A poly(urethane-acrylate) polymer (PUA) was synthesized, and a sufficiently high molecular weight starting from urethane-acrylate oligomer (UAO) was obtained. PUA was then loaded with two types of powdered ligno-cellulosic waste, namely from licorice root and palm leaf, in amounts of 1, 5 and 10%, and the obtained composites were chemically and mechanically characterized. FTIR analysis of final PUA synthesized used for the composite production confirmed the new bonds formed during the polymerization process. The degradation temperatures of the two types of waste used were in line with what observed in most common natural fibers with an onset at 270 °C for licorice waste, and at 290 °C for palm leaf one. The former was more abundant in cellulose (44% vs. 12% lignin), whilst the latter was richer in lignin (30% vs. 26% cellulose). In the composites, only a limited reduction of degradation temperature was observed for palm leaf waste addition and some dispersion issues are observed for licorice root, leading to fluctuating results. Tensile performance of the composites indicates some reduction with respect to the pure polymer in terms of tensile strength, though stabilizing between data with 5 and 10% filler. In contrast, Shore A hardness of both composites slightly increases with higher filler content, while in stiffness-driven applications licorice-based composites showed potential due to an increase up to 50% compared to neat PUA. In general terms, the fracture surfaces tend to become rougher with filler introduction, which indicates the need for optimizing interfacial adhesion. 相似文献
Three new types of heterogeneous catalysts were prepared using a facile approach by the immobilization of Grubbs catalysts on PEGylated Merrifield resin. One of the immobilized catalysts was more efficient than the free catalyst for the metathesis of leaf alcohols in conversion and selectivity and was reused repeatedly (up to 5 cycles) with only a slight loss of activity (10.5 %). The long-chain PEGylated linker provided an appropriate distance between the resin and the catalytic center so that the ruthenium catalysts acted as the free catalyst. 相似文献
The surface of the taro plant leaf was replicated using a nanoimprinting technique (NIT) supplemented with an electric field. This field‐aided nanoimprinting method (FA‐NIT) consists of two steps: applying an electric field to a liquid polymer under the plant leaves and the curing process of the polymer with the applied electric field. An appropriate electric field was needed to induce the electrokinetic phenomena of a liquid polymer to obtain a good replicated surface. The roughness fabricated by the FA‐NIT was about 45% higher than the one prepared by NIT. The FA‐NIT method is a good supplementary technique to improve the quality of NIT.