Novel reaction of 1-aryl-2-bromodiazene 1-oxides with olefins. Synthesis of 1-aryl-2-(2-bromoalkyl)diazene 1-oxides

The addition of 1-aryl-2-bromodiazene 1-oxides to olefins yields 1-aryl-2-(2-bromoalkyl)diazene 1-oxides (4). A radical mechanism of the reaction has been suggested. Compounds4 decompose to give bromohydrazones of formaldehyde and aldehydes. The structural factors that affect the rate of this process are discussed.Translated fromIzvestiya Akademii Nauk. Seriya Khimicheskaya, No. 5, pp. 917–923, May, 1995.The work was carried out in the Scientific Educational Center of the Institute of Organic Chemistry of the RAS with financial support of the Russian Foundation for Basic Research (Project No. 93-03-18461).     

Formation of α-Mn2O3 nanorods via a hydrothermal-assisted cleavage-decomposition mechanism

A hydrothermal cleavage-decomposition mechanism was used to synthesize single-crystal α-Mn₂O₃ nanorods at 160 °C for 16 h using KMnO₄ as manganese source and CTAB as reducing regent. The as-synthesized products were characterized by powder X-ray diffraction, transmission electron microscopy, high-resolution transmission electron microscopy and infrared spectrum. The results indicate that the reaction temperature is a crucial factor for the formation of α-Mn₂O₃ nanorods. These nanorods exhibit single-crystal nature, and have an average diameter of 36 nm and lengths of up to 1 μm. Based on our experimental results, a hydrothermal cleavage-decomposition mechanism has been proposed on the formation of α-Mn₂O₃ nanorods.     

Electron Probe Microanalysis of HfO2 Thin Films on Conductive and Insulating Substrates

Quantitative electron probe microanalysis of highly insulating materials is a complicated problem, partially solved by coating samples with grounded thin conductive layers or using novel scanning electron microscopy (SEM) techniques, such as low-voltage and/or variable pressure SEM. In this work, some problems of quantitative X-ray microanalysis of thin HfO₂ films, in particular the possibility to determine mass thickness correlated to the density of the layer material, are discussed. For comparison, Al₂O₃, Ta₂O₅ and TiO₂ films grown onto both semiconductive Si and insulating quartz substrates were also analysed. All the films studied were synthesized by atomic layer deposition method.     

Role of the surface heterogeneity in adsorption of hydrogen ions on metal oxides: theory and simulations

In this article we study the effect of energetic heterogeneity of a crystalline surface on the adsorption of hydrogen ions (protons) from the liquid phase. In particular, we examine the influence of the shape of the adsorption energy distribution on the equilibrium isotherms of hydrogen ions. To that purpose, a few popular distribution functions, including rectangular, exponential, and asymmetric Gaussian are considered. Additionally, multimodal distribution functions, which may correspond to the adsorption on different crystal planes of the oxide, are also used. Lateral interactions between adsorbed charges are modeled using the potential function proposed by Borkovec et al., which accounts also for polarization of the liquid medium. The results presented here are obtained using both Monte Carlo (MC) simulations and theoretical calculations involving Mean Field Approximation (MFA). They indicate that increased energetic heterogeneity of the adsorbing surface may, in general, considerably change the behavior of the adsorption isotherms, regardless of the assumed distribution function. It is also shown that the predictions of the proposed theory are consistent with the data obtained from the MC simulations.     

A density functional study on magnetic exchange interaction between Mn(II) ion and nitronyl nitroxide radical in <Emphasis Type="Italic">trans</Emphasis>-and <Emphasis Type="Italic">cis</Emphasis>-metal-radical complexes

The magneto-structural correlation between a Mn(ll) ion, coordinated in an octahedral environment, and two nitronyl nitroxide radical ligands in trans- and cis-metal-radical complexes is investigated by the broken symmetry (BS) approach within density functional theory (DFT). The dependences of coupling constants J on three structural parameters: (i) bond angle θ (Mn-O-N (nitroxide)); (ii) rotating angle ψ, defined by the nitronyl nitroxide radical plane rotating around the axial Mn-O (nitroxide); (iii) bond distance R (Mn-O (nitroxide)) are directly calculated. Our calculations showed that both trans- and cis-Mn(ll)-radical complexes behave a stronger antiferromagnetic interaction, consistent with experiments. In view of molecular orbital theory, the direct exchanges, including σ-type and π-type exchanges, are responsible for the magnetic exchange pathways. There is a preferable linear correlation between the calculated coupling constants J and the overlap integral squares S b between the local magnetic orbitals at the various rotating angle ψ at the fixed bond angle θ and bond distance R, in both trans- and cis-Mn(ll)-radical complexes.     

A new method for the synthesis of diorganylvinylphosphine oxides

Diorganylvinylphosphine oxides were synthesized in 31–38% yields on heating (50°C) diorganylphosphine oxides with vinyl sulfoxides or divinyl sulfone in the presence of KOH. Translated fromIzvestiya Akademii Nauk. Seriya Khimicheskaya, No. 10, pp. 1895–1896, October, 1997.     

