薄膜沉积过程中TiO_2的金红石相向锐钛矿相转变

用ＲＦ磁控放电方法以纯金属钛做靶材在氩氧混合气体中制备了ＴｉＯ２薄膜,Ｒａｍａｎ光谱测量表明,在２Ｐａ工作气压下制备的ＴｉＯ２薄膜为锐钛矿结构,而在０２Ｐａ工作气压下制备的是金红石结构。工作气压的改变引起了ＴｉＯ２薄膜沉积中的相转变。     

Studying surfaces and thin films using Mössbauer spectroscopy

Using a series of bi-layer samples, we show how Conversion Electron Mössbauer Spectroscopy (CEMS) and X-ray Backscatter Mössbauer Spectroscopy (XBS) can be done with the same experimental set up. The penetration depths of the K and L conversion electrons are measured as 51(6) and 330(240) nm, respectively, with relative contributions of 88(9) and 12(9)%. The penetration depth of the Fe-K _α X-ray signal is determined to be 3.6(2) μm. As a demonstration we show data on surface damage effects in electropolished TRIP steels, and by comparing CEMS and XBS Mössbauer patterns we estimate the thickness of a damaged layer (created by sanding) to be 550(50) nm.     

Dc and ac electrical conductivity of bulk CdSexTe1−x (0x0.4)

Measurements of the dc and ac conductivity were made for polycrystalline CdSe_xTe_1−x (0x0.4) at various frequencies (0.1–100 kHz) and at various temperatures (293–413 K). The temperature dependence of the dc conductivity was measured in the temperature range (293–413 K). It was found that the obtained dc activation energy for the investigated compositions decrease with the increase of Se content. The ac conductivity is found to be frequency and temperature dependent and obeys the Aω^s law, where s decreases with the increase of temperature. The ac conductivity of these compositions are explained on the basis of the correlated barrier hopping model.     

Adsorption of a semiflexible wormlike chain

Adsorption of ideal polymers with stiff backbone onto a flat surface is considered theoretically. Both scaling approach and quantitative theory are developed. We predict a self-similar monomer concentration profile c(x) ∼ x ^-4/3 near the surface (when the distance to the surface x is much smaller than the chain persistence length l /2). The typical conformation of a weakly adsorbed chain can be viewed as a sequence of alternating flat (2-dimensional) trains of wormlike short loops (flat blobs) and coil-like (3-dimensional) loops forming a triple-layer structure: contact layer (x < Δ) of adsorbed fragments virtually laid on the surface, proximal layer (Δ < x < l) of flat blobs, and more dilute distal corona layer (x > l). Here Δ defines the range of monomer/surface attraction, Δ ≪ l. The adsorption transition is continuous. However, its relative width is small (T ^* is the adsorption temperature, ΔT is the relevant temperature interval): ∼ , i.e. a discontinuous transition in the limit Δ/l↦ 0. Received 10 October 2002 and Received in final form 22 November 2002 RID="a" ID="a"Permanent address: Physics Department, Moscow State University, Moscow 119992, Russia. e-mail: semenov@polly.phys.msu.ru     

金纳米空心半球壳膜的可调谐光学性质研究

以单层聚苯乙烯微球阵列为模板,通过控制其表面金膜蒸镀时间,制备了具有不同厚度的空心半球壳结构的金纳米膜.利用扫描电子显微镜和自制光谱仪分别测量了金膜表面形貌和其透射光谱,并分析了金膜形貌与其光学性质间的关系,同时以4-巯基苯胺为探针分子测定了金膜的表面增强喇曼散射效应.结果表明,该金纳米膜的表面等离子体共振波长随膜厚度增大而发生红移,在可见与近红外波段较宽范围内可调谐,并且,当金膜共振波长与入射激发光波长较近时,探针分子可产生出较强的表面增强喇曼信号.同时,对该现象的产生机制也进行了理论解释.     

