An experimental study on the kinetics of leaching for the preparation of a Raney-silver catalyst

A Raney-Ag catalyst was prepared by leaching out aluminium from a Raney Ag-Al alloy with NaOH solution. The kinetics of leaching has been investigated in a stirred-batch-reactor at various temperatures by using alloy particles of different sizes. The kinetic model best fitting the experimental results has been determined. This revised version was published online in June 2006 with corrections to the Cover Date.     

快冷Fe_(71)Al_(29)合金中的两个内耗峰

用一个计算机控制的倒扭摆研究了快冷Fe71 Al2 9合金中的两个内耗峰 .在快冷的Fe71 Al2 9样品中分别在 180℃(P1 ) ,340℃ (P2 )和 5 10℃ (P3)出现了内耗峰 ,而在慢冷的Fe71 Al2 9样品中只发现了P3峰 .快冷样品中的P1 和P2峰在从 6 5 0℃冷却下来的测量过程中或在 35 0℃经过较长时间的时效后消失 ,其峰高随时效时间的增加而下降 ,直至消失 .P1 和P2 峰都有弛豫特征 ,它们的激活能分别为 :H1 =1.0 3± 0 .0 8eV(P1 峰 ) ;H2 =1.6 4± 0 .0 5eV(P2 峰 ) .P1 峰被认为是无序合金中Al原子在四面体点阵内的最近邻运动所引起 ,P2 峰则是无序合金中Al原子在四面体点阵内的次近邻运动所引起     

Mossbauer investigations of corrosion environment influence on Fe valence states in oxide films of zirconium alloys

Mössbauer investigations about iron atom redistribution in oxide films of zirconium alloys subjected to corrosion at 500°C in pure oxygen and water pair have been analysed. The alloys were also subjected to autoclave conditions at a pressure of 10.0 MPa and autoclave conditions at 350°C and at a pressure of 16.8 MPa, using distilled water and water with additives of lithium and fluorine. It is shown that, depending on the corrosion environment, various compounds of iron, such as α-Fe₂O₃, Fe₃O₄, and FeO, as solid solutions of iron in ZrO₂ are formed in oxide films.     

侵彻环境下两种钨合金的细观响应特性

本文实验发现具有较大密度和较高速度的93W钨合金长杆模拟弹的穿靶深度反而比密度较小，速度较低的90W钨合金长杆弹的穿靶深度小．针对这一现象，本文从两种材料在侵彻环境下的细观响应特性的差异上给出了有实验根据的合理分析，结论是90W在侵彻环境下较易于形成绝热剪切带，从而在弹头部发生“自锐化”效应所致．     

Specific heat and related thermophysical properties of liquid Fe-Cu-Mo alloy

The specific heat and related thermophysical properties of liquid Fe77.5Cu13Mo9.5 monotectic alloy were investigated by an electromagnetic levitation drop calorimeter over a wide temperature range from 1482 to 1818 K. A maximum undercooling of 221 K (0.13 Tm) was achieved and the specific heat was determined as 44.71 J·mol-1·K-1. The excess specific heat, enthalpy change, entropy change and Gibbs free energy difference of this alloy were calculated on the basis of experimental results. It was found that the calculated results by traditional estimating methods can only describe the solidification process under low undercooling conditions. Only the experimental results can reflect the reality under high undercooling conditions. Meanwhile, the thermal diffusivity, thermal conductivity, and sound speed were derived from the present experimental results. Furthermore, the solidified microstructural morphology was examined, which consists of (Fe) and (Cu) phases. The calculated interface energy was applied to exploring the correlation between competitive nucleation and solidification microstructure within monotectic alloy.     

室温下压致铁钴镍合金的bcc→hcp相变

 本文采用高压X光衍射方法在金刚石对顶压砧中在位地（in situ）研究了Fe₆₈Co₂₄Ni₈（wt%）合金在室温下的压致bcc→hcp结构相变和直到40.5 GPa的等温压缩行为。实验结果表明该合金在常压下为bcc结构，晶格常数a₀=(0.287 0±0.000 1) nm，体积V₀=(7.119±0.007) cm³/mol，密度ρ₀=(7.981±0.008) g/cm³；在20.9 GPa附近出现bcc→hcp结构相变，两相共存压力区约10 GPa，在此区域内有晶面间距d(002)_hcp=d(110)_bcc，且原子平面(002)_hcp//(110)_bcc，hcp相比bcc相体积减小(0.33±0.02) cm³/mol；高压相hcp结构的晶格参数比值c/a=1.608±0.004；相变后原子配位数的增加使得hcp相(002)平面内及(002)平面间的最近邻原子间距比bcc相最近邻原子间距分别增大约1.6%和0.5%；用Murnaghan状态方程对实验数据进行最小二乘法拟合，得到bcc相B₀=(130±13) GPa，B₀'=12.6±0.5；hcp相V₀=(6.62±0.04) cm³/mol，B₀=(243±21) GPa，B₀'=6.8±0.3；对于该合金的bcc→fcp相变时的结构转变机制做了详细的讨论。     

Mössbauer effect study of the decagonal quasicrystal Al65Co15Cu20

The ⁵⁷Fe Mössbauer effect study at 5.0 K and in an external magnetic field of 9.0 T on a high-quality stable decagonal quasicrystal Al₆₅Co₁₅Cu_19.9Fe_0.1 is presented. It is shown that the iron atoms are located in two distinct classes of sites. The values of the principal component of the electric field gradient tensor and the asymmetry parameter at these sites are, respectively, ?1.90(10)?×?10²¹ V/m², 0.97(15) and ?3.95(12)?×?10²¹ V/m², 0.00(17).     

微脉冲电子枪的初步实验研究

给出了微脉冲电子枪的模拟计算及其初步实验结果. 该电子枪采用铜铝镁合金作为冷阴极材料, 在以磁控管作为微波功率源的出束实验中得到了100mA/cm²的电流密度.实验结果与次级电子倍增解析计算和SEEG程序的模拟计算结果基本符合, 初步验证了微脉冲电子枪的基本原理, 为今后实验中得到更大的电流密度打下了基础.     

3004铝合金“反常”锯齿屈服现象的研究

在应变速率为5.56×10^-5s^-1—5.56×10^-3s^-1的范围内，在不同温度下(从223K至773K)，对3004铝合金进行系列拉伸试验，探索其锯齿屈服规律；通过激活能的计算、内耗研究、微观组织观察和能谱分析，探讨锯齿屈服的机理与物理本质.结果表明，3004铝合金在形变过程中会出现动态应变时效现象；发现了一种“反常”的锯齿屈服现象：在出现锯齿屈服的温区内，存在锯齿屈服临界应变量转变温度T_t， 关键词： 动态应变时效 锯齿屈服 铝合金 内耗