Mutual influence of the morphology and capillary rheological properties in nylon/glass‐fiber/liquid‐crystalline‐polymer blends

Nylon‐6/glass‐fiber (GF)/liquid‐crystalline‐polymer (LCP) ternary blends with different viscosity ratios were prepared with three kinds of nylon‐6 with different viscosities as matrices. The rheological behaviors of these blends were characterized with capillary rheometry. The morphology was observed with scanning electron microscopy and polarizing optical microscopy. This study showed that although LCP did not fibrillate in binary nylon‐6/LCP blends, LCP fibrillated to a large aspect ratio in some ternary blends after GF was added. The addition of 5 wt % LCP significantly reduced the melt viscosity of nylon‐6/GF blends to such an extent that some nylon‐6/GF/LCP blends had quite low viscosities, not only lower than those of neat resins and nylon‐6/GF blends but also lower than those of corresponding nylon‐6/LCP blends. The mutual influence of the morphology and rheological properties was examined. The great reduction of the melt viscosity was considered the result of LCP fibrillation. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 1619–1627, 2004     

Structure of a poly(2,5‐benzimidazole)/phosphoric acid complex

As‐cast films of poly(2,5‐benzimidazole) exhibit uniplanar orientation in which the planes of the aromatic rings lie parallel to the film surface. Upon doping with phosphoric acid, the original crystalline order is lost, but the doped film can be stretched to produce films with uniaxial orientation. After thermal annealing at 540 °C, nine Bragg reflections are resolved in the fiber diagram, and these are indexed by an orthorhombic unit cell with the dimensions a = 18.1 Å, b = 3.5 Å, and c = 11.4 Å, containing four monomer units of two chains. The absence of odd‐order 00l reflections points to a 2₁ chain conformation, which is probably planar so that the aromatic units can be stacked along the b axis. The water and phosphoric acid contents of the crystalline structure cannot be determined exactly because of the presence of extensive amorphous regions that probably have different solvation. The best agreement between the observed and calculated intensities is for an idealized structure containing two phosphoric acids and two water molecules per unit cell. However, the phosphoric acid is probably present mainly in the form of pyrophosphoric acid and its higher oligomers. In addition, the X‐ray data are consistent with a more disordered structure containing chains with random (up and down) polarity and a lack of c‐axis registry. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 2576–2585, 2004     

Plasticized microporous poly(vinylidene fluoride) separators for lithium-ion batteries. III. Gel properties and irreversible modifications of poly(vinylidene fluoride) membranes under swelling in liquid electrolytes

Microporous poly(vinylidene fluoride) (PVdF) separators for lithium-ion batteries, used in liquid organic electrolytes, have been characterized with respect to the swelling phenomena on dense PVdF membranes (obtained through hot pressing). In the first and second parts of this study, we have described the swelling equilibria and swelling kinetics of dense PVdF. Here the thermal properties of PVdF gels and their irreversible modifications induced by swelling are characterized. Particular attention is paid to crystallinity modifications, polymer plasticization, and membrane degradation. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 2308–2317, 2004     

Statistical thermodynamics evaluation of polymer–polymer miscibility

The Simha and Somcynsky (S–S) statistical thermodynamics theory was used to compute the solubility parameters as a function of temperature and pressure [δ = δ(T, P)], for a series of polymer melts. The characteristic scaling parameters required for this task, P*, T*, and V*, were extracted from the pressure–temperature–volume (PVT) data. To determine the potential polymer–polymer miscibility, the dependence of δ versus T (at ambient pressure) was computed for 17 polymers. Close proximity of the δ versus T curves for four miscible polymer pairs: PPE/PS, PS/PVME, and PC/PMMA signaled the usefulness of this approach. It is noteworthy, that the tabulated solubility parameters (derived from the solution data under ambient conditions) propounded the immiscibility of the PVC/PVAc pair. The computed values of δ also suggested miscibility for polymer pairs of unknown miscibility, namely PPE/PVC, PPE/PVAc, and PET/PSF. In recognizing the limitations of the solubility parameter approach (the omission of several thermodynamic contributions), these preliminary results are auspicious because they indicate a new route for estimating the miscibility of any polymeric material at a given temperature and pressure. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 2909–2915, 2004     

Cr3+：MgAl2O4晶体EPR参量及其电子精细光谱的研究

考虑了SS(Spin-Spin)作用和SOO(Spin-Other-Orbit)作用，采用完全对角化方法，结合自旋Hamiltonian理论，研究了Cr³⁺∶MgAl₂O₄晶体EPR参量及其吸收光谱，理论与实验符合甚好. 在此基础上，进一步研究了⁴A₂(3d³)离子EPR参量的微观起源. 研究表明，EPR参量起源于四种微观机制：(1) SO(Spin-Orbit) 耦合机制；(2) SS耦合机制；(3)SOO耦合机制；(4) SO～SS～SOO总联合作用机制. 在这些机制中，SO机制是最主要的.     

