚集使电阻不断减小，这是材料出现ＮＴＣ现象的原因。材料总的电阻温度特性是体积膨胀、炭黑向聚乙烯熔融区扩散及相互聚集三个因素共同作用的结果。     

高分子基PTC复合材料的研究及其应用

本文概述了高分子基PTC复合材料最近的研究动态，阐述了其作为热敏材料在自控温加热系统和过流保护元件方面的广泛应用。     

镧对含锡、锑残余元素的34CrNi3Mo钢热塑性的改善作用

采用Gleeble-1500热模拟机测定了不同含量的残余元素锡、锑及稀土镧对低氧、低硫的34CrNi3Mo钢热塑性的影响;采用SEM及EDS手段研究了稀土镧对不同锡、锑含量的钢断裂方式的影响及在其中形成夹杂物的情况。结果表明,用稀土金属可以改善低氧、低硫钢中残余元素对钢性能的危害;镧可以和钢中较低含量的锑作用生成镧锑金属间化合物,并且发现了少量的镧锡金属间化合物。     

Synthesis of novel mesoporous silica spheres with starburst pore canal structure

Novel spherical mesoporous silica materials with uniform diameters and starburst mesopore structures were synthesized by a simple one-step procedure with ethanol as the co-solvent in dilute aqueous solution and their formation mechanism was proposed. The arrangement of the pore canal and the diameter of the sphere could be tailored by altering the concentration of ethanol.     

Synthesis, X-ray crystal structures, and gas sorption properties of pillared square grid nets based on paddle-wheel motifs: implications for hydrogen storage in porous materials

A systematic modulation of organic ligands connecting dinuclear paddle-wheel motifs leads to a series of isomorphous metal-organic porous materials that have a three-dimensional connectivity and interconnected pores. Aromatic dicarboxylates such as 1,4-benzenedicarboxylate (1,4-bdc), tetramethylterephthalate (tmbdc), 1,4-naphthalenedicarboxylate (1,4-ndc), tetrafluoroterephthalate (tfbdc), or 2,6-naphthalenedicarboxylate (2,6-ndc) are linear linkers that form two-dimensional layers, and diamine ligands, 4-diazabicyclo[2.2.2]octane (dabco) or 4,4'-dipyridyl (bpy), coordinate at both sides of Zn(2) paddle-wheel units to bridge the layers vertically. The resulting open frameworks [Zn(2)(1,4-bdc)(2)(dabco)] (1), [Zn(2)(1,4-bdc)(tmbdc)(dabco)] (2), [Zn(2)(tmbdc)(2)(dabco)] (3), [Zn(2)(1,4-ndc)(2)(dabco)] (4), [Zn(2)(tfbdc)(2)(dabco)] (5), and [Zn(2)(tmbdc)(2)(bpy)] (8) possess varying size of pores and free apertures originating from the side groups of the 1,4-bdc derivatives. [Zn(2)(1,4-bdc)(2)(bpy)] (6) and [Zn(2)(2,6-ndc)(2)(bpy)] (7) have two- and threefold interpenetrating structures, respectively. The non-interpenetrating frameworks (1-5 and 8) possess surface areas in the range of 1450-2090 m(2)g(-1) and hydrogen sorption capacities of 1.7-2.1 wt % at 78 K and 1 atm. A detailed analysis of the sorption data in conjunction with structural similarities and differences concludes that porous materials with straight channels and large openings do not perform better than those with wavy channels and small openings in terms of hydrogen storage through physisorption.     

无机层状复合氢氧化物中顺铂-DNA模型分子的选择性插入

药物分子的选择性包裹和控制释放是药物研究领域中具有挑战性的研究方向。本文研究表明:顺铂-DNA模型分子cis-[Pt(NH₃)₂(5′-GMP)₂](5′-GMP 5′-单磷酸鸟苷)可插入无机层状复合氢氧化物[Zn_0.68Al_0.32(OH)₂](NO₃)_0.32·mH₂O。但另一种层状复合氢氧化物[LiAl₂(OH)₆]Cl·H₂O由于其阳离子层中正电荷密度较高、阳离子层与层间阴离子之间静电作用较强,因而顺铂-DNA模型分子不能通过离子交换方式插入其层间。光谱数据证实插入层间的顺铂-DNA模型分子结构不变。这可能为铂-DNA分子的传递提供新的方法。