Synthesis and Infrared Multi‐band Absorption Properties of Core‐shell NaYF4:Yb3+, Er3+@SiO2 Nanoparticles

Due to the unique size effects, nanomaterials in infrared absorption have attracted much attention for their strong absorption in the infrared region. To achieve the infrared multi‐band absorption, we propose to synthesize a core‐shell structure nanomaterial consisting of NaYF₄:Yb³⁺, Er³⁺ core and a layer of SiO₂ as shell. A series of NaYF₄:Yb³⁺, Er³⁺ nanocrystals were synthesized through hydrothermal method by adjusting the ratio of citric acid(CA)‐to‐NaOH, and the effects of CA concentration, and NaOH concentration were studied in detail. NaYF₄:Yb³⁺, Er³⁺@SiO₂ nanoparticles were synthesized by sol‐gel method using TEOS as silica source. The results show that the core‐shell NaYF₄:Yb³⁺, Er³⁺@SiO₂ nanoparticles were successfully synthesized. Up‐conversion spectra of these nanoparticles were recorded with 980 nm laser excitation under room temperature. There are no changes of the emission centers of nanoparticles before or after silica coating, but the emission intensities of nanoparticles after silica coating are weakened. Furthermore, the property of infrared multi‐band absorption was tested through ultraviolet‐visible‐near infrared spectrophotometer and infrared absorption spectra. The results illustrate that the multi‐band infrared absorption nanomaterial was successfully synthesized.     

Mo/Fe3O4(111)表面对燃煤烟气汞吸附的密度泛函研究

利用CASTEP软件包采用密度泛函理论计算研究了过渡金属Mo掺杂Fe_3O_4(111)Fe_(tet)表面对Hg~0、HgCl和HgCl_2的吸附特征,分析了Mo掺杂前后Fe_3O_4(111)Fe_(tet)表面上不同汞物种的吸附形态。结果表明,Mo掺杂Fe_3O_4(111)Fe_(tet)表面对HgCl和HgCl_2为化学吸附,而对Hg~0的吸附为物理吸附;与纯净表面相比,HgCl在Mo原子掺杂表面上的吸附能提高了40%-66%。HgCl_2在纯净Fe_3O_4(111)Fe_(tet)表面形成"M"形结构;而掺杂Mo原子后,由于Cl原子与Mo原子之间更强的相互作用,使得HgCl_2发生了完全解离,两个Cl原子分别与Mo原子和Fe原子成键吸附在表面,Hg脱附。相关研究结果可为脱除燃煤烟气中的汞提供一定的理论指导。     

镧掺杂锡酸钡/多壁碳纳米管改性隔膜的制备及其在锂硫电池中的应用

通过将共沉淀法制备的钙钛矿型氧化物镧掺杂锡酸钡(LBSO)与多壁碳纳米管(MCNT)混合均匀,制成浆料,并利用刮涂法将其涂布在商业隔膜Celgard 2500(PP)表面构筑阻挡层,获得改性隔膜(LBSO/MCNT/PP)。基于该改性隔膜的锂硫电池在0.1C下具有高达1 433 mAh·g^-1的初始放电比容量,1C时300次循环后每圈容量衰减率为0.114%;当电流密度提高到3C时,仍具有764 mAh·g^-1的放电比容量,表现出优良的倍率性能和循环稳定性,这主要是由于该阻挡层能够有效抑制多硫化物的穿梭。     

碱土金属Ben (n=1~3)对B12团簇结构的调控研究

基于第一性原理, 系统地研究了Be_n (n=1~3)对B₁₂团簇结构的调控. 结果表明: 团簇BeB₁₂全局极小结构为C_s对称性准平面结构, 而Be₂B₁₂和Be₃B₁₂最稳定的结构均为笼状结构, 对称性分别为C_s和C_2v. 随着Be_n (n=1~3)原子数的增加, 团簇B₁₂由准平面结构过渡到笼状结构, 且Be倾向内嵌在B₁₂笼状结构表面的B₇或B₈单元环中, 通过离子和共价作用形成稳定Be&B₇和Be&B₈单元, 从而稳定笼状结构. 自然键轨道(NBO)分析表明, 团簇C_s BeB₁₂, C_s Be₂B₁₂, C_2v Be₃B₁₂内部存在电子转移情况, Be原子2s轨道上失去电子, Be—B键主要以离子作用为主, 同时也存在共价作用. 成键分析显示C_s Be₂B₁₂和C_2v Be₃B₁₂的π键遵循球状芳香性2(n+1)² (n=1)电子计数规则, 表明该团簇具有球状芳香性. 预测了三个结构的红外和拉曼光谱, 为以后的合成实验和数据表征提供了理论基础.     

