Noninvasive Temperature Measurement in Dental Materials Using Nd3+, Yb3+ Doped Nanoparticles Emitting in the Near Infrared Region

In this work, the application of near infrared (NIR)-emitting NaYbF₄:1%Tm³⁺@NaLuF₄:30%Nd³⁺ core–shell nanoparticles is reported for noninvasive probing and monitoring the temperature during photopolymerization of dental materials. When excited at 808 nm, the synthesized nanoparticles emit NIR photoluminescence (PL) with two distinctive peaks at 865 and 980 nm which correspond to radiative transitions from the doped Nd³⁺ and Yb³⁺ ions, respectively. Luminescence intensity ratio between these two bands is found to vary with temperature due to temperature-dependent electronic excitation energy transfer between Nd³⁺ and Yb³⁺ ions at the core/shell interface. This finding allows luminescence ratiometric evaluation of the in situ temperature during photopolymerization of resin cement (doped with nanoparticles) in a veneer placement procedure. In addition, the NIR emission also enables PL imaging of the distribution of the adhesive under the veneer. The results highlight that rare-earth ions–doped nanoparticles with both excitation and emission in the NIR spectral range are advantageous for both PL-based nanothermometry and imaging due to the reduced attenuation of NIR light by dental ceramics.     

A Shell-by-Shell Approach for Synthesis of Mesoporous Multi-Shelled Hollow MOFs for Catalytic Applications

Over the past two decades, advanced materials with hollow interiors have received significant attention in materials research owing to their great application potential across a vast number of technological fields. Though with great difficulty, multi-shelled hollow metal–organic frameworks (MSHMs) have also been successfully synthesized in recent years. Herein, a rational shell-by-shell soft-templating protocol has been devised to fabricate highly uniform multi-shelled hollow cobalt-imidazole-based MOF (ZIF-67). For the first time, it has become possible to endow mesoporosity to this new type of functional material (i.e., mesoporous MOFs). When used as carrier materials in catalytic reactions, in principle, these mesoporous MSHMs with high surface area not only improve the dispersity of metal nanoparticles (NPs), but also efficiently facilitate the mass diffusion of the reactions, resulting in enhanced catalyst activity. Moreover, the obtained MSHMs/M nanocomposites serve as base-metal bifunctional catalysts for one-pot oxidation-Knoevenagel condensation cascade reaction, in which the MSHMs itself serves as a pristine active catalyst in addition to its role of catalyst support. The results demonstrate that excellent multifunctional catalysts can be achieved via preparing intrinsically microporous bulk MOFs into extrinsically mesoporous MSHMs which possess many structural merits that conventional bulk MOFs do not have.     

Biodegradable Black-Phosphorus-Nanosheet-Based Nanoagent for Enhanced Chemo-Photothermal Therapy

Black phosphorus nanosheet (BPNS) is a promising multifunctional material in the biomedical field with biodegradability and low side effects, however its features are always weakened severely owing to its poor stability. Here, a novel method is developed for improving the defect of BPNS based on the effective protection of poly(lactic-co-glycolic acid) (PLGA), which preserves the stable photothermal therapy (PTT) effect of BPNS and biodegradability of the material. Meanwhile, doxorubicin (DOX) is loaded on BPNS/PLGA to get BPNS/PLGA/DOX for further chemotherapy and preventing the recurrence of tumor after PTT. The presented combined therapeutic strategy exploits the strengths and improves the defects of BPNS, thus developing an efficient and safe nanoagent for cancer therapy, which affords and reveals the great potential of BPNS in nanomedicine.     

Magnetocaloric properties in a FeNiGaMnSi high entropy alloy

We investigated a new Fe_26.7Ni_26.7Ga_15.6Mn₂₀Si₁₁ high entropy alloy (HEA) without the rare earth element. The structural, magnetic and magnetocaloric properties of the resulting materials are presented. The HEAs successfully is produced by the arc melting with suction casting method. The crystal structures are characterised through multiphase Rietveld refinement of X-ray diffraction data. The structure of the HEAs was found to be the body centred cubic (bcc). In the magnetic measurements, the ferromagnetic to paramagnetic transition was obtained in the range of 300–400 K. With the employed suction casting method; the Fe_26.7Ni_26.7Ga_15.6Mn₂₀Si₁₁ HEA shows the best magnetocaloric properties as 1.59 Jkg⁻¹K⁻¹ maximum magnetic entropy change (0–2 T) and 75.68 Jkg^-1 refrigeration capacity after the annealing process.     

