托卡马克磁探针阵列通常是围绕等离子体均匀布置的完整环形系统。由于受到布置空间的限制，HL-2A装置的磁探针只能组成带空白区域的间断阵列。在分析了HL-lM极向磁场振荡——Mirnov振荡模式的基础上，探索了HL-2A磁探针阵列诊断应注意的问题。     

Synthesis and characterization of a novel nano-scale magnetic solid base catalyst involving a layered double hydroxide supported on a ferrite core

A nano-scale magnetic solid base catalyst MgAl-OH-LDH/MgFe₂O₄ (where LDH denotes layered double hydroxide) composed of MgAl-OH-LDH Brønsted base catalytic layers coated on MgFe₂O₄ spinel cores has been prepared. A magnetic precursor MgAl-CO₃-LDH/MgFe₂O₄ was prepared by a method involving separate nucleation and aging steps, and subsequently calcined to give a mixed metal oxide composite MgAl(O)/MgFe₂O₄ which was rehydrated to give MgAl-OH-LDH/MgFe₂O₄. The structure and magnetic properties of the nano-scale magnetic solid base MgAl-OH-LDH/MgFe₂O₄, together with those of the magnetic precursor MgAl-CO₃-LDH/MgFe₂O₄ and MgFe₂O₄ were characterized by XRD, XPS, low temperature N₂ adsorption and vibrating sample magnetometry (VSM). The MgAl-OH-LDH/MgFe₂O₄ composite possesses a mesoporous structure with pore size ranging from 2 to 20 nm with particle size mainly in the range 35-130 nm. The catalytic properties of MgAl-OH-LDH/MgFe₂O₄ were evaluated using the self-condensation of acetone at 273 K as a probe reaction. The results showed that the conversion of acetone to diacetone alcohol reached the thermodynamic equilibrium value of 23% at 273 K. The catalyst was easily recovered through application of an external magnetic field, and when the reclaimed catalyst was used in a second run for the same reaction, the reactivity remained unchanged.     

Ab initio X-ray powder diffraction characterisation of molecule-based magnetic materials

Use of ab initio X-ray powder diffraction (XRPD) methods in the study of magnetically active species of covalent nature is presented. Selected cases are chosen in order to underline the power of XRPD methodologies, highlighting the importance of independent physico-chemical information from ancillary techniques.     

Magnetoresistance of Fe3O4/Au/Fe3O4 and Fe3O4/Au/Fe spin-valve structures

A detailed study of the in-plane magnetotransport properties of spin valves with one and two Fe₃O₄ electrodes is presented. Fe₃O₄/Au/Fe₃O₄ spin valves exhibit a clear anisotropic magnetoresistance in small magnetic fields but no giant magnetoresistance (GMR). The absence of GMR in these structures is due to simultaneous magnetization reversal in the two Fe₃O₄ layers. By contrast, a negative GMR effect is measured on Fe₃O₄/Au/Fe spin valves. The negative GMR is attributed to an electron spin scattering asymmetry at the Fe₃O₄/Au interface or an induced spin scattering asymmetry in the Au interfacial layers.     

α-Fe2O3-In2O3 mixed oxide nanoparticles synthesized under hydrothermal supercritical conditions

α-Fe₂O₃-In₂O₃ mixed oxide nanoparticles system has been synthesized by hydrothermal supercritical and postannealing route, starting with (1−x)Fe(NO₃)₃·9H₂O·xIn(NO₃)₃·5H₂O aqueous solution (x=0-1). X-ray diffraction and Mössbauer spectroscopy have been used to study the phase structure and substitutions in the nanosized samples. The concentration regions for the existence of the solid solutions in the α-Fe₂O₃-In₂O₃ nanoparticle system together with the solubility limits of In³⁺ ions in the hematite lattice and of Fe³⁺ ions in the cubic In₂O₃ structure have been evidenced. In general, the substitution level is considerably lower than the nominal concentration x. A justification of the processes leading to the formation of iron and indium phases in the investigated supercritical hydrothermal system has been given.     

Does phenazine form triplet excimer and dimer anion radical?

Laser flash photolysis of phenazine (PZ) solution reveals the existence of a stable species with a long lifetime at 380 nm in addition to the usual triplet PZ at 440 nm. The former is suggested to be due to formation of triplet PZ excimer. The triplet excimer also undergoes photoinduced electron transfer with some aromatic amines. The formation of PZ dimer anion radical and amine cation radicals are confirmed by external magnetic field effect studies. Measurement of B_1/2, which estimates hyperfine present in the system, also supports this assignment.     

Behavior of zirconium in the ZrOW(100) system at high temperature, studied by ISS, AES and work-function measurements

The behavior of zirconium atoms at the W(100) surface associated with oxygen adsorption at different sample temperatures has been studied by Auger electron spectroscopy (AES), ion scattering spectroscopy (ISS), and the relative change of the work function (Δф) measured by the onset of the secondary electron energy distribution. The results have revealed: (i) adsorption of zirconium onto the W(100) surface followed by the elevation of the sample temperature up to 1710 K in an oxygen partial pressure of 2.7 × 10⁻⁴ induces complete diffusion of zirconium atoms into the W(100) substrate; (ii) further exposure of oxygen induces co-existence of oxygen and tungsten on the surface at 1710 K, resulting in a work function of 4.37 eV; (iii) keeping the sample temperature at 1710 K, simple evacuation of the system has resulted in surface segregation of zirconium atoms to the surface to form a zirconium atomic layer on the top-most surface, reducing the work function to 2.7 eV. The results have revealed that this specific behavior of zirconium atoms at high temperature assures, with very good reproducibility, the highly stable performance and long service life of Zr---O/W(100)-emitters in practical use, even in a low vacuum of 10⁻⁶ Pa.     

第Ⅰ种强度不对称三态叠加多模叠加态光场N次方Y压缩—第一正交相位分量的压缩情况

根据量子力学中的线性叠加原理,构造了由三个强度不等的多模相干态光场|{Z_j^(A)}>_q、|{Z_j^(B)}>_q和|{Z_j^(C)}>_q的线性叠加所组成的第Ⅰ种强度不对称三态叠加多模叠加态光场|ψ_l^(ABC)>_q.利用多模压缩态理论,研究了态|ψ_l^(ABC)>_q的第一正交方分量(即磁场分量)的广义非线性等幂次N次方Y压缩特性.结果发现:①在上述各多模相干态光场中各模的强度和各模的初始相位各不相等的情况下,态|ψ_l^(ABC)>_q的第一正交分量-磁场分量在一定的条件下,总可呈现出周期性变化的、任意等幂次的N次方Y压缩效应;②当上述各多模相干态光场的强度和各模的初始相位相等时,态|ψ_l^(ABC)>_q的磁场分量的N次方Y压缩现象消失,态|ψ_l^(ABC)>_q可恒处于等幂次N-Y最小测不准态.