过渡金属/氮掺杂石墨的制备及电催化氧还原

用简单的化学方法制备了过渡金属(TM)壳聚糖水杨醛席夫碱配合物,然后以此配合物为金属源和N源、以硝酸预处理石墨为载体,经热处理后制备了过渡金属/氮掺杂石墨催化剂TM-N-C-t(TM=Co,Ni,Cu;t=200,400,600,800,1 000℃).以此催化剂为修饰剂制备了玻碳修饰电极,并用循环伏安法(CV)和旋转圆盘电极(RDE)伏安法研究了催化剂TM-N-C-t的电化学行为和电催化氧还原(ORR)的催化性能,催化剂的组成和结构采用TG,FT-IR,XRD,XPS等技术进行了表征.研究结果表明,催化剂TM-N-C-t对ORR均显示不同程度的催化活性,其中以1 000℃热处理的钴基催化剂Co-N-C-1000的催化活性最好,其活性已接近相同条件下的商用催化剂JM 20%Pt/C,催化活性位主要为Co—N—C.根据扩散控制的不可逆反应的循环伏安行为,计算得到了TM-N-C-t催化剂电催化ORR的动力学参数,并以此提出了氧还原催化反应的机理,在活性最好的催化剂Co-N-C-1000修饰电极上,氧气以4e转移途径被还原为水.     

小麦粉衍生中孔氮掺杂颗粒炭负载金催化剂用于乙炔氢氯化反应（英文）

聚氯乙烯是五大工程塑料之一,在国民经济中占有重要的地位.基于中国富煤少油缺气的能源格局,我国主要采用基于煤化工的电石法氯乙烯生产工艺,但该工艺必须采用氯化汞催化剂,受到国际限汞公约的影响,无汞催化剂的开发迫在眉睫.其中炭负载金催化剂在该反应中活性最高,近几年来取得了较大进展,有望实现产业化.氮掺杂的炭材料在诸多反应中展现了较好的性能,其负载金属催化剂可以有效提高金属的分散度及稳定性,成为近几年多相催化领域的一个研究热点.最近我们课题组报道了一种氮掺杂中孔成型的制备方法:以小麦粉为原料,通过直接炭化法制备了氮掺杂中孔成型炭,这种氮掺杂中孔成型炭作为无汞催化剂在乙炔氢氯化反应中显示出了优异的催化性能.小麦粉衍生的氮掺杂中孔成型炭具有成型容易.原料价廉易得、易于放大生产等优点,是优选的工业化催化剂的载体.本文以这种氮掺杂的成型炭为载体制备了负载型金催化剂,研究其催化乙炔氢氯化性能.结果表明,氮的掺杂使得中孔炭负载金(Au/N-MC)催化剂上乙炔氢氯化活性明显提高.在氯化氢/乙炔比例1.1、反应温度180℃、乙炔空速600 h~(-1)的条件下,Au/N-MC上的乙炔转化率为50%,是Au/MC催化剂活性的2倍.通过对催化剂的表征发现,氮的掺杂能有效地锚定Au/N-MC催化剂中活性组分Au~(3+),抑制催化剂制备过程中Au~(3+)还原为Au~0,从而提高催化剂活性和稳定性.小麦粉衍生的氮掺杂中孔炭的原料廉价易得,生产工艺简单,易成型,也容易实现工业化生产,是负载型金属催化剂的优良载体,其负载的无汞催化剂性能优越,有望取代电石法氯乙烯产业的汞催化剂,成为新一代无汞催化剂.     

