NdOx作为助催化剂对PtRu/C电催化氧化甲醇活性的影响

采用沉积-还原法制备了PtRu-NdOx/C催化剂, 借助TEM、EDS和XRD等测试手段对其进行了微结构和组成的表征. 结果表明, 催化剂中Pt与Ru以合金形式存在, 而Nd的氧化物则以无定形形态存在. 催化剂粒子的平均粒径在2 nm左右, 晶胞参数为0.3896 nm, Nd氧化物的加入对PtRu合金的晶体结构影响不明显. 采用循环伏安法和计时电流法, 比较了PtRu-NdOx/C催化剂和PtRu /C催化剂对甲醇氧化的电催化活性, 结果表明, 加入Nd的氧化物作为助催化剂能明显提高PtRu /C催化剂对甲醇氧化的电催化性能.     

桥联双β-环糊精对N-[4-(1-芘基)]丁酰-D/L-苯丙氨酸的手性识别及机理研究

利用紫外-可见吸收和荧光发射光谱, 结合非线性最小二乘法拟合曲线以及分子力学(MM2)模拟系统地研究了手性分子N-[4-(1-芘基)]丁酰-D/L-苯丙氨酸(PDP和PLP, 总称PPs)与β-环糊精(β-CD)、 2-位硒桥联双β-CD(2-SeCD)和2-位碲桥联双β-CD(2-TeCD)的包结能力大小及这3个环糊精对PPs手性识别能力的差异和识别机理. 研究结果表明, PPs不能与单疏水空腔的β-CD形成很好的包结复合物, 与具有较长桥联链的2-TeCD结合能力最强. 2-TeCD与PDP和PLP的结合常数分别为2.33×104和6.07×103 L/mol, 对PPs的手性识别比达到KD/KL=3.84, 高于2-SeCD(KD/KL=2.61). 用MM2模拟得出了PPs与这两个双环糊精形成复合物的三维结构: PPs的绝大部分位于双环糊精两个空腔之间, 但是在这两个复合物中, 苯环与芘环所成的二面角不同. 此外, PPs与这两个双环糊精作用时均存在明显的氢键相互作用, 且2-TeCD强于2-SeCD.     

明胶中α组分含量对明胶/羟基磷灰石复合材料力学性能的影响

选用α组分含量分别为20.5%,41%和50%的A、B、C 3种明胶作为原料,采用同时加入法制备了明胶/羟基磷灰石(HAP)复合材料.通过对干态复合物膜拉伸性能的测试和对比,发现,明胶α组分含量的变化对复合材料的弹性模量影响较大,而对拉伸强度和断裂伸长率的影响则相对较小,但总的来说,三者均随α组分含量的增加而增大.其中,α组分含量最高的复合物C的拉伸强度为86.40 MPa,弹性模量为2682.35 MPa,断裂伸长率为8.65%.另外,对复合物C基本性质的表征结果表明,该材料具有类似于自然骨的组成和结构性质,因此有望成为一种具有优异力学性能的骨替代材料.     

甲烷在Mo/HZSM-5催化剂上的脱氢聚合反应

对不同Mo含量的Mo／HZSM－5催化剂的结构进行了表征，并对这些催化剂的甲烷非氧气氛下的转化反应进行了考察．催化剂的BET比表面积及酸性随Mo含量的增加而降低，当Mo含量大于5％时，Mo对ZSM－5分子筛的晶型有影响，并出现MoO3物相．甲烷在700℃时可高选择性地生成苯和乙烯，最佳Mo含量大约为2％．纯的MoO3或HZSM－5上该反应几乎不进行，因此，可能是分散的钼氧离子和分子筛的酸中心是甲烷转化的活性中心，只有二者的协同作用才能促进甲烷的转化．反应后催化剂中的钼物种被还原了．催化剂上的积炭可能是催化剂失活的主要原因之一，烧炭后催化剂活性基本恢复．     

分散法制备的CuCl/MCM-41上C3H6选择催化还原NO反应的研究

研究了由分散法制备的两种CuCl/MCM-41催化剂上丙烯在过量氧存在下选择催化还原NO反应, 发现所制备的CuCl/AlMCM-41催化剂的反应活性明显高于CuCl/SiMCM-41. XRD, IR, TPR及ESR的研究结果表明, CuCl/AlMCM-41催化剂上的主要活性中心是与骨架铝配位的铜离子(Cu2+/Cu+).     

Enhanced Acid/Base Catalysis in High Temperature Liquid Water

High temperature liquid water (HTLW), as an environmentally benign medium, has drawn increasing attention for organic chemical reactions and biomass conversion1-3. HTLW has a strong tendency to ionize and can act as an acid and/or base catalyst. In addition, HTLW can dissolve organic compounds to some extent allowing for a homogenous reaction within an aqueous phase. Extensive researches4-10 have been pursued on acid/base-catalysis reactions in HTLW without addition of acid or base. Howe…     

Preparation and Characterization of Nano-ZnFe2O4/TiO2 Films

The nano-ZnFe2O4/TiO2 films possess the functions of desulfurization and degradation for organic pollutants. The sols of ZnFe2O4/TiO2 were prepared by sol-gel method and coated on glass and porous ceramic by vertical coating and dipping-lift processes, respectively, and the samples were obtained after drying and sintering. The composition, appearance, absorption spectrum of the films, and the influence of the film on porous ceramic performances were analyzed using SEM, AFM, UV-Vis spectrometer, and mercury porosimeter, respectively, to determine the operation parameters of the multifunction porous ceramic elements for gas-purification.     

多柱色谱技术进展

在色谱分析过程中，利用串联、并联或串并联结合的方式将多根色谱柱组合起来，可以实现高通量和高分辨的分离效果。相比于传统单柱色谱技术，多柱技术很好地满足了批量样品分析和复杂生物样品分离分析的需求，因此引起了广泛关注。该文对多柱技术在多维分离、芯片色谱、毛细管电泳、固定相筛选以及串联色谱等领域的应用进行了综述，并对其发展前景进行了展望。     

在二甲基亚砜中电化学制备铈钴合金

利用循环伏安法和恒电位电解法研究了室温下在二甲基亚砜中铈钴合金膜的电化学制备.结果表明,二甲基亚砜中Ce(Ⅲ)在Pt电极上的还原反应为一步完全不可逆反应.控制沉积电位在-2.10V～2.30V,利用恒电位电解得到表面平滑,附着力好,铈含量为37wt%～45wt%的铈钴合金膜.     

红外光谱研究甲烷和氧与SrO-La2O3/CaO表面的相互作用

在甲烷氧化偶联（ＯＣＭ）反应条件下，用原位红外光谱研究ＳｒＯ－Ｌａ２Ｏ３／ＣａＯ催化剂，结果表明，晶格氧使甲深度氧化，Ｌａ２Ｏ３和ＣａＯ具有活泼的晶格氧，ＳｒＯ的晶格氧比较稳定，气相氧通过催化剂表面消耗掉的晶格氧，加速甲烷了深度氧化，另一方面，催化剂表面的碳酸根物种在氧气氛下分解，在Ｌａ２Ｏ３和ＬＣ催化剂中，催化剂表面Ｌａ２Ｏ２（ＣＯ３）的分解形成配位不饱和的晶格氧Ｏ＾２－，并为气相氧吸附提供氧空