Direct melting polycondensation and characterization of poly(ɛ-caprolactone-co-lactic acid)

A kind of biodegradable material, poly(ɛ-caprolactone-co-lactic acid) [P(CL-co-LA)] was synthesized via the direct melting polycondensation of lactic acid (LA) and ɛ-caprolactone (CL). The influences of the polycondensation time, and the catalyst type on the intrinsic viscosity of P(CL-co-LA) were also investigated. The results indicate that P(CL-co-dl-LA), with an intrinsic viscosity of 0.4733 dL/g, can be prepared by direct melting polycondensation with the molar ratio LA/CL = 3:7 at 180°C and 70 Pa for 12 h, using 0.5% (mass fraction) of SnCl₂ as the catalyst. Compared with lactide ring-opening polycondensation (ROP), the direct melting polycondensation of LA and CL is more practicable and simple. Translated from Journal of South China University of Technology, 2006, 34(7): 7–11 (in Chinese)     

聚苯基膦酸双酚A酯的合成与表征

聚苯基膦酸双酚Ａ酯的合成与表征唐旭东陈晓婷王玉忠杨科珂王波（四川联合大学化学系成都６１００６４）吴大诚（四川联合大学轻纺学院成都６１００６５）关键词聚膦酸酯，阻燃剂，熔融缩聚，热性能聚膦酸酯类化合物是一类重要的磷系阻燃剂［１～３］，与传统的非聚...     

WHOLLY-AROMATIC THERMOTROPIC LIQUID CRYSTALLINE POLYMER AND ITS BLOCK COPOLYMER

A wholly-aromatic thermotropic liquid crystalline polymer (WATLCP) composed ofp-hydroxybenzoic acid (HBA), 4,4'-dihydroxy bisphenyl (BP), terephthalic acid (TPA),m-phthalic acid (MPA) was synthesized. It was symbolized by BP-LCP. Using a simi-lar method, a new copolymer BP-PSF was prepared. BP-PSF has a semi-flexible chainpolysulfone and a rigid-rod chain like BP-LCP. By FT-IR, polarizing microscope and DSCtechnique, the structures and properties of BP-LCP and BP-PSF were studied.     

Fluorinated poly(arylene ether ketone)s bearing pentafluorostyrene moieties prepared by a modified polycondensation

The polycondensation of decafluorobenzophenone with hexafluorobisphenol A was modified by the addition of a molecular sieve dehydrating apparatus to the refluxing reaction system. This modification promoted the polymerization and enabled the reactions to be conducted in milder conditions and completed in a shorter time, thereby depressing side reactions such as branching and crosslinking. The resulting fluorinated poly(arylene ether ketone)s (FPAEK) were free of gel particles and possessed the designed molecular weights. This modified procedure was also suitable for introducing crosslinkable pentafluorostyrene (FSt) moieties into the polymers at the chain ends and/or inside the chain with the vinyl group of FSt being pendant. The resulting FSt containing fluorinated poly(arylene ether ketone)s (FPAEK‐FSt) can then be thermally crosslinked at 100 °C in the presence of 1% benzoyl peroxide (BPO) or at 250 °C without any initiator. The glass‐transition temperatures (T_g's) of FPAEK increased with increasing molecular weight and leveled off at about 147 °C for the polymer with a number‐average molecular weight of 18,600 Da, whereas the values were not apparently affected by the addition of FSt units. However, crosslinking of the FPAEK‐FSt resulted in an approximate 30 °C increase of the T_g. Spin‐coating FPAEK‐FSt onto silicon wafers followed by crosslinking gave films with excellent thermal stability, physical strength, and adhesion to the substrate as well as good reproducibility in terms of film preparation and optical properties. The refractive index and birefringence of the films measured at a wavelength of 1.55 μm were 1.502 and 2.5 × 10^?3, respectively. © 2002 Government of Canada. Exclusive worldwide publication rights in the article have been transferred to Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 4205–4216, 2002     

Synthesis and characterization of some carbazole-based imine polymers

Five imine polymers, all containing 3,6-disubstituted carbazole ring in the main polymer chain, were synthesized by solution polycondensation of 3,6-diformyl (N-hexyl) carbazole with hydrazine, 1,4-diaminobenzene, 4,4′-diaminobiphenyl, 1,5-diaminonaphthalene and 3,6-(N-hexyl) diaminocarbazole. The polymers were analyzed by spectroscopic methods and compared with two imine models.     

