γ-Zirconium and γ-Titanium Phosphates Platinum Intercalation Compound Preparation, characterization and thermal behaviour

Inorganic ion-exchangers with a layered structure such as γ-zirconium and γ-titanium phosphates, intercalated with organic diamines, are able to exchange Pt²⁺ ions to give new intercalation compounds that can be utilized in heterogeneous catalysis. The experiments performed at different temperatures (25 and 45°C), show different ion uptakes, greater at 45°C and for the materials derived from γ-zirconium phosphate. After platinum exchange, all the materials show an amorphization in the XRD if compared with their precursors. The thermal behaviour of the platinum materials is specific, depending on the exchanger used and the ligand inside the exchanger. Pt²⁺ ion has a catalytic effect on ligand elimination in the γ-zirconium phosphate platinum compounds, but not in those derived from γ-titanium. All the obtained yellow materials show a small step in the TG curves and simultaneously we have the Pt²⁺→Pt⁰ reduction: this is confirmed by XRD registered at the temperatures of the thermal effect, showing peaks at d_hkl=2.27 and 1.95 Å. This revised version was published online in July 2006 with corrections to the Cover Date.     

Intercalation of Cyclic Amines into α-Titanium Phosphate

The intercalation of some amines (aniline, benzylamine, cyclohexylamine,piperidine, pyridine, pyrazine and piperazine) into -titaniumphosphate, Ti(HPO₄)_2×H₂O,has been investigated by the batch method and/or by exposing the host to thevapour of the amines. The changes in the interlayer distance of the solidduring the intercalation process was followed by X-ray powder diffraction.The new intercalates were characterised by chemical and thermal analysis.Materials with a monolaminar and/or bilaminar arrangement of amine moleculesin the phosphate interlayer region are obtained depending on the nature ofthe amine. Due to steric hindrance, saturated phases are not obtained forall amines studied. The thermal decomposition of the intercalates (nitrogenatmosphere), takes place in three stages: dehydration, removal of amines andcondensation of the hydrogenphosphate to pyrophosphate groups.     

锂离子电池用α-Fe2O3-Ag复合纳米棒负极材料的制备及储锂性能

采用FeOOH纳米棒为前驱体,通过层层自组装法及随后的热处理过程制备出α-Fe2O3-Ag复合纳米棒.采用透射电子显微镜(TEM)、高分辨透射电子显微镜(HRTEM)和电化学性能测试对样品的形貌、结构及电化学性能进行了表征.结果表明,Ag纳米颗粒均匀地分布在α-Fe2O3纳米棒的表面.作为锂离子电池负极材料,α-Fe2O3-Ag复合纳米棒表现出了较好的循环性能和较高的比容量.180个循环后,其比容量高达549.8 mA.h/g.     

A novel method for asymmetric synthesis of both enantiomers of α-substituted carboxylic acid derivatives from optically active 1-chlorovinyl p-tolyl sulfoxides and lithium ester enolates with 1,4-chiral induction from the sulfur chiral center

Treatment of optically active 1-chlorovinyl p-tolyl sulfoxides, which were synthesized from symmetrical ketones and (R)-(−)-chloromethyl p-tolyl sulfoxide in three steps, with lithium enolate of carboxylic acid tert-butyl esters gave optically active adducts having a substituent at the α-position with high 1,4-chiral induction from the sulfur chiral center in high yields. The adducts were converted to optically active esters and carboxylic acids having a chiral center at the α-position. When this addition reaction was carried out with the ester enolate generated from excess carboxylic acid tert-butyl ester with LDA in the presence of HMPA, the diastereomer of the adduct was obtained. By using the two reaction conditions for the generation of the ester enolates, a new method for asymmetric synthesis of both enantiomers of carboxylic acid derivatives having a substituent at the α-position from the one chiral source, (R)-(−)-chloromethyl p-tolyl sulfoxide, was realized.     

Spectroscopic Studies on the Interaction of Tetramethylpyridylporphyrins and Cationic Clays

