Thermogravimetric Evidence of Cobalt or Manganese Isomorphously Substituted into a Zeolite

Pure silica zeolite ZSM-5 has been synthesised in a slightly acidic aqueous fluoride medium which produces the protonated form of the zeolite ZSM-5 [1]. Tetrahalometallate [2] species of cobalt and manganese have been synthesised and increasing mole fractions incorporated into the zeolite synthesis gel. The products have been analysed and characterised using simultaneous thermogravimetric-derivative thermogravimetric analysis (TG-DTG). The thermal decomposition, under nitrogen of the associated tetraethylammonium (TEA⁺) and tetrapropylammonium (TPA⁺) cations occluded within the zeolite channels is indicative and characteristic of the incorporation of the heteroatoms into the zeolitic framework. Analysis by X-ray diffraction (XRD), scanning electron microscopy (SEM), X-ray fluorescence (XRF), and Fourier transform infrared spectroscopy (FTIR) has confirmed the reliability of thermogravimetric (TG) and derived thermogravimetric analysis (DTG) as a diagnostic tool. This revised version was published online in July 2006 with corrections to the Cover Date.     

对甲苯磺酰谷氨酸桥联的一维双链锰配合物的合成、表征与晶体结构

A one-dimensional double-chain coordination polymer [Mn(phen)(tsgluo)] was synthesized in a mixed solution and its crystal structure was determined by X-ray diffraction method. It crystallizes in orthorhombic system with space group P2₁2₁2₁. The crystal data are: a=0.530 78(17) nm, b=1.723 9(5) nm, c=2.456 9(8) nm, Z=4, μ=0.729 mm^-1, D_c=1.579 g·cm^-3, V=2.248 1(12) nm³, R₁=0.033 1, ωR₂=0.078 9. In the title complex, each Mn(Ⅱ) ion presents a octahedral geometry with the coordination of two nitrogen atoms from 1,10-phenanthroline and four oxygen atoms from three different tsgluo^2- ligands. The γ-carboxyl coordinates to Mn(Ⅱ) in the mode of bidentate chelate, while the α-carboxyl coordinates in a bidentate bridging mode. CCDC: 253910.     

锂离子电池负极合金CoSn和Cu-Sn的制备与表征

CoSn alloy and Cu-Sn samples were synthesized by H₂-reduction following solid-state reaction between Co(Ⅱ)， Cu(Ⅱ)， Sn(Ⅳ) and NaOH at ambient temperature. The samples were characterized by XRD， SEM. The results showed that CoSn alloy (80～200nm) is globe-shaped， ultrafine hexagonal material， and Cu-Sn alloy powder consists of two phases， i.e. Cu₆Sn₅ and Cu₃Sn. Cu-Sn powder has spherical morphology and the particle size is estimated to be 60～70nm. The electrochemical performances of CoSn alloy and Cu-Sn powder were studied using lithium-ions model cell Li/LiPF₆ (EC+DMC)/CoSn (or Cu-Sn). It was demonstrated the reversible discharge capacities for 10 cycles keep above 280mAh·g^-1 for nanophase Cu-Sn， and 60mAh·g^-1 for CoSn alloy. Differ-ential capacity plots showed that the reaction mechanisms of Cu-Sn with lithium were reversible.     

Methane Combustion Over Fe, Co and Ni Modified Manganese Oxide Catalysts

Fe-Mn, Co-Mn and Ni-Mn composite oxide catalysts based on high specific surface area MnO₂ precursor were prepared and applied to catalytic combustion of CH₄. Results were compared with that of unmodified MnOx and 1wt.% Pd/-Al₂O₃. Below 450°C, manganese oxide catalysts show higher activity than Pd/-Al₂O₃, while the modified manganese oxide catalysts exhibit higher activity than the unmodified one below 420°C. All catalysts were characterized by means of N₂-BET, XRD, TG-DTA and H₂-TPR. Due to the interaction between Fe, Co or Ni oxides and manganese oxide, the activity of the oxygen species of the modified catalysts is improved, which leads to the increase of their CH₄ combustion activity.     

