尖晶石型LiMn1.9Al0.1O3.95F0.05材料的制备及其增强的倍率性能

通过溶胶-凝胶和高温固相掺杂反应可控合成了形貌均匀、结晶性好的尖晶石型LiMn_1.9Al_0.1O_3.95F_0.05正极材料,探究了Al部分取代Mn、F部分取代O后对结构的影响,测试并比较了电极材料的倍率性能和循环充放电性能. 结果表明,尖晶石型LiMn_1.9Al_0.1O_3.95F_0.05和LiMn₂O₄有同样的晶型,但电极较传统的LiMn2O4电极倍率稳定性有显著提高. 在连续混合（如0.1C、0.5C和1C）充放电150次后,LiMn_1.9Al_0.1O_3.95F_0.05电极的容量仍能保持90%以上.     

二氧化锰含量对活性炭电极电化学性能的影响

本文采用液相法、热分解MnCO₃法以及电解沉积法制备不同二氧化锰粉末,并将其与活性炭复合,应用于水系超级电容器. 使用X射线衍射（XRD）、扫描电子显微镜（SEM）技术对材料形貌进行表征. 使用循环伏安法以及恒流充放电法对其电化学性能进行测试. 实验数据表明,α-MnO₂（质量分数70%）掺杂活性炭电极的最大比容量为151 F•g^-1,β-MnO₂（质量分数60%）掺杂活性炭电极的最大比容量为172F•g^-1,γ-MnO₂（质量分数50%）掺杂活性炭电极的最大比容量为141F•g^-1,但二氧化锰粉末对电极内阻的影响呈无规律性.     

Effect of current density on the microstructure and corrosion behaviour of plasma electrolytic oxidation treated AM50 magnesium alloy

Plasma electrolytic oxidation (PEO) of an AM50 magnesium alloy was accomplished in a silicate-based electrolyte using a DC power source. Coatings were produced at three current densities, i.e. 15 mA cm⁻², 75 mA cm⁻², and 150 mA cm⁻² and were characterised for thickness, roughness, microstructural morphology, phase composition, and corrosion resistance. Even though the 15 min treated coatings produced at higher current density levels were thicker, they showed poor corrosion resistance when compared to that of the coatings obtained at 15 mA cm⁻². Short-term treatments (2 min and 5 min) at 150 mA cm⁻² yielded coatings of thickness and corrosion resistance comparable to that of the low current density coatings. The superior corrosion resistance of the low thickness coatings is attributed to the better pore morphology and compactness of the layer.     

Preparation and properties of electroless Ni-P-SiO2 composite coatings

Dispersible SiO₂ nanoparticles were co-deposited with electroless Ni-P coating onto AISI-1045 steel substrates in the absence of any surfactants in plating bath. The resulting Ni-P/nano-SiO₂ composite coatings were heat-treated for 1 h at 200 °C, 400 °C, and 600 °C, respectively. The hardness and wear resistance of the heat-treated composite coatings were measured. Moreover, the structural changes of the composite coatings before and after heat treatment were investigated by means of X-ray diffraction (XRD), while their elemental composition and morphology were analyzed using an energy dispersive spectrometer (EDS) and a scanning electron microscope (SEM). Results show that co-deposited SiO₂ particles contributed to increase the hardness and wear resistance of electroless Ni-P coating, and the composite coating heat-treated at about 400 °C had the maximum hardness and wear resistance.     

Characteristic and microstructure of the microarc oxidized TiO2-based film containing P before and after chemical- and heat treatment

Chemical- and heat treatment was performed to modify the surface of the microarc oxidized TiO₂-based (TOB) film containing P to produce nano-scale compounds containing Na, Ti and O elements. In the TOB film, anatase and rutile nanocrystals were randomly distributed in P-doped matrix. On the surface of the chemically treated TOB (C-TOB) film, amorphous titanium oxide containing Na shows nano-scale ribbonlike morphology. Na, Ti and O show uniform distribution in the outer layer of the C-TOB film along surface depth. Chemical treatment did not alter the surface roughness of the TOB film obviously; however, it improved its hydrophilic property. Heat treatment has no influence on the chemical states of Ti, Na and O, as well as wetting ability, elemental composition and atomic concentration in the outer layer of the C-TOB film. However, the phase compositions and surface morphology of the C-TOB film after heat treatment are dependent on the heat treatment temperature.     

快速凝固Cu-Pb过偏晶合金的性能表征

研究了Cu-Pb过偏晶合金的急冷快速凝固组织特征,定量表征了快速凝固Cu-Pb过偏晶合金的电阻率和力学性能,理论分析了冷却速率和组织形态对合金性能的影响规律. 研究结果表明,在急冷快速凝固条件下,Cu-Pb过偏晶合金中的(Cu)相和(Pb)相均以枝晶方式生长,晶体形态以均匀细小的等轴晶为特征. 随着冷却速率增大,一方面,凝固组织显著细化,晶界增多,对自由电子的散射作用增强,合金电阻率显著增大;另一方面,细晶强化作用增强,合金的抗拉强度呈线性升高,同时,伴随着晶体缺陷数量的增多,合金的伸长率降低. 关键词： Cu-Pb过偏晶合金 快速凝固 电阻率 力学性能     

U–Al system: Ab-initio and many body potential approaches

The U–Al binary system exhibits the formation of three intermetallic compounds: cubic Laves phase C15 UAl₂, cubic L1₂ UAl₃, and orthorhombic D1_b UAl₄. However, some uncertainties are found in the literature concerning UAl₄ structure and composition. A computational first principles based approach is a useful tool to shed some light on this problem. To the author's knowledge there are no such contributions. UAl₄ stabilization with composition and uranium constitutional vacancies is specially discussed.     

MgxZn1-xO薄膜的生长及其光学性能

利用金属有机化学气相沉积(MOCVD)法在蓝宝石(1120)衬底上生长高质量的Mg_xZn_1-xO合金薄膜,实验研究了各种不同Mg组分对样品光学性能的影响。通过光致发光荧光衰减特性对激子发光寿命的研究表明,激子的寿命随Mg组分的增加而增加,当Mg组分达到50%时,激子的寿命为872 ps。     

论FeCr合金辐照损伤的多尺度模拟

铁素体/马氏体钢具有优异的抗辐照肿胀和抗腐蚀能力,是聚变堆、ADS和四代堆结构材料重要候选者之一.多尺度模拟在核武器自辐照损伤、压力容器辐照脆化、医学材料辐照损伤等方面有着广泛的应用.国际上围绕F/M FeCr合金辐照损伤开展了大量的多尺度模拟工作.论文概述了F/M FeCr合金辐照损伤多尺度模拟研究现状及进展,并针对目前存在的某些问题提出了解决建议. 关键词： 铁素体/马氏体FeCr合金 辐照损伤 多尺度模拟     

红外测温法研究Al-Mg合金中的Portevin-Le Chatelier效应

试件塑性变形过程伴随着机械能向热能的转化.利用红外测温法,通过分析红外热像仪采集的温度场图像,系统研究了Al-Mg合金中的Portevin-Le Chatelier （PLC）效应.在不同应变率下,实验得到了三类锯齿形应力-应变曲线,分析了相应情况下试件温度变化曲线的异同及其原因,探讨了三种类型PLC变形带的空间传播特性.研究发现,试件表面的温升随着应变率的增加而增加;PLC带的倾角转向发生在试件的两端或者带外的温度最高处. 关键词： Portevin-Le Chatelier效应 红外测温 Al-Mg合金