Thermal decomposition of copper(II) and zinc carbonate hydroxides by means of TG-MS

Summary For the quantitative analyses of evolved CO₂and H₂O during the thermal decomposition of solids, calibration curves, i.e. the amounts of evolved gases vs. the corresponding peak areas of mass chromatograms measured by TG-MS, were plotted as referenced by the reaction stoichiometry of the thermal decomposition of sodium hydrogencarbonate NaHCO₃. The accuracy and reliability of the quantitative analyses of the evolved CO₂and H₂O based on the calibration curves were evaluated by applying the calibration curves to the mass chromatograms for the thermal decompositions of copper(II) and zinc carbonate hydroxides. It was indicated from the observed ratio of evolved CO₂and H₂O that the compositions of copper(II) and zinc carbonate hydroxides examined in this study correspond to mineral malachite, Cu₂CO₃(OH)₂, and hydrozincate, Zn₅(CO₃)₂(OH)₆, respectively. Reliability of the present analytical procedure was confirmed by the fairly good agreement of the mass fraction of the evolved gases calculated from the analytical values with the total mass-loss during the thermal decompositions measured by TG.     

Rb2I(OH): Ein Hydroxidiodid im System RbOH/RbI

Rb₂I(OH): A Hydroxide Iodide in the System RbOH/RbI The pseudobinary system RbOH/RbI was investigated by X-ray methods. The crystal structure of Rb₂I(OH) was solved by single crystal data: Rb₂I(OH): Pnma, Z = 4, a = 7.748(1) Å, b = 5.654(2) Å,c = 13.254(2) Å Z(F_o) with (F_o)² ? 3σ = (F_o)² = 449, Z (parameter) = 25, R/R_w = 0.021/0.023 Rb₂I(OH) crystallizes in a new type of structure, built up by a three dimensional network of [Rb₂(OH)⁺] containing the iodide ions.     

甲状腺机能亢进症头发锌、硒、钒、锂、锗5种微量元素的动态变化

测定了２４例甲亢治疗前后及３０例健康对照的头发锌、硒、钒、锂及锗的含量，发现未治疗的甲亢头发锌、硒、钒、锂及锗含量较对照组低，Ｚｎ、Ｓｅ、Ｌｉ、Ｇｅ，Ｐ＜０．００１，Ｖ，Ｐ＜０．０１．甲亢经６～１２周抗甲亢药物治疗后．头发中５种元素均较治疗前上升（Ｐ＜０．００１），且头发钒和锂含量治疗后已达到对照组水平，Ｖ，Ｐ＞０．２，Ｌｉ，Ｐ＞０．１，而头发锌、晒及锗含量治疗后仍低于对照组（Ｐ＜０　．００１）．结论：甲亢头发锌、硒、钒、锂及锗含量降低．经６～１２周抗甲亢治疗可使头发钒及锂含量恢复正常水平，而其余３种元素则可能需要更长时间的抗甲亢治疗才能恢复至正常水平。     

Solvent and thiourea adsorption/intercalation effects on the solid-state electrochemistry of α-phase nickel hydroxide nanoparticles

Nanoparticles of α-phase nickel hydroxide were synthesized by a single-step hydrothermal method using urea as the hydrolytic agent. Precipitated powders were of pure turbostratic α-phase as confirmed by x-ray diffraction profile. The ageing of α-Ni(OH)₂ in 1.0 M alkali solutions is investigated for pure non-intercalated α-Ni(OH)₂ and thiourea intercalated/absorbed α-phase nanomaterials. The α-Ni(OH)₂ powder immobilized on the surface of graphite electrodes shows a gradual α→β phase transformation with continuous voltammetric cycling, and the concentration gradient of water that exists in the layered-double-hydroxide-like interlayers of α-phase and the solution was shown to play a crucial role on the high electrochemical activity of this phase nickel hydroxide. To understand the role of water in the ageing process, concomitant entries of non-aqueous solvents like ethanol and acetonitrile along with thiourea were effected. Cyclic voltammetric measurements of thiourea-treated α-Ni(OH)₂ samples revealed that hydroxyl ion influx during the anodic oxidation depends on the counter flux of solvent molecules, and if the intercalated the solvent is acetonitrile, then the electrochemical activity of α-Ni(OH)₂ reduced drastically; Q _a/Q _c>1 for water as solvent in the interlayers α-Ni(OH)₂ and Q _a/Q _c<1 for ethanol and acetonitrile as solvents. The α-phase gets stabilized in the presence of thiourea with water and ethanol as co-intercalates. Transmission electron microscope images of α-Ni(OH)₂ and thiourea-treated samples show a change in particle size and morphology. Elemental CHNS analysis confirms the presence of sulphur in the thiourea intercalated samples.     

Synthesis and phase transition of Li-Mn-O spinels with high Li/Mn ratio by thermo-decomposition of LiMnC2O4(Ac)

LiMnC₂O₄(Ac) precursor in which Li⁺ and Mn²⁺ were amalgamated in one molecule was prepared by solid-state reaction at room-temperature using manganese acetate, lithium hydroxide and oxalic acid as raw materials. By thermo-decomposition of LiMnC₂O₄(Ac) at various temperatures, a series of Li_1+y[Mn_2−xLi_x]_16dO₄ spinels were prepared with Li₂MnO₃ as impurities. The structure and phase transition of these spinels were investigated by XRD, TG/DTA, average oxidation state of Mn and cyclic voltammeric techniques. Results revealed that the Li-Mn-O spinels with high Li/Mn ratio were unstable at high temperature, and the phase transition was associated with the transfer of Li⁺ from octahedral 16c sites to 16d sites. With the sintering temperature increasing from 450 to 850 °C, the phase structure varied from lithiated-spinel Li₂Mn₂O₄ to Li₄Mn₅O₁₂-like to LiMn₂O₄-like and finally to rock-salt LiMnO₂-like. A way of determining x with average oxidation state of Mn and the content of Li₂MnO₃ was also demonstrated.     

