用热聚法固定指示剂的光纤氧气传感器研究

采用热聚法将甲叉双丙烯酰胺（MBBA）聚合并共价交联在硅烷化的玻璃微珠上 ，同时将指示剂Ru（Ⅱ）-邻啡咯啉配合物物理包埋于聚合物中，研制了一种基于 荧光猝灭原理的光纤氧气传感器，采用NaHSO_3-O_2-MnSO_4体系引发MBBA水溶液热 聚合后应，通过确定NaHSO_3,MnSO_4,MBBA和Ru(phen)_3Cl_2的最佳反应浓度以及 玻璃微珠的尺寸，优化了聚合反应条件，改善了指示剂的固定效果，制备了性能较 好的传感器探头，该传感器的检测下限为5×10~(-6)(V/V)，响应时间为10s该传感 器连续工作50min,重复性标准偏差为±1%。     

Extended applications of electric cell-substrate impedance sensing for assessment of the structure-function of α2β1 integrin

Electric cell-substrate impedance sensing (ECIS) was applied to assess the structure-function of α2β1 integrin, receptor for collagen and laminin. On collagen-coated gold electrodes, expression of this integrin on human rhabdomyosarcoma (RD) cells (RDX2C2) yielded a five-fold increase in resistance when compared with mock transfected RD (RDpF) cells (34.5±5.2 versus 6.5±0.8 Ω/cell). An intermediate level of 16±2 Ω/cell was measured upon expression of an α2β1 mutant that lacked the α2 cytoplasmic domain (RDX2CO). On laminin, the resistance measured for RDX2C2 cells was also higher but only twice that of RDpF cells at 71±4 and 37±4 Ω/cell, respectively. In comparison, RDX2CO cells (38±4 Ω/cell), exhibiting no enhanced adhesive function, yielded a similar result to that of RDpF cells. On fibronectin, RDX2C2 and RDpF cells, exhibiting comparable levels of adhesion, were similar in resistance measurements at 85±5and 89±7 Ω/cell, respectively. It has been shown that deletion of α2 cytoplasmic domain results in dysregulated recruitment of the α2β1 mutant to focal adhesion complexes that mediate binding of fibronectin. RDX2CO cells on fibronectin, exhibiting reduced adhesive function, was associated with noticeably lower resistance (60±4 Ω/cell). Monitoring electroporation of the RD plasma membrane also indirectly validated cell attachment as reflected by the resistance measured. Results from this study demonstrated the potential of ECIS for study of the structure-function of βl integrin adhesion receptors.     

Glass capillary gas chromatography of amino acid enantiomers

Glass capillaries coated with Chirasil-Val, a chirally functionalised polysiloxane, are capable in principle of resolving all protein amino-acid enantiomers in a single run and within a short analysis time, thus allowing for example the quantitative amino acid determination by enantiomer labelling. The elution characteristics of the individual amino acids however are also dependent upon the chemical nature of the capillary wall surface, and a surface pretreatment is found to be necessary if all protein amino acids are to be analysed. Of the various methods of pretreatment tested, etching of borosilicate glass with gaseous HCl followed by deposition of colloidal silicic acid is considered to be the most suitable.     

Influence of mechanical properties of pectin films on charge density and charge density distribution in pectin macromolecule

The hydration and mechanical properties of citrus pectin films were examined in conditions relevant to those in the plant cell wall. The pectins used for this study varied in the degree of esterification (DE) (high or low) and charge distribution on the backbone (random or block). The hydration of the films was controlled in an osmotic pressure experiment using polyethylene glycol solutions (PEG 20000). Hysteresis tests at constant deformation rate (stress vs deformation) were used for investigating the mechanical behaviour of films. Mechanical and hydration properties of pectin films were examined as a function of charge density, charge density distribution and counterion environment—K⁺, Ca²⁺, Mg²⁺. Swelling decreased with increasing counterion concentration. The effect is stronger in the case of Ca²⁺ and Mg²⁺ for low esterified pectins and therefore crosslinks from divalent ions could be assumed. The crosslink effect is confirmed in mechanical experiments where an increase in the film tensile modulus is observed with increasing counterion concentration. It is shown for the first time that in case of highly concentrated pectin solutions Mg²⁺ cations also act as a crosslinker for pectin macromolecules.     

Morphology and electric conductivity of cross-linked polyethylene–carbon black blends prepared by gelation/ crystallization from solutions

 Ultra-high-molecular-weight polyethylene (UHMWPE) – carbon black (CB) blends were prepared by gelation/ crystallization from PE dilute solutions containing CB particles. The UHMWPE/CB composition chosen were 1/0.15, 1/0.25, 1/0.5, 1/0.75, 1/1, 1/3, 1/5, and 1/9, etc. The cross-linking of PE chains was performed by chemical reaction of dicumyl-peroxide at 160 ^°C. X-ray diffraction patterns indicate that the crystallinity of PE within the blends decreased drastically through the chemical reaction at high temperature. The sample preparation method by gelation/crystallization provided the UHMWPE–CB system with various CB contents up to 90% and the conductivities for the resultant specimens were in the range from 10^-9 to 1 Ω^-1 cm^-1 corresponding to the electric conductivity range of semiconductors. The blends assured thermal stability of electric conductivity by cross-linking of PE chains, although the mechanical property such as the storage and loss moduli were very sensitive to temperature. The conductivity of the blends with CB content ≥20% were almost independent of temperature up to 220 ^°C and the values in the heating and cooling processes were almost the same. On the other hand, for the UHMWPE–CB blends with 13% CB content corresponding to the critical one, temperature dependence of electric resistivity showed positive temperature coefficient (PTC) effect. The PTC intensities for non-cross-linked and cross-linked materials were lower than that of the corresponding low-molecular-weight-polyethylene (LMWPE)–CB blend but the maximum peak appeared at 160 ^°C which is higher than the peak temperature of LMWPE–CB blend. Received: 10 December 1997 Accepted: 9 April 1998     

MoS2纳米管包覆单壁碳纳米管束的制备

MoS₂ nanotube coated SWNT (Single wall carbon nanotube) bundles have been successfully prepared by adsorbing (NH₄)₂MoS₄ onto SWNT bundles and subsequent heat treatment under H₂ at 900 ℃ in a tube furnace. The morphologies, structure and composition of the as-prepared sample were investigated by XRD, SEM, HRTEM coupled with EDS. The formation mechanism has also been preliminarily discussed.     

