Catalysis by Using TiO2 Nanoparticles and Nanotubes

TiO2 has attracted considerable attention due to its stability, non-toxicity, low cost, and great potential for use as a photocatalyst in environmental applications. Since strong metal-support interaction (SMSI) of titania-supported noble metals was first reported in 1978, titania supported catalyst has been intensively studied in heterogeneous catalysis. However, the effective catalytic activity was restricted due to the low surface area of TiO2. Recently, TiO2-based nanotubes were extensively investigated because of their potentials in many areas such as highly efficient photocatalysis and hydrogen sensor.In the present study, formation of titanium oxide (TiO2) nanotubes was carried out by hydrothermal method, with TiO2 nanoparticle-powders immersed in concentrated NaOH solution in an autoclave at 110 ℃. Preparation of nano-size Pt on TiO2-nanoparticles or TiO2-nanotubes was performed by photochemical deposition method with UV irradiation on an aqueous solution containing TiO2 and hexachloroplatinic acid or tetrachloroauric acid. The TEM micrographs show that TiO2-nanotubes exhibit ～300 nm in length with an inner diameter of ～ 6 nm and the wall thickness of ～ 2 nm, and homogeneous nanosize Pt particles (～ 2 nm) were well-dispersed on both nanoparticle- and nanotube- titania supports. It also shows the nanotube morphology was retained up2o n Pt-immobilization. Nitrogen adsorption isotherm at 77K resulted a high surface area (～ 200m/g) of TiO2-nanotubes, which is about 40 times greater than that of "mother" TiO2 nanoparticles (～5 m/g). All the spectroscopic results exhibited that the nanotube structure was not significantly affected by the immobilized Pt particles. Ti K-edge XANES spectra of TiO2 nanotube and Pt/TiO2-nanotube represent that most titanium are in a tetrahedral coordination with few retained in the octahedral structure.In the in-situ FT-IR experiments, an IR cell was evacuated to a pressure of 10-5 torr at room temperature as soon as the catalyst-pellet, Pt/TiO2 or Pt/TiO2-nanotube, was placed inside the cell.Then, 60 torr of hydrogen was introduced into the cell and subsequently the temperature was programmed to increase from room temperature to 300℃ at a constant heating rate of 5℃/min.For Pt/TiO2, an IR peak at 2083 em-1 started to appear at 200℃ with a maximum intensity at 250℃ and then decreasing as temperature increased. The 2083 em-1 IR peak corresponds to the linearly adsorption of CO on the well-dispersed Pt sites. Simultaneously, the IR bands of gaseous methane at 3016 em-1 started to appear at 225℃ and the peak intensity increased with temperature. The results reveal that Pt/TiO2 can adsorb gaseous CO2 and further catalyzes the reduction of CO2 by H2 through the intermediate CO, which further produces gaseous methane. While for the Pt/TiO2-nanotube catalyst, methane was produced at relatively low temperature, 100℃, and it catalyzed the direct conversion of CO2 to CH4. The absence of intermediate CO-adsorption signals durinng the temperature programmed process indicates that the prepared TiO2 nanotube-supported nanosize Pt possesses a potent capability for CO2 adsorption and highly catalytic activity in the hydrogenation of CO2, and was superior to the conventional Pt/TiO2 catalyst. The catalytic activity of Pt/TiO2-nanotube was indeed significantly enhanced by the high surface area of TiO2-nanotubes.Details will be discussed.     

MoO_3、NiO、ZnO在小表面金红石上的分散行为

氧化物、盐类在氧化物载体表面的自发分散是一种广泛存在的现象，文献中已报导过大量氧化物和盐类在高比表面载体上分散的研究结果［'－3］TIO。作为一种较新型的载体，与Y－AI。O。、硅胶等传统载体相比，有许多不同特性．活性组分在TIO。表面的分散状态及所得催化剂的性能已有不少报导［'－'］，但所用的TIOZ主要是较高比表面的锐钛矿型TIOZ（刘金红石型TIO。（r）和锐钛矿型TIOZ（a）的结构不同，它是高温生成相，比表面较小［'］．氧化物在金红石上的分散行为仍未见报导．我们制备了三种具有不同比表面的TIO水），系统地研…     

Gas Phase Catalysis by Metal Nanoparticles in Nanoporous Alumina Membranes

Nanoporous alumina membranes, loaded with palladium and ruthenium nanoparticles of various size, were used for gas phase hydrogenation of 1, 3‐butadiene and for oxidation of carbon monoxide, respectively. Those membranes contain 10⁹ ‐ 10¹¹ pores per cm², all running perpendicular to the surface. Membrane discs of 20 mm in diameter and only 60 μm thick, incorporated in a reactor in which the reactants can be pumped in a closed circuit through the pores, turned out to very actively catalyze hydrogenation of butadiene (Pd) and oxidation of CO (Ru). The activity of the Pd catalysts depends characteristically on the particles size, the gas flow, and of the educts ratio. As could be expected, larger particles are less active than smaller ones, whereas increasing gas flows in case of hydrogenation accelerates the reactions. Excessive hydrogen reduces selectivity with respect to the various butenes, but favours formation of butane.     