链珠状氢氧化亚镍的准电容特性及其在复合型超电容器中的应用(英)

本文采用溶胶凝聚方法制备了超细氢氧化亚镍电极材料并通过在其中掺加适量碳纳米管的方法大大提高了电极的比容量并有效改善了电极材料的阻抗特性。掺有20%碳纳米管的氢氧化亚镍复合电极材料的单电极比容量可达到320 F·g^-1。本文分别采用氢氧化亚镍/碳纳米管复合电极作为正极，活性炭作为负极，6 mol·L^-1 KOH作为电解液制备了复合型电化学电容器。采用上述方法制备的复合型电容器工作电压达到1.6 V，电容器质量比容量达到60 F·g^-1。复合型电容器能量密度达到20.11 Wh·kg^-1，最大功率密度达到8.6 kW·kg^-1,兼具高能量特性和优良的大电流放电特性。     

Nb 掺杂LiFePO4/C 的一步固相合成及电化学性能

用固相法一步合成了Nb掺杂的LiFePO4/C复合材料, 研究了Nb掺杂量对材料电化学性能的影响. 结果表明, Nb掺杂后LiFePO4/C复合材料的电化学性能明显提高. 在0.5C、1C和2C充放电倍率下, 名义成分为Li0.96Nb0.008FePO4/C正极材料的比容量分别为161、148和132 mAh•g−1, 已达到实用化水平. 阻抗谱和循环伏安特性测试显示, Nb掺杂有效地降低了复合材料电极的阻抗和极化, 说明Nb掺杂的主要作用是提高了LiFePO4的电子电导率.     

Apparent Molar Volume, Heat Capacity, and Conductance of Lithium Bis(trifluoromethylsulfone)imide in Glymes and Other Aprotic Solvents

Lithium bis(trifluoromethylsulfone)imide (LiTFSI) is a promising electrolyte for high-energy lithium batteries due to its high solubility in most solvents and electrochemical stability. To characterize this electrolyte in solution, its conductance and apparent molar volume and heat capacity were measured over a wide range of concentration in glymes, tetraethylsulfamide (TESA), acetonitrile, -butyrolactone, and propylene carbonate at 25°C and were compared with those of LiClO₄ in the same solvents. The glymes or n(ethylene glycol) dimethyl ethers (nEGDME), which have the chemical structure CH₃–O–(CH₂–CH₂–O) _n –CH₃ for n = 1 to 4, are particularly interesting since they are electrochemically stable, have a good redox window, and are analogs of the polyethylene oxides used in polymer-electrolyte batteries. TESA is a good plasticizer for polymer-electrolyte batteries. Whenever required, the following properties of the pure solvents were measured: compressibilities, expansibilities, temperature and pressure dependences of the dielectric constant, acceptor number, and donor number. These data were used in particular to calculate the limiting Debye-Hückel parameters for volumes and heat capacities. The infinite dilution properties of LiTFSI are quite similar to those of other lithium salts. At low concentrations, LiTFSI is strongly associated in the glymes and moderately associated in TESA. At intermediate concentrations, the thermodynamic data suggests that a stable solvate of LiTFSI in EGDME exists in the solution state. At high concentrations, the thermodynamic properties of the two lithium salts approach those of the molten salts. These salts have a reasonably high specific conductivity in most of the solvents. This suggests that the conductance of ions at high concentration in solvents of low dielectric constant is due to a charge transfer process rather than to the migration of free ions.     

A novel Fe（OH）3/TiO2 nanoparticles and its high photocatalytic activity

A very simple and controllable approach was proposed to synthesize novel Fe(OH)_3/TiO_2 nanoparticles.Compared with neat TiO2,the Fe(OH)_3/TiO_2 increased the rate of the photocatalytic degradation of methyl orange at pH 6.0 by more than five times, showing photocatalytic activity as excellent as P25.This enhancing effect is mainly attributed to the ferric hydroxide deposits as the electron scavenger and the enriched surface hydroxyl groups.     

Organically pillared layered zinc hydroxides

The two organically pillared layered zinc hydroxides [Zn₂(OH)₂(ndc)], CPO-6, and [Zn₃(OH)₄(bpdc)], CPO-7, were obtained in hydrothermal reactions between 2,6-naphthalenedicarboxylic acid (ndc) and zinc nitrate (CPO-6) and 4,4′biphenyldicarboxylate (bpdc) and zinc nitrate (CPO-7), respectively. In CPO-6, the tetrahedral zinc atoms are connected by two μ₂-OH groups and two carboxylate oxygen atoms, forming infinite layers extending parallel to the bc-plane. These layers are pillared by ndc to form a three-dimensional structure. In CPO-7, the zinc hydroxide layers are containing four-, five- and six coordinated zinc atoms, and the layers are built like stairways running along the [001] direction. Each step is composed of three infinite chains running in the [010] direction. Both crystal structures were solved from conventional single crystal data. Crystal data for CPO-6: Monoclinic space group P2₁/c (No. 14), a=11.9703(7), b=7.8154(5), c=6.2428(4) Å, β=90.816(2)°, V=583.97(6) Å³ and Z=4. Crystal data for CPO-7: Monoclinic space group C2/c (No. 15), a=35.220(4), b=6.2658(8), c=14.8888(17) Å, β=112.580(4)°, V=3033.8(6) Å³ and Z=8. The compounds were further characterized by thermogravimetric- and chemical analysis.