The surface and materials science of tin oxide

The study of tin oxide is motivated by its applications as a solid state gas sensor material, oxidation catalyst, and transparent conductor. This review describes the physical and chemical properties that make tin oxide a suitable material for these purposes. The emphasis is on surface science studies of single crystal surfaces, but selected studies on powder and polycrystalline films are also incorporated in order to provide connecting points between surface science studies with the broader field of materials science of tin oxide. The key for understanding many aspects of SnO₂ surface properties is the dual valency of Sn. The dual valency facilitates a reversible transformation of the surface composition from stoichiometric surfaces with Sn⁴⁺ surface cations into a reduced surface with Sn²⁺ surface cations depending on the oxygen chemical potential of the system. Reduction of the surface modifies the surface electronic structure by formation of Sn 5s derived surface states that lie deep within the band gap and also cause a lowering of the work function. The gas sensing mechanism appears, however, only to be indirectly influenced by the surface composition of SnO₂. Critical for triggering a gas response are not the lattice oxygen concentration but chemisorbed (or ionosorbed) oxygen and other molecules with a net electric charge. Band bending induced by charged molecules cause the increase or decrease in surface conductivity responsible for the gas response signal. In most applications tin oxide is modified by additives to either increase the charge carrier concentration by donor atoms, or to increase the gas sensitivity or the catalytic activity by metal additives. Some of the basic concepts by which additives modify the gas sensing and catalytic properties of SnO₂ are discussed and the few surface science studies of doped SnO₂ are reviewed. Epitaxial SnO₂ films may facilitate the surface science studies of doped films in the future. To this end film growth on titania, alumina, and Pt(1 1 1) is reviewed. Thin films on alumina also make promising test systems for probing gas sensing behavior. Molecular adsorption and reaction studies on SnO₂ surfaces have been hampered by the challenges of preparing well-characterized surfaces. Nevertheless some experimental and theoretical studies have been performed and are reviewed. Of particular interest in these studies was the influence of the surface composition on its chemical properties. Finally, the variety of recently synthesized tin oxide nanoscopic materials is summarized.     

共沉淀浸渍法制备由合成气直接合成二甲醚的Cu-Mn催化剂

采用共沉淀浸渍法,制备了直接合成二甲醚的Cu-Mn-Zn催化剂,通过对组成成分及其配比的研究,发现Cu含量一定的条件下,n(Zn)/n(Mn)摩尔比对催化剂性能有较大的影响,当n(Zn)/n(Mn)=1/3～1/2时,催化剂对CO的转化率和对二甲醚的选择性达到最佳,分别为53.6%和63.5%；如锰添加比例过大,对催化剂催化合成二甲醚有微弱抑制；添加锌比例过大,会大大降低CO的转化率。载体Y分子筛的含量对催化剂性能也有影响,用量过大将降低催化剂的活性和对二甲醚的选择性,当其含量为33%时,催化剂上CO转化率和选择性可分别达到66%和68%,且催化剂活性随分子筛含量减少不再有明显的变化。     

用MES及XRD研究FT合成催化剂的活性结构

采用穆斯堡尔谱及Ｘ光衍射法研究了共沉淀法制备的不同Ｆｅ／Ｍｎ比催化剂在焙烧、合成气还原及ＦＴ反应后体系相结构的变化。结果表明：锰助剂的加入使催化本相由铁磁性逐渐转化为超顺磁性，相应使催化剂还原逐渐难，Ｍｎ助剂促进了ＦＴ合成反应进行。反应性能与Ｆｅ／Ｍｎ尖晶石（Ｆｅ１－ｙＭｎｙ）３Ｏ４组成含量及式中ｙ大小密切相关，与ＭｎＣｏ３及ＭｎＯ的存在也有一定关系。富铁催化剂中Ｍｎ主要起电子助剂作用，而富锰催化     

Towards supramolecular fixation of NOX gases: encapsulated reagents for nitrosation

The use of simple calix[4]arenes for chemical conversion of NO2/N2O4 gases is demonstrated in solution and in the solid state. Upon reacting with these gases, calixarenes 1 encapsulate nitrosonium (NO+) cations within their cavities with the formation of stable calixarene-NO+ complexes 2. These complexes act as encapsulated nitrosating reagents; cavity effects control their reactivity and selectivity. Complexes 2 were effectively used for nitrosation of secondary amides 5, including chiral derivatives. Unique size-shape selectivity was observed, allowing for exclusive nitrosation of less crowded N-Me amides 5 a-e (up to 95 % yields). Bulkier N-Alk (Alk>Me) substrates 5 did not react due to the hindered approach to the encapsulated NO+ reagents. Robust, silica gel based calixarene material 3 was prepared, which reversibly traps NO2/N2O4 with the formation of NO+-storing silica gel 4. With material 4, similar size-shape selectivity was observed for nitrosation. The N-Me-N-nitroso derivatives 6 d,e were obtained with approximately 30 % yields, while bulkier amides were nitrosated with much lower yields (<8 %). Enantiomerically pure encapsulating reagent 2 d was tested for nitrosation of racemic amide 5 t, showing modest but reproducible stereoselectivity and approximately 15 % ee. Given high affinity to NO+ species, which can be generated by a number of NOX gases, these supramolecular reagents and materials may be useful for NOX entrapment and separation in the environment and biomedical areas.