The thermal conductivity of alumina nanoparticles dispersed in ethylene glycol

The thermal conductivities of several nanofluids (dispersions of alumina nanoparticles in ethylene glycol) were measured at temperatures ranging from 298 to 411 K using a liquid metal transient hot wire apparatus. Our measurements span the widest range of temperatures that have been investigated to date for any nanofluid. A maximum in the thermal conductivity versus temperature behavior was observed at all mass fractions of nanoparticles, closely following the behavior of the base fluid (ethylene glycol). Our results confirm that additional temperature contributions inherent in Brownian motion models are not necessary to describe the temperature dependence of the thermal conductivity of nanofluids. Our results also show that the effect of mass or volume fraction of nanoparticles on the thermal conductivity of nanofluids can be correlated using the Hamilton and Crosser or Yu and Choi models with one adjustable parameter (the shape factor in the Hamilton and Crosser model, or the ordered liquid layer thickness in the Yu and Choi model).     

Effect of WO3 particle size on the type and concentration of surface oxygen

1. Download : Download high-res image (65KB)
2. Download : Download full-size image

     

沉淀溶解法制备纳米硫化锌

以烷基黄原酸锌和硫化钠分别为锌源和硫源，采用烷基黄原酸锌沉淀溶解法制备了粒度可调、粒径分布比较窄的面心硫化锌纳米粒子，利用比表面积(BET)测定、透射电镜(TEM)、粉末X射线衍射(XRD)、傅里叶转换红外光谱(FTIR)等方法对合成的硫化锌纳米粒子进行了表征。结果表明随着烷基黄原酸锌链长的增长，通过添加硫化钠而生成的硫化锌纳米粒子的粒径逐渐减小。本文还对沉淀溶解法制备纳米硫化锌的溶液化学反应机理进行了探讨。     

表面修饰纳米CdS制备中两个重要影响因素及结构表征

利用溶胶-凝胶法制备了PVP表面修饰的CdS纳米晶粒。考察了影响纳米CdS制备的两个重要因素Cd²⁺/S^2-和PVP,及其作用机理。确证表面过剩S^2-和PVP在反应体系中的作用是在较高浓度下制备纳米CdS的两个重要因素,进一步确定了PVP的最佳用量。通过TEM、ED、XRD、FT-IR等手段对合成的纳米粒子进行了结构表征,最小粒径为7～10nm,闪锌矿构型,粒子大小及形貌可通过改变Cd²⁺/S^2-及反应物浓度来控制。最后给出了CdS/PVP纳米晶粒的结构模型。     

Plasmid DNA isolation using amino-silica coated magnetic nanoparticles (ASMNPs)

A simple and efficient approach for the rapid isolation of plasmid DNA from crude cell lysates has been described. The approach took advantage of the amino-modified silica coated magnetic nanoparticles (ASMNPs) with positive zeta potential at neutral pH and superparamagnetism under the external magnetic fields. As a demonstration, the pEGFP-N3 plasmid has been concentrated and isolated from the E. coli DH5α transformed with pEGFP-N3 plasmid through electrostatic binding between the positive charge of the amino group of ASMNPs and the negative charge of the phosphate groups of the plasmid DNA. Then the pEGFP-N3 plasmid has been released easily and quickly from the pEGFP-N3 plasmid-ASMNPs complexes with 3 M NaCl. The entire procedure could be carried out by the aid of external magnetic fields in 15 min and eliminate the need of phenol, cesium chloride gradients or other noxious reagents and complexes operation. Moreover, the pEGFP-N3 plasmid obtained by this approach retains biological activity that can be suitable for restriction enzyme digestion and cells transfection with expression of green fluorescence protein.     

A method to construct polyelectrolyte multilayers film containing gold nanoparticles

Gold nanoparticles in polyelectrolyte multilayers film can be easily prepared by repeating immersion of a substrate in poly(diallyl dimethylammonium) chloride (PDDA)-AuCl₄⁻ complexes solution followed by reduction Au³⁺ through heating. UV-vis spectroscopy, cyclic voltammetry (CV) and tapping-mode atomic force microscopy (AFM) are used to confirm the successful construction of the polyelectrolyte multilayers film and the formation of gold nanoparticles. The multilayers film shows electrocatalytic activity to dioxygen reduction.     

硫化锌掺锰/聚乙烯醇复合纳米纤维的制备与表征

利用静电纺丝法与气固反应相结合, 成功地制备了硫化锌掺锰/聚乙烯醇复合纳米纤维, 并对所制备的复合物进行了表征, 探讨了复合物的结构及其性能.