A Systematic Evaluation of Polyurethane as a Conformal Coating for the Inhibition of Corrosion on Electronic Components

The corrosion of printed circuit boards can be effectively prevented with a polyurethane conformal coating. In this study, the protective performance of PU coating was investigated systematically through electrochemical measurements and simulated exposure/immersion tests. Some fungi tests were also included. All experimental results show that a polyurethane coating effectively inhibits corrosion on printed circuit boards. The optimal thickness of the coating film should be about 60 μm. Long-term exposure tests showed that this coating material could preserve the reliability of the investigated printed circuit boards for more than 400 days in a 90% relative humidity environment at 25°C.     

非晶态镍磷—镍钨磷双层组合镀层的耐蚀性能研究

本文对比研究了镍磷镀层、镍钨磷镀层及非晶态镍磷和镍钨磷双层组合镀层的耐蚀性能，分别进行了各种镀层的浸渍腐蚀实验，镀层的Ｘ射线衍射图象、镀层的扫描电镜图象、以及在工厂实际的腐蚀环境里进行的腐蚀实验。实验结果表明镍磷及镍钨磷双层组合镀层的耐 性优于镍磷镀层、镍钨磷镀层的耐蚀性。     

2A12-T6铝合金表面双-(γ-三乙氧基硅丙基)四硫化物薄膜的特性

采用傅立叶变换红外光谱分析了2A12-T6铝合金表面自组装双-(!-三乙氧基硅丙基)四硫化物硅烷偶联剂(SCA)薄膜结构特征,并采用电化学极化曲线评价了薄膜的耐蚀性能.结果表明,铝材表面自然晾干,SCA薄膜分子之间主要通过氢键连接,腐蚀电流密度减小1个数量级以上.120℃的加热处理促进铝板表面通过SiOSi链接而形成SCA网状薄膜结构,并通过在界面上形成SiOAl界面相结构而与铝板表面牢固连接,腐蚀电流密度降低2个数量级以上.SCA乙醇溶液浸泡处理10min比浸泡2s～1min的铝板表面SCA薄膜内氢键缔合羟基要多.     

Alkylsulfamoyl Chlorides as Key Units in the Synthesis of Novel Biologically Active Compounds for Crop Protection

Due to their bifunctional character, alkylsulfamoyl chlorides are versatile units for the synthesis of heterocycles, polar sulfamates, and sulfonamides. In the last decade, synthetic methods of general preparative use have been developed, by means of which amine hydrochlorides, isocyanates, aziridines or tertiary alcohols can be reacted with suitable sulfuric acid derivatives to give novel, variously substituted alkylsulfamoyl chlorides. These compounds can subsequently be converted either to previously unobtainable N-alkoxyalkyl-N-alkylsulfamoyl chlorides or to novel heterocycles of the type 1H-2,1,3-benzothiadiazin-4-one-2,2-dioxide, 2H-1,2,6-thiadia-zin-3-one-1,1-dioxide and 2H-1,2,4,6-thiatriazin-5-one-1,1-dioxide; these compounds are examples of interesting models which illustrate the relation between the structure and the action of the compound, and in some cases lead to highly selective, ecologically unobjectionable herbicides. On the other hand, the alkylsulfamoyl chlorides themselves can be N-acylated to give further 3- to 5-atom bifunctional synthesis units, with which novel heterocyclic syntheses can be carried out. Further uses of the alkylsulfamoyl chlorides include the preparation of biologically active sulfamates, and cycloaddition reactions of N-sulfonylamines prepared in situ.     

Synthesis and characterization of sol–gel derived glass-ceramic and its corrosion protection on 316L SS

Glass-ceramic was prepared by sol–gel method using Ca(NO₃)₂·4H₂O and P₂O₅ as Ca and P precursors, respectively. In order to improve the bioactivity of the implant material, glass-ceramic (β-Ca₂P₂O₇) coating was developed on 316L SS substrate by spin coating method. Coating was annealed at different temperatures and its corrosion resistance was evaluated by electrochemical polarization and impedance analysis using Ringer’s solution as electrolyte. The results from the present study, show excellent corrosion resistance for coated 316L SS, corroborated by the high values of charge transfer resistance from impedance analysis and higher breakdown and repassivation potential with the corresponding lower current density from polarization measurements. Based on the results, the glass-ceramic coating on 316L SS can be considered as a corrosion resistant material.     

Sol-gel ZrO2 coatings for chemical protection of stainless steel

ZrO₂ coatings deposited on 316 L stainless steel sheets were synthesized by sol-gel method using Zr(OC₃H₇)₄ as precursor and isopropanol, glacial acetic acid, and water as solvents for application with ultrasounds. Different solutions for dip-coating were prepared with compositions varying between 0.025 and 0.9 mol/dm³ of ZrO₂. X-ray diffraction shows that the films densified at 800°C are crystalline with a tetragonal structure. The thickness of the coatings varied from 0.35–0.75 m. The influence of the ZrO₂ coatings on the corrosion behavior of stainless steel substrates in aqueous NaCl was studied through potentiodynamic polarization curves at 1 mV/s. The values of the electrochemical parameters allow for an explanation of the role of the films in the increased resistance of steel against corrosion in moderately aggressive environments.     