旋光性与电光效应交互作用及其对旋光晶体电光Q开关的影响

研究了晶体的旋光性与电光效应的交互作用、以及此交互作用对 旋光晶体电光Q开关的影响. 关键词： 旋光性 电光效应 电光Q开关 3Ga₅SiO₁₄晶体')" href="#">La₃Ga₅SiO₁₄晶体     

掺杂偶氮苯聚合物光致异构Z扫描测量及其理论解释

用He_Ne激光对掺有偶氮苯聚合物DR 13的PMMA薄膜样品进行Z扫描研究 ,发现其折射率改变量与光强的关系存在着饱和效应 ,且线偏振光引起的折射率改变明显大于圆偏振光引起的折射率改变 .对于这些现象 ,用光致异构的角烧孔机理进行解释     

Yb:FAP和Yb:C_3S_2-FAP晶体光谱的温度特性和选择激发

报导了Yb :FAP和Yb :C3S2 _FAP晶体在不同温度下的吸收光谱和荧光光谱实验结果 ,研究发现由于电子_声子近共振耦合作用 ,Yb :FAP和Yb :C3S2 _FAP晶体均存在有明显的振动谱 ,Yb :FAP晶体的零声子线在低温下还劈裂为相差 10cm- 1 的两条线 .采用激光选择激发技术研究了Yb3 离子在FAP和C3S2 _FAP晶体中的格位特征 ,结果表明Yb3 离子在这两种基质中都只占据Ca(Ⅱ )格位 ,但由于CaF2 的挥发 ,导致了Ca(Ⅱ )格位的局部畸变 .     

Two-Layered Poly-o-phenylenediamine/Polyaniline Composite: Electrosynthesis and Spectroelectrochemical Properties

Spectroelectrochemical properties of poly-o-phenylenediamine (PPD) and the synthesized composite of PPD and polyaniline—two chemically related polymers containing an amino-substituted benzene ring but having different conduction nature—are studied. The polyaniline synthesis on PPD-modified electrodes involves stages of the reaction initiation, the copolymer formation, and the formation of a polyaniline layer at the copolymer/solution interface.     

Synthesis of Cationic PEM Emulsion and Application in Waste Water Treatment

Cationic polymer as a kind of flocculant is widely applied in purification treatment of waste water. Because it has positive charge group, it is able to connect strongly the suspended matters, short cellulose and other microparticles. The research on synthesis of cationic polymer and application in treatment of waste water is very universal abroad. But domestic research on those is not general. The technology of synthesis of PEM is simple, and the production cost is low. It is easy to apply in treatment of waste water.Synthesis of PEM Emulsion FlocculantSome distilled water, PVA(poly(vinyl alcohol)), EA(ethyl acrylate), and K2S2O8(potassium persulfate) were put into reaction vessel. Kept stirring up under nitrogen. When heated the solution to 40℃, dropped the water solution of MTA[(2-methacryloxylethyl)trimethyl ammonium].Maintained the temperature at 70℃, reacted about 7-8 hours. Then got the PEM emulsion. Changed the ratio of EA and MTA. Obtained a series of PEM emulsions.Stability and Convertibility of PEM EmulsionThe test results showed that when the EA/MTA was 85/15, the PEM emulsion was most stable.When the total monomer quantity was 35%, the convertibility of PEM emulsion was the highest,i.e.98.6%.The MTA Copolymerization Ratio and Morphology of PEM EmulsionWhen the monomers EA/MTA=85/15 and total monomer quantity was 35%, the MTA copolymerization ratio of PEM emulsion was 95.15%(the highest), and the PEM emulsion was some microspheres with 100-180nm of diameter.The Test Results of PEM Emulsion in Treatment of Waste Water The PEM emulsion flocculant was applied in treatment of waste water of paper mill, and measured the precipitation time(t) and transmittancy(T). The test results were showed in table 1. The optimum value of PEM which was able to make the waste water of paper mill into clear water was 0.008%.