蟹壳基氮/氧共掺杂多孔炭的原位制备及其超级电容器性能

采用废弃蟹壳为碳源,KOH为活化剂原位制备了氮/氧共掺杂多孔炭,并研究其作为电极材料在超级电容器中的应用。 固定蟹壳与KOH的质量比为5:3,考察了煅烧温度对所得炭材料产率、孔结构和氮氧含量的影响。 结果表明,蟹壳基炭材料的孔结构和氮/氧含量可通过改变煅烧温度调变。 随着煅烧温度从500 ℃上升至700 ℃,多孔炭的比表面积和孔体积逐渐增大,而氮/氧含量随温度升高则降低。 采用循环伏安和恒流充放电对所得材料的电化学性能进行测试。 结果表明,所得多孔炭的电化学性能取决于其孔结构与氮/氧表面性质的协同作用,其中煅烧温度为600 ℃所得的多孔炭比表面积为612 m²/g,氮和氧含量分别为3.53%和32.8%,在50 mA/g的电流密度下比电容达到310 F/g,循环1000次比电容仍然保持95%以上,展现出良好的电化学性能。     

基于聚多巴胺的氮掺杂碳材料的制备及其电化学性能

多孔碳材料由于高的比表面积、优异的电子传导率、良好的化学稳定性等优点在超级电容器电极材料领域被广泛研究。 碳材料的组成及表面孔结构直接影响其电化学性能,为进一步提高碳材料的电容性能,本文首次以聚多巴胺球为前体,KOH为活化剂,通过高温碳化成功制备了良好电化学性能的氮掺杂多孔碳材料。 通过扫描电子显微镜(SEM)、透射电子显微镜(TEM)、 X射线粉末衍射(XRD)、傅里叶变换红外光谱(FT-IR)、X射线光电子能谱(XPS)和Raman光谱等对所制备的氮掺杂多孔碳材料进行了形貌及结构组成的表征。 在6 mol/L KOH电解液中, 采用循环伏安、恒电流充放电对多孔碳材料的电化学性能进行了研究。 结果表明,由于双电层电容和赝电容的协同作用,在电流密度为1 A/g时,材料的比电容可达269 F/g,充放电循环1000圈后电容仍可保留初始值的93.5%。     

利用钐掺杂氧化铈提高燃料电池阳极活性

用浸渍法制备并采用交流阻抗、极化等技术考察了不同组成的Ni-Sm3＋掺杂的CeO2(SDC) 复合镍阳极的电化学性能及相应电池的功率输出性能.结果表明，SDC掺入镍阳极后,阳极极化过电位及电池的欧姆电阻显著减小.其中阳极过电位的减小与SDC掺入镍电极引起的三相界扩展有关，但SDC的掺入同时引起了电极反应活化能的增加,造成低温下Ni-SDC的极化过电位大于纯Ni电极.高温下,Ni-SDC阳极的阻抗谱由两个半圆组成，其中高频半圆随着SDC掺入量的增加而减小,而低频环与SDC的掺入量基本无关.低温下只观察到一个高频环.高频环可能对应三相界反应,而低频环可能对应氢的解离吸附及扩散.75％（w）Ni-25％（w）SDC/La0.9Sr0.1Ga0.8Mg0.2O3(LSGM)/Sm0.5Sr0.5CoO3(SSC)在所研究的电池中具有最大功率输出密度，其值在1073、973、873 K下分别达到1.1、0.43、0.14 W•cm－2.     

过渡金属掺杂二氧化钛光催化性能的研究

采用浸渍法制备了过渡金属掺杂的光催化剂MOx/TiO2(M=Cr、Mn、Fe、Co、Ni、Cu).以乙酸的光催化氧化降解反应为探针,研究了催化剂的光催化性能.研究结果表明,经过渡金属掺杂改性的二氧化钛,光催化性能都有所提高.掺杂量有一个最佳值,在最佳掺杂量时,催化剂光催化性能的提高程度与对应金属氧化物的生成焓有很好的一致性,还发现光催化性能与过渡金属离子稳定氧化态的电子亲和势与离子半径的比值间呈现火山型关系曲线.