Assessment of corrosion resistance of surface-coated galvanized steel by analysis of the AC impedance spectra measured on the salt-spray-tested specimen

In the present work, corrosion resistance of surface-coated galvanized steel was quantitatively determined by an analysis of the alternating current (AC) impedance spectra measured on the salt-spray-tested specimen. To evaluate the corrosion resistance of the surface-coated galvanized steel, AC impedance spectroscopy was performed on the salt-spray-tested specimen previously exposed to salt-sprayed corrosive environment. From the analysis of the impedance spectra, the area fraction transient of white rust θ ₂(t) was theoretically derived from the equivalent circuit equation by using two fitting parameters. The values of the two fitting parameters were determined by fitting the empirical transient equations to the area fraction of the resin coating layer and to the total resistance obtained from the impedance spectra measured, respectively. From the analyses of θ ₂(t) for four kinds of surface-coated galvanized steels with various resin coating layers, it is indicated that as the values of the two fitting parameters decrease in the order of CP, GI, OD and OM (commercial trade names) specimens, the corrosion resistance increases in that order as well. Furthermore, from the quantitative comparison of the two fitting parameters with the polarization resistance of the upper resin coating layer R _p determined from the potentiodynamic polarization curve, it is suggested that the two fitting parameters decrease in value as well with increasing R _p.     

Protective properties of redox polymer film deposited on stainless steel

We propose a novel composite organic-inorganic coating in the form of a redox polymer film for protection of stainless steel against general corrosion in strong acid medium (2 M H₂SO₄). We utilize an anion exchange polymer, protonated poly(4-vinylpyridine), into which hexacyanoferrate anions have been introduced. Owing to the presence of Fe(CN)₆^3–/4– at the interface formed by the film and the steel, a sparingly soluble metal hexacyanoferrate (mostly Prussian blue, PB) is formed as an overcoating on the steels surface, presumably on the passive (metal oxide) layer. The redox polymer film on the steel seems to act as a composite three-dimensional bilayer-type coating in which hexacyanoferrate(III,II) anions (that are capable of effective charge storage) exist in the outer portions of the film, whereas the inner PB layer improves the systems overall adherence and stability. By analogy to a conducting polymer (e.g. polyaniline, polypyrrole), introduction of the redox polymer composite film leads to stabilization of the steel substrates potential within the passive range.Contribution to the 3rd Baltic Conference on Electrochemistry, Gdansk-Sobieszewo, Poland, 23–26 April 2003Dedicated to the memory of Harry B. Mark, Jr. (28 February 1934–3 March 2003)     

铁掺杂TiO2纳米管阵列对不锈钢的光生阴极保护

在含FeSO4的HF、H2SO4/HF、NaF/Na2SO4溶液中,通过电化学阳极氧化直接在纯钛表面制备Fe 掺杂的TiO2(Fe-TiO2)纳米管阵列. 应用X射线衍射(XRD)、扫描电子显微镜(SEM)、紫外-可见吸收光谱(UV-Vis)、X 射线光电子能谱(XPS)等手段对纳米管阵列的结构、形貌及化学组成进行表征. 利用光电化学测量研究Fe-TiO2纳米管阵列在不同波长范围内的光电响应特性和光生阴极保护行为. 考察了温度、时间、掺杂含量等参数对TiO2纳米管阵列的几何尺寸、形貌和光电性能的影响. 结果表明, Fe掺杂可有效减缓TiO2纳米管阵列载流子的复合, 窄化TiO2带隙宽度, Fe-TiO2在410-650 nm范围显示强吸收, 并使光谱响应扩展到波长大于400 nm 的可见光区. 实验结果还表明, Fe-TiO2纳米管阵列对316不锈钢(316L)具有良好的光生阴极保护作用, 暗态下阴极保护作用可继续维持.     

Analysis and Protection of One Thousand Hand Buddha in Dazu Stone Sculptures

The components of the rock, the pigments, the gold foils and the adhesive of One Thousand Hand Buddha in Dazu stone sculptures, Chongqing, China, have been analyzed by X-ray diffraction (XRD), X-ray fluorescence (XRF), infrared spectroscopy (IR), energy dispersive X-ray analysis (EDX) and fiber optics reflectance spectroscopy (FORS). Furthermore, the weathering and degeneration of One Thousand Hand Buddha have been discussed and the protective methods have been provided. In this work some useful information to study on conservation of stone relics is given.