Aromatic poly(sulfone sulfide amide imide)s as new types of soluble thermally stable polymers

A new diamine monomer containing flexible sulfone, sulfide, and amide units was prepared via three steps. Nucleophilic chloro displacement reaction of 4‐aminothiophenol with 4‐nitrobenzoyl chloride in the presence of propylene oxide afforded N‐(4‐mercapto‐phenyl)‐4‐nitrobenzamide and subsequent reduction of the nitro intermediate led to 4‐amino‐N‐(4‐mercapto‐phenyl)benzamide. Two moles of this amino thiophenol compound was reacted with bis‐(4‐chloro phenyl)sulfone to provide a novel diamine monomer. The diamine was reacted with aromatic dianhydrides to form polyimides via a two‐step polycondensation method, formation of poly(amic acid)s, followed by chemical imidization. The resulting polymers were characterized and their physical properties including thermal behavior, thermal stability, solubility and inherent viscosity were studied. Copyright © 2007 John Wiley & Sons, Ltd.     

Preparation and characterization of novel polyaryloxydiphenylsilanes with high glass transition temperature by melt polycondensation of dianilinodiphenylsilane with bisphenols

Novel polyaryloxydiphenylsilanes with reduced viscosities of 0.31–0.65 dL/g were obtained by the melt polycondensation of dianilinodiphenylsilane with three bisphenols, 2,2-bis (4-hydroxyphenyl)-1,1,1,3,3,3-hexafluoropropane, 3 (4-hydroxyphenyl)-1,1,3-trimethyl-5-indanol, and 9,9-bis (4-hydroxyphenyl) fluorene, at 200–320°C in vacuo. These polymers are all amorphous and readily soluble in a wide variety of organic solvents such as chlorinated and aromatic hydrocarbons, cyclic ethers, and polar aprotic solvents. Because of their bulky and/or rigid ring structures, polyaryloxydiphenylsilanes containing diphenylhexafluoropropane, phenylindane, and diphenylfluorene units in the main chain have high glass transition temperatures of 106, 112, and 172°C, respectively. They are thermally stable showing almost no weight loss up to 350°C in air. Colorless, transparent, but brittle films are obtained from these polymers by solution casting. Ultraviolet transmission is sharply cut off by these polyaryloxydiphenylsilane films at ca. 300 nm, and the cut-off wavelength depends on the bisphenols used.     

缩聚反应合成侧链液晶聚合物

侧链液晶聚合物的合成方法,可归纳为3类:一是烯基的单体,如甲基丙烯酸酯,或丙烯酸酯,氯代丙烯酸酯等,经自由基聚合反应,阴离子聚合反应及甲基丙烯酸酯的基团转移聚合反应,得到侧链液晶聚合物;二是变性反应,如聚硅氧烷与丙烯酸酯介     

Cation radical intermediates in benzene and toluene polycondensation on sulfated zirconia

Benzene dimer cation radicals were detected on sulfated zirconia at low temperature and benzene coverage. Two temperature regions for their transformations were observed. Below 473 K the radical concentration remained stable reflecting the amount of strong surface acceptor sites. Above 623 K it increased drastically.     

Synthesis and characterization of oligo-4-[(pyridin-3-ylimino)methyl]phenol

The oxidative polycondensation of 4-[(pyridin-3-ylimino)methyl]phenol (4-PIMP) with O₂, H₂O₂, and NaOCl was studied in an aqueous alkaline medium between 50°C and 90°C. Oligo-4-[(pyridin-3-ylimino)methyl]phenol (O-4-PIMP) prepared was characterized by ¹H-NMR, ¹³C-NMR, FT-IR, UV-VIS, size-exclusion chromatography, and elemental and thermal analyses techniques. At the optimum reaction conditions, the yield of O-4-PIMP was 18.9%, 39.4%, and 46.8% using H₂O₂, O₂, and NaOCl oxidant, respectively. According to the TG analysis, the initial degradation temperature of O-4-PIMP was 218°C, which was by 50°C higher than that of 4-PIMP. Thermal analyses of 4-PIMP and O-4-PIMP were carried out in N₂ atmosphere at 15–1000°C. The highest occupied molecular orbital, the lowest unoccupied molecular orbital, and electrochemical energy gaps of 4-PIMP and O-4-PIMP were determined from the onset potentials for n-doping and p-doping, respectively. Also, optical band gaps of 4-PIMP and O-4-PIMP were determined according to UV-VIS measurements.