利用可见-近红外-中红外超快光谱揭示离子交换法制备的少层MoS2中缺陷介导的载流子动力学

本文结合可见-近红外-中红外瞬态吸收光谱技术对离子交换法制备的少层MoS₂中缺陷介导的载流子动力学进行了详细的解析. 在近红外瞬态吸收光谱中观察到的宽带漂白信号表明少层MoS₂纳米片带隙中分布着大量的缺陷态. 实验结果明确揭示了载流子被缺陷态的快速捕获以及进一步的复合过程,证明带隙中的缺陷态对MoS₂光生载流子动力学过程起着至关重要的作用. 在中红外瞬态吸收光谱中观察到的正信号到负信号的转变进一步证实了在导带下小于0.24 eV处存在被载流子占据的缺陷态. 这些在少层MoS₂纳米片中存在的缺陷态可以作为有效的载流子捕获中心来辅助光生载流子在皮秒时间尺度内完成非辐射复合过程.     

Mechanistic model for the dielectric spectrum of a simple dielectric material

ABSTRACT

In this paper, we perform molecular dynamics simulations of a dielectric fluidic material composed of permanent molecular dipoles. The dielectric spectrum features two peaks at lower frequencies than the system phonon frequency. The primary peak is observed at all temperatures studied and shifts toward lower frequencies as the temperature decreases. During this shift, the secondary peak emerges with a higher peak frequency than the primary peak. The secondary peak amplitude increases as the temperature decreases. Both peaks are dependent on the wavevector; in the small wavevector regime, the primary peak is shifted to higher frequencies as the wavevector squared and the secondary peak amplitude increases as the wavevector increases, but shows no shift in frequency. From the polarisation balance equation, we propose a model for the dielectric spectrum. This captures the spectrum features, and we conjecture that the primary peak is due to dipole moment correlations (Debye-type) and the secondary peak is due to the correlation between the dipole moment and a microscopic local field.     

基于PdSe2/GaAs异质结的高灵敏近红外光伏型探测器的制备和图像传感的应用

本文制备了一种基于PdSe₂/GaAs异质结的高灵敏近红外光电探测器,该探测器是通过将多层PdSe₂薄膜转移到平面GaAs上制成的. 所制备的PdSe₂/GaAs异质结器件在808 nm光照下表现出明显的光伏特性,这表明近红外光电探测器可以用作自驱动器件. 进一步的器件分析表明,这种杂化异质结在零偏电压和808 nm光照下具有1.16×10⁵的高开关比. 光电探测器的响应度和比探测度分别约为171.34 mA/W和2.36×10¹¹ Jones. 而且,该器件显示出优异的稳定性和可靠的重复性. 在空气中2个月后,近红外光电探测器的光电特性几乎没有下降,这归因于PdSe₂的良好稳定性. 最后,基于PdSe₂/GaAs的异质结器件还可以用作近红外光传感器.     

压力诱导发光未来可期

科技创新的根源是基于基础科学研究的提升,而"从0到1"的突破是需要长期的积累和灵感的。本文讲述了发现压力诱导发光这一新现象的思想和材料设计。     

损伤材料裂纹尖端附近的应力场

本文导出了损伤材料的全量理论,导出了全量公式中H的渐近表达式;最后得到损伤材料平面应变条件下的裂纹尖端的应力应变场。     

Dual-parameter elastic-plastic fracture criterion of metals and alloys in the plane strain case

In recent years, some investigators discussed the applicability of the HRR theory for engineering materials based on the results of numerical analyses and experimental studies. In the present paper, the finite element method is employed to analyze the crack tip fields of the engineering elastic-plastic material with a variety of geometry configurations of cracked specimens from elastic state to intensely general yielded state in the plane strain case. The results indicate that the HRR theory loses its validity of application for engineering elastic-plastic materials in the plane strain case. The reasons for this are analyzed. A dual-parameter fracture criterion is suggested for this case.