Polyelectrolytes tethered to a free surface

Several attempts have been already carried out in order to tether charged chains by an end at a free fluctuating surface. We review here most of these attempts and focus on how close the physics of charged brushes can be investigated by such an approach. We first describe results about films of charged-neutral diblock copolymers spread at the surface of water. Results can be mostly rationalized in terms of charged brushes although additional structurations and fluctuations of the interface can be observed. The latter deformations are also observed when adsorbed layers of charged-neutral diblock copolymers are considered. At last, we examine how free suspended films of charged-neutral diblock copolymers can be viewed as two opposing charged brushes, both in terms of thickness and pressure. Received 9 May 2000     

Development of plasticised PVC sensing films for the determination of BTEX compounds in aqueous samples

A novel plasticised PVC polymer membrane as a sensing film for the determination of BTEX compounds using ATR-FTIR spectroscopy is demonstrated. A range of 10 plasticised PVC phases have been investigated using toluene and tetrachloroethylene as test analytes. Both analyte enrichment rates and infrared absorbance values were considered when choosing a suitable polymer for sensing. An enhancement in analyte absorbance at the characteristic IR absorption bands was noted as the plasticiser concentration in the film was increased. 2% PVC with 75% diisooctyl azelate was found to show promising results for simultaneous determination of the BTEX compounds. All BTEX analytes can be measured in less than 8 min. A study of a multicomponent sample demonstrated that analyte enrichment times were influenced by the presence of even one additional analyte component in the sample.     

Effect of the rate of deformation on the crystallization behavior of polymers

Deformation has a significant influence on the crystallization process in a number of polymers. In this paper, the response of a recently developed model for crystallizing polymers is investigated when subject to uni-, bi-axial and constant width extensions for a range of strain rates. Both the loading and unloading behavior are examined for these deformations. The particular model studied here was developed to capture the effect of strain induced crystallization in polymers and has been applied to model crystallization in polyethylene terephthalate at temperatures just above its glass transition temperature. The model has been formulated using the notion of multiple natural configurations within a full thermodynamic framework. The connection between micro-structural changes taking place in the polymer and the form of the model are elucidated. The interplay between the relaxation processes, the rate of deformation and their combined effect on crystallization is illustrated. The results show an earlier onset of crystallization for high strain rates due to stretching of the polymer network. At low strain rates however, crystallization is not observed as the polymer network is able to relax during the deformation. A sharp upturn in the stress is observed after the onset of crystallization due to the formation of a rigid crystalline phase. The unloading curves clearly show a hysteric behavior with the amount of dissipation increasing for increasing values of strain rate. These results compare favorably with experimental observations available in literature.     

Vibrational Study of Dipotassium Zinc Bis(Dihydrogendiphosphate) Dihydrate,K2ZN(H2P2O7)2·2H2O

Abstract

Infrared and Raman spectra of dipotassium zinc bis(dihydrogendiphosphate) dihydrate, K₂Zn(H₂P₂O₇)₂ .2H₂O have been collected and interpreted using factor group analysis. Noncoincidence of the Raman and infrared spectra bands confirms a centrosymmetric structure for K₂Zn(H₂P₂O₇)₂ .2H₂O previously investigated by X-ray structural study, as well as the joint appearance of ν_as POP and ν_s POP point to a bent POP configuration.     

PREPARATION AND PHYSICAL PROPERTIES OF BLEND FILMS FROM SODIUM ALGINATE AND POLYACRYLAMIDE SOLUTIONS

Blend films of sodium alginate and polyacrylamide (PAAm) were prepared by mixing the aqueous solution of both samples at a different ratio. All blend films obtained are optically clear to the naked eye. The structure and physical properties of the films were studied by FT-infrared (FT-IR), wide angle X-ray diffraction (WAXD), differential thermal analysis (DTA), thermogravimetic analysis (TGA), scanning electron microscopy (SEM), and tensile strength test. The results showed that the occurrence of interactions between -COO^?, -OH groups of sodium alginate and -CONH₂ groups of PAAm in the blends through hydrogen formation. The blend films exhibited the higher thermal stability and improved mechanical properties in dry states. These properties had the maximum value around 20 wt% PAAm content in the blend film. The morphological transition of the blend films from sodium alginate-like to PAAm-like was observed by scanning electron microscopy.