In the present work, the interaction between5,10,15,20-tetrakis(1-methyl-4-pyridyl)-21H,23H-porphine (TMPyP) and its metallated form(CoTMPyP) with three cationic clays was investigatedby X-ray diffraction (XRD), UV-VIS and resonance Ramanspectroscopies. Sodium montmorillonites K10 and KSFand a synthetic fluorohectorite (FHT) containingdifferent macrocycle loadings, were prepared by an ionexchange reaction. In nonsaturated KSF and FHT, theCoTMPyP molecule assumes a flat orientation, relativeto the host layers, giving rise to at least twoabsorption bands in the Soret region (ca. 445 and 465 nm)assigned to adsorbed and intercalated CoTMPyP,respectively. For the delaminated K10 sample, a broadband centered around 456 nm, indicates a majorcontribution from the metalloporphyrin on the clayexternal surfaces. The electronic spectra of FHTsamples containing increasing amounts of CoTMPyPshow bands red shifted even when a small amount ofporphyrin is used, suggesting that the electroniclevels of the macrocycle are more affected by theinteraction with the clay than by the metalloporphyrindistortion inside the galleries. The resonance Ramanspectra obtained for all CoTMPyP samples presentedonly minor shifts in peak positions and band width,with the exception of the FHT saturated sample, wherethe bands are clearly broader when compared to otherloadings, suggesting that porphyrin aggregation isoccurring. In the case of TMPyP, the bands at ca. 430and 468 nm were assigned to nonprotonated andprotonated molecules, respectively. This assignment issupported by resonance Raman spectroscopy, which alsoshowed the ₂ mode (ca. 1550 cm^-1) to bethe most sensitive peak to protonation.     

锂电池正极材料1,4,5,8-四羟基-9,10-蒽醌的电化学性能

研究了一种新型有机醌类化合物1,4,5,8-四羟基-9,10-蒽醌(THAQ)及其氧化产物(O-THAQ)的电化学性能.循环伏安和充放电结果显示,在放电时材料中的羰基和羟基均被还原为烯醇锂盐(襒C—O-Li+)结构,其中羰基还原为烯醇锂盐结构的过程可逆.O-THAQ首次放电容量和循环性能都有显著提高,氧化产物的首次放电容量为250 mAh.g-1,20次循环容量为100 mAh.g-1.讨论了THAQ氧化前后性能差异的原因.     

Li2CO3添加剂对石墨电极性能的影响

运用电化学阻抗谱(EIS)和循环伏安法(CV)研究了在1mol/LLiPF6-EC(碳酸乙烯酯):DMC(碳酸二甲酯)电解液中添加Li2CO3对石墨电极性能的影响及机制.CV研究结果表明,在1mol/LLiPF6-EC:DMC电解液中添加Li2CO3能够有效抑制石墨电极首次充放电过程中碳酸乙烯酯(EC)的单电子还原过程,即还原分解产生乙烯和碳酸锂的过程,进而改善石墨电极的电化学循环性能.EIS研究结果表明,在添加Li2CO3的1mol/LLiPF6-EC:DMC电解液中,石墨电极表面的固体电解质相界面膜(SEI膜)具有较强的黏弹性,可以更好地适应锂离子嵌入过程中石墨颗粒体积的微小变化,从而使锂离子的嵌入过程更容易进行.     

Physical and Electrochemical Characterization of Hydrothermal Prepared α'-NaV_2O_5 Crystals

α'-NaV2O5 was prepared by a simple hydrothermal process.X-ray diffraction confirmed the orthorhombic structure of α'-NaV2O5,with preferential growth along the (001) direction.Scanning electron microscopy showed α'-NaV2O5 was composed of flake-shaped crystals.X-ray photoelectron spectroscopy confirmed the co-existence of V4+ and V5+ in α'-NaV2O5,which results in an average V4.5+ oxidation state of α'-NaV2O5.The observed Raman bands are ascribed to different V―O vibrations.α'-NaV2O5 shows a reversible specific capacity of about 100 mA·h·g-1 between 3.5 and 1.0 V,with a good capacity retention.The good electrochemical stability of the material is attributed to its structural stability during Li+ intercalation.     

Control of organoclay structure in hydrocarbon polymers

Two different kinds of organoclays were prepared by mixing a pristine montmorillonite and a double‐chain ammonium salt in many different thermoplastic or elastomeric polymers. Independently of the chemical nature of the considered polymers, the obtained organoclays presented a basal spacing of 4 or 6 nm, when the mixing occurred in the absence or in the presence of a small amount of stearic acid (SA), respectively. X‐ray diffraction and Fourier transform infrared measurements support the hypothesis that these two kinds of organoclays correspond to paraffin‐type tilted and perpendicular bi‐layer intercalates, respectively. The co‐intercalation of SA molecules with the double‐chain amphiphile is suggested, to explain the observed expansion of the clay interlayer distance. The obtained results suggest an easy way to control the organoclay structure in polymer composites. Moreover, the authors on the basis of these results propose a criticism to the extensive literature that systematically explains most d basal spacing increase observed for clays in polymer with the penetration of apolar polymer chains in the clay interlayer space. Copyright © 2010 John Wiley & Sons, Ltd.