Sensitive Voltammetric Response of p‐Nitroaniline on Single‐Wall Carbon Nanotube‐Ionic Liquid Gel Modified Glassy Carbon Electrodes

An ionic liquid (i.e., 1‐butyl‐3‐methylimidazolium hexafluorophosphate, BMIMPF₆)‐single‐walled carbon nanotube (SWNT) gel modified glassy carbon electrode (BMIMPF₆‐SWNT/GCE) is fabricated. At it the voltammetric behavior and determination of p‐nitroaniline (PNA) is explored. PNA can exhibit a sensitive cathodic peak at ?0.70 V (vs. SCE) in pH 7.0 phosphate buffer solution on the electrode, resulting from the irreversible reduction of PNA. Under the optimized conditions, the peak current is linear to PNA concentration over the range of 1.0×10^?8–7.0×10^?6 M, and the detection limit is 8.0×10^?9 M. The electrode can be regenerated by successive potential scan in a blank solution for about 5 times and exhibits good reproducibility. Meanwhile, the feasibility to determine other nitroaromatic compounds (NACs) with the modified electrode is also tested. It is found that the NACs studied (i.e., p‐nitroaniline, p‐nitrophenol, o‐nitrophenol, m‐nitrophenol, p‐nitrobenzoic acid, and nitrobenzene) can all cause sensitive cathodic peaks under the conditions, but their peak potentials and peak currents are different to some extent. Their peak currents and concentrations show linear relationships in concentration ranges with about 3 orders of magnitude. The detection limits are 8.0×10^?9 M for p‐nitroaniline, 2.0×10^?9 M for p‐nitrophenol, 5.0×10^?9 M for o‐nitrophenol, 5.0×10^?9 M for m‐nitrophenol, 2.0×10^?8 M for p‐nitrobenzoic acid and 8.0×10^?9 M for nitrobenzene respectively. The BMIMPF₆‐SWNT/GCE is applied to the determination of NACs in lake water.     

Swelling behavior of ionically cross-linked polyampholytic hydrogels in varied salt solutions

Ionically cross-linked polyampholytic hydrogels were synthesized by redox copolymerization of acrylamide and an ionic complex of (N,N-diethylamino)ethyl methacrylate and acrylic acid (designated as PADA hydrogel). The swelling behavior of the hydrogels in water indicated that a minimal equilibrium swelling ratio is found when the molar ratio of anionic/cationic monomers was 1.55. In NaCl solution, the hydrogels exhibited the typical swelling behavior of conventional polyampholytic gels. Their equilibrium swelling ratios increased with an increase in the NaCl concentration. In solutions of multivalent ions (CaCl₂ and trisodium citrate solutions), the equilibrium swelling ratios of the hydrogels increased first and were then followed by a decrease with an increase in salt concentration. Interestingly, an unexpected abrupt swelling phenomenon was observed when the fully swollen hydrogels in salt solution were transmitted to pure water. The unique swelling behavior of PADA hydrogels depends not only on the molar ratio of the anionic/cationic monomers but also on the valency of the ions.     

The photosensitizing effect of the photoproduct of protoporphyrin IX

The photodynamic effect of a photoproduct of protoporphyrin IX (PpIX) induced by 5-aminolevulinic acid (ALA) was investigated in WiDr cells, a human adenocarcinoma cell line. The fluorescence excitation and emission spectra of PpIX and the photoproduct were measured. After 1, 3 or 5 min exposure of the ALA-incubated cells to 140 mW/cm² light at 635 nm, the photoproduct — the chlorin photoprotoporphyrin (Ppp), had an emission band around 670 nm. The Ppp excitation peak at 670 nm is well separated from the PpIX peak at 635 nm. The outcome of photodynamic therapy (PDT) was determined by measuring intracellular fluorescence intensity of propidium iodide (PI) 2 h following PDT and methylene blue (MB) staining 24 h following PDT. A significant increase in the fluorescence intensity of PI was noted when the ALA-loaded cells were exposed to 670 nm light after exposure to 635 nm, indicating enhanced cell membrane inactivation induced by the photodynamic action of the photoproduct. However, the fraction of the cells that survived following the same treatment as measured by MB staining was not significantly affected based on an analysis of variance. The fluorescence of PpIX decayed significantly during 635 nm light exposure. Exposure to light at 670 nm does not lead to any photodegradation of PpIX. The fluorescence of Ppp was bleached during 670 nm light exposure. Exposure of Ppp at 670 nm gives no PpIX back. Thus, the phototransformation of PpIX to Ppp is probably not a reversible process.     

单壁碳纳米管的结构修饰

由于单壁碳纳米管具有独特的结构、电学及机械等性能，可望在许多新领域得 到应用，已引起广泛的关注。但由于单壁碳纳米管不溶于水和常见的有机溶剂，极 大地制约了其应用性能的研究。随着单壁碳纳米管制备技术的不断完善，其研究方 向已开始转向结构修饰及应用性能的研究。主要介绍近年来单壁碳纳米管结构修饰 方面的最新发展状况，重点讨论化学功能化及物理吸附。