SOLID STATE CHEMISTRY OF La_(1-x)Li_(x)MnO_3 AND RELATED COMPOUND

A series of perovskite type oxides La_(1-x)A_(x)MnO_3(x=0.1 for A=Li,Na,K;x=0.1～0.5 for A=Li)have been prepared by impregnation.Experimental results showed that the substitution of La~(3 ) by Li~ inLaMnO_(3 ?) greatly increased the selectivity to ethane and ethylene for theoxidative coupling of methane.Temperature-programmed desorption of oxygenproved the presence of oxygen vacancies in the oxide lattice.The higher Mn~(4 )/Mn_t ratio in oxide made the formation of oxygen vacancies easier on the oxidesurface.The general formula of the oxides is La_(1-x)Li_(x)Mn＇V＇_(y)O_(3-y),V=vacancy.     

低钴AB5型稀土系贮氢电极合金的研究

为了进一步降低AB5型混合稀土系贮氢合金的成本,采用Cr,Si,Cu替代Co和调节化学计量比的方法制备低钴AB5型贮氢合金。结果表明:3种取代元素在寿命方面的效果依次为Si>Cr>Cu,在放电容量和活化性能方面依次是Cu>Cr>Si。Cr,Cu,Si只有少量的替代才可能发挥其有利影响;通过非化学计量比的调节,低钴混合稀土系贮氢电极合金的放电容量、活化性能及倍率放电能力都能较好地达到实用要求,但是循环寿命有待提高。     

N,N-二甲基甲酰胺中电沉积制备镁镍储氢合金

采用恒电位沉积法, 选用适宜的添加剂和络合剂, 成功地从N,N-二甲基甲酰胺(DMF)中沉积出致密的黑色Mg-Ni储氢合金膜. 并初步探讨了其共沉积机理. XRD显示沉积层中含有非晶态Mg-Ni相和微晶态Mg相. SEM图及相应能谱图分析表明合金颗粒以团聚状态存在, 合金成分不是很均匀. AAS分析表明沉积合金中Mg的原子摩尔分数达27.3%. LAND电池测试系统测得所镀合金膜的放电比容量最高为172.4 mAh/g.     

2A12-T6铝合金表面双-(γ-三乙氧基硅丙基)四硫化物薄膜的特性

采用傅立叶变换红外光谱分析了2A12-T6铝合金表面自组装双-(!-三乙氧基硅丙基)四硫化物硅烷偶联剂(SCA)薄膜结构特征,并采用电化学极化曲线评价了薄膜的耐蚀性能.结果表明,铝材表面自然晾干,SCA薄膜分子之间主要通过氢键连接,腐蚀电流密度减小1个数量级以上.120℃的加热处理促进铝板表面通过SiOSi链接而形成SCA网状薄膜结构,并通过在界面上形成SiOAl界面相结构而与铝板表面牢固连接,腐蚀电流密度降低2个数量级以上.SCA乙醇溶液浸泡处理10min比浸泡2s～1min的铝板表面SCA薄膜内氢键缔合羟基要多.     

混合稀土对共晶Al-2%Fe合金组织形态的影响

研究了富La混合稀土对共晶Al-2?合金组织形态的影响. 当混合稀土加入量较少时, 合金中的α-Al相为明显的胞状枝晶;随着混合稀土加入量的增加, α-Al枝晶优先形核生长得到抑制, 共晶Al3Fe相得到细化;当稀土加入量增至0.6% (质量分数)共晶Al3Fe相尺寸逐渐增大. 并对混合稀土对共晶Al-2?合金组织形态的影响机制进行了探讨.     

粉末化学镀法制备的NiB／TiO2非晶态合金催化剂对环丁烯砜加氢反应的催化性能

 采用诱导沉积法及粉末化学镀法分别制备了纯态NiB及负载型NiB／TiO2非晶态合金催化剂．用XRD，ICP，SEM，TEM和DSC等手段对催化剂的物性及TiO2载体与NiB非晶态合金之间的相互作用进行了表征，考察了非晶态合金的结构、组成、形貌和热稳定性，并将其用于环丁烯砜加氢反应中．结果表明，相对于NiB而言，NiB／TiO2催化剂具有优良的热稳定性和催化活性，这缘于NiB和TiO2载体之间的相互作用及载体的分散作用．