On the magnetic properties of Lithium Vanadium Bronzes LixV2O5

Magnetic susceptibility of V₂O₅ and of the α-, ?-, δ- and γ-Li_xV₂O₅ bronzes prepared either at high or at room temperature has been measured between liquid helium and ambient temperature. The results are representative of the localized character of the V⁴⁺ ion d-electron and, for high enough x-values, of the existence of antiferromagnetic interactions in a low dimensional system. The intrachain exchange integral J has been determined using the Bonner/Fischer model for Heisenberg chains with S = 1/2 spin. It is larger for the γ- than for the δ-phase. This result as well as the occurrence of long range ordering below T_N ≈ 130 K in the γ-phase may be ascribed to ordering of V⁴⁺ and V⁵⁺ ions in the former bronze and to the random distribution of V⁴⁺ ions in the latter one.     

B2O3/TiO2-ZrO2催化环己酮肟气相Beckmann重排反应研究Ⅱ.焙烧温度的影响

采用XRD、FT-IR和NH3-TPD等方法，研究了载体预焙烧温度和催化剂活化焙烧温度对B2O3/TIO2-ZRO2催化剂的结构、酸性和催化环己酮肟气相Beckmann重排反应性能的影响。结果表明，在383-773K范围内，载体预烧温度对催化剂性能的影响不大，但经973K高温预焙烧后，由于生成了ZrTiO4晶相，使其与H3BO3的相互作用减弱，从而导致催化剂的酸性和反应性能降低，提高催化剂活化焙烧温度，有利于B2O3与TiO2-ZrO2的相互作用，生成更多的Beckmann重排反应所需的中等强度酸中心，使催化剂的活性和选择性提高；但活化焙烧温度过高，会使催化剂中大量的B2O3晶粒析出，引起酸中心数量和催化活性的明显下降。     

Mechanistic aspects of the Wolff-Kishner reaction. V. The cation effect on the reaction of benzophenone hydrazone in butyl carbitol and decyl alcohol

The rate of the Wolff-Kishner reaction of benzophenone hydrazone in butyl carbitol increases as the cation of the alkoxide base is varied in the order K>Na>Li>Mg. The replacement of butyl carbitol by 1-decanol also accelerates the reaction, and an additional increase is caused by the presence of crown ether. On the basis of changes in the activation parameters, it is concluded that the reactivity of the hydrazone anion increases as the contact ion pair becomes more fully solvated and dissociated.     

七-O-乙酰基-β-乳糖异硫氰酸酯的合成、表征及电化学研究

本文合成了并培养出了七-O-乙酰基—β—乳糖异硫氰酸酯的单晶，用X射线衍射分析了其晶体结构。结果表明，晶体为正交晶系，P2₁2₁2₁空间群，a＝1．23282(7)，b＝1．80012(10)，c＝1.85230(10) nm，α＝β＝γ＝90°，V＝4．1107(4) nm³，Z＝4。电化学实验观测到单链DNA和双链DNA对该化合物的峰电流均有明显降低作用，表明化合物与DNA发生了静电作用。     

Electrochemical characteristics of Ce0.8Gd0.2O1.9|La0.6Sr0.4CoO3-δ + Ce0.8Gd0.2O1.9 half-cell

The analysis of the medium temperature half-cell Ce_0.8Gd_0.2O_1.9|70 wt% La_0.6Sr_0.4CoO_3- (LSCO) + 30 wt % Ce_0.8Gd_0.2O_1.9 (CGO) has been made by electrochemical impedance, cyclic voltammetry and chronoamperometry. The shape of complex impedance plots depends on temperature and cathodic polarisation of the electrode. Nyquist (Z, Z-) plots were fitted by equivalent circuit taking into account the electrolyte properties (at very high frequencies), charge transfer process at grain boundaries (at high frequencies), and medium and low frequency O₂ reduction process at the cathode surface and inside the porous cathode material. Two different time constants have been obtained for the cathode process, i.e. for electroreduction of oxygen. It was found that the addition of CGO into the cathode material (LSCO) only somewhat decreases the surface catalytic activity but the noticeably higher low-frequency resistance (i.e. mainly diffusion-like mass transfer resistance R_D) values at lower temperatures have been calculated. It was found that the mainly bulk diffusion-limited process at T773 K deviates toward the kinetically mixed process (diffusion + charge transfer) with increasing temperature.     

Y2O3薄膜处理对3Cr25Ni7N合金的抗高温氧化性能的影响

采用电沉积-热解法在3Cr25Ni7N合金表面制备了Y2O3薄膜,并研究了薄膜处理对合金在1000℃空气中的抗高温氧化性能的影响。氧化动力学曲线、SEM及XRD分析结果表明,Y2O3薄膜处理使合金表面氧化膜以尖晶石结构为主,氧化膜致密,有效地抑制了Cr2O3的挥发反应,且氧化膜与基体的附着性好,因此合金在高温下的抗氧化性能得到提高,这与氧化钇薄膜在较低温度下抗高温氧化性能提高的机制是不同的。在不同温度下,Y2O3薄膜处理均可以有效提高合金的抗高温氧化性能。     

Growth and Characterization of Crystal Nd_(0.06)Y_(0.94)Sr_6Sc(BO_3)_6

<正>The crystal of Nd0.06Y0.94Sr6Sc(BO3)6 with the dimensions up to 35 mm × 28 mm × 13 mm was grown by a top-seeded solution growth method from Li6B4O9 flux. The grown crystal was characterized by X-ray powder diffraction. The optical absorption of the crystal shows that it has a strong absorption band at 8070 A, and the absorption coefficient is 2.17cm-1 with a FWHM of 41 A, which can match with the wavelength of the diode-laser (LD) and is suitable for the LD pumping. Based on the Judd-Ofelt theory, the three parameters of line oscillator strength Ω(λ) (λ = 2, 4 and 6) of the Nd3+ion in the crystal were calculated as follows: Ω2= 1.194 × 10-20, Ω4= 4.186 × 10-20 and Ω6 = 3.351 × 10-20cm2, which are relatively larger. The results indicate that the crystal Nd0.06Y0.94Sr6Sc(BO3)6 may be a kind of high-efficient laser material for diode-pumped.     

Ein neues Kupfercobaltboratoxid mit isolierten B2O5-Baugruppen: Cu2Co(B2O5)O

On a New Copper Cobalt Borate Oxide with Isolated B₂O₅ Units: Cu₂Co(B₂O₅)O Single crystals of a new compound with the empirical formula Cu₂CoB₂O₆ were obtained by using a B₂O₃ flux technique. X-ray single crystal technique led to a new structure type. Cu₂CoB₂O₆ crystallizes monoclinic, space group C-P2₁/c (No. 14); a = 3.2250(6); b = 14.847(1); c = 9.1171(6) Å; β = 93.67°; Z = 4. All metal sites are octahedrally coordinated and form a two dimensional framework consisting of edge sharing octahedra ribbons. In addition one observes isolated B₂O₅-units and oxygen which is not coordinated to boron. The far relation to the crystal structure of the mineral Warwickite is illustrated.