Preparation and characterization of acrylic‐based black particles of poly(methyl methacrylate‐co‐ethylene glycol dimethacrylate) by dispersion polymerization for electrophoretic displays

Ultrafine black particles, ranging in diameter from 1 to 3 μm, were prepared by dispersion polymerization in a methanol/water mixture with vinyl monomers, nonpolymerizable Sudan black B dyes, and fluorescein isothiocyanate labeled charge control additives. Both the ratio of the methanol to the water dispersion medium and the polymeric stabilizer concentration had significant effects on the particle size. The important role of the stabilizer concentration lay in the particle formation step, during which it determined the particle stability and final particle size. These could affect the extent of the aggregation of nuclei by changing the adsorption rate of the stabilizer and the viscosity of the dispersion medium, resulting in smaller particles. The fluorescent‐labeled charge control additives strongly affected the electrophoretic mobility. A small concentration of fluorescent‐labeled charge control additives increased the electrophoretic mobility. However, a further addition reduced the electrophoretic mobility of the polymer particles. The concentration dependence of the fluorescent‐labeled charge control additives on the deposition behavior in the polymer particles was successfully imaged and thereafter quantified by image analysis. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 5608–5616, 2004     

Multicyclic polyethers derived from 1,1,1‐tris(4‐hydroxyphenyl)ethane and 2,6‐dihalopyridines

Poly(pyridine ether)s were prepared in two ways: the polycondensation of silylated 1,1,1‐tris(4‐hydroxyphenyl)ethane (THPE) with 2,6‐difluoropyridine (method A) and the polycondensation of free THPE with 2,6‐dichloropyridine (method B). With method A, the THPE/difluoropyridine feed ratio was varied from 1.0:1.0 to 1.0:1.6. Cycles, bicycles, and multicycles were the main reaction products, and crosslinking was never observed. When ideal stoichiometry was used exclusively, multicycles free of functional groups were obtained. These multicycles were detectable in matrix‐assisted laser desorption/ionization time‐of‐flight (MALDI‐TOF) mass spectra up to B₃₈C₇₆ with a mass of approximately 32,000 Da. With method B, the reaction conditions were varied at a fixed feed ratio to achieve an optimum for the preparation of multicyclic polyethers, but because of the lower reactivity of 2,6‐dichloropyridine, a quantitative conversion was not achieved. The reaction products were characterized with MALDI‐TOF mass spectrometry, viscosity measurements, and size exclusion chromatography. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 5725–5735, 2004     

Hollow latex particles as submicrometer reactors for polymerization in confined geometries

A method was developed for free‐radical polymerization in the confines of a hollow latex particle. Hollow particles were prepared via the dynamic swelling method from polystyrene seed and divinylbenzene and had hollows of 500–1000 nm. So that these hollow poly(divinylbenzene) particles could function as submicrometer reactors, the particles were filled with a monomer (N‐isopropylacrylamide) via the dispersion of the dried particles in the molten monomer. The monomer that was not contained in the hollows was removed by washing and gentle abrasion. Free‐radical polymerization was then initiated by γ radiolysis in the solid state. Transmission electron microscopy showed that poly(N‐isopropylacrylamide) formed in the hollow interior of the particles, which functioned as submicrometer reactors. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 5706–5713, 2004     

Synthesis and characterization of well‐defined diblock and triblock copolymers of poly(N‐isopropylacrylamide) and poly(ethylene oxide)

Well‐defined diblock and triblock copolymers composed of poly(N‐isopropylacrylamide) (PNIPAM) and poly(ethylene oxide) (PEO) were successfully synthesized through the reversible addition–fragmentation chain transfer polymerization of N‐isopropylacrylamide (NIPAM) with PEO capped with one or two dithiobenzoyl groups as a macrotransfer agent. ¹H NMR, Fourier transform infrared, and gel permeation chromatography instruments were used to characterize the block copolymers obtained. The results showed that the diblock and triblock copolymers had well‐defined structures and narrow molecular weight distributions (weight‐average molecular weight/number‐average molecular weight < 1.2), and the molecular weight of the PNIPAM block in the diblock and triblock copolymers could be controlled by the initial molar ratio of NIPAM to dithiobenzoate‐terminated PEO and the NIPAM conversion. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 4873–4881, 2004     

Structure and properties of the mesophase of syndiotactic polystyrene. VIII. Solvent sorption behavior of syndiotactic polystyrene/p‐chlorotoluene mesophase membranes

A crystalline δ form of a syndiotactic polystyrene (sPS) membrane was prepared from a solution of sPS (1 wt %) and p‐chlorotoluene (p‐CT) by a solution‐casting method. The mesophase (δ empty form) of sPS was obtained by the extraction of the guest solvent from the δ form of sPS by a stepwise solvent‐extraction method. The sPS/p‐CT mesophase membrane [p‐CT (A‐M)] was used for the sorption of 1 mol % p‐CT for different times and for the sorption of different concentrations of p‐CT, chlorobenzene (CB), p‐xylene (p‐X), toluene, and chloroform for 48 h. The presence of solvents in the sPS membrane was confirmed by IR analysis. A thermal study revealed that the sorption amount of 1 mol % p‐CT increased with increasing immersion time, and the sorption amounts of different solvents increased with increasing solvent concentration. Differential scanning calorimetry results showed that the desorption peak temperature increased as the amount of the solvent increased in the clathrated sPS membrane. Wide‐angle X‐ray diffraction results showed that 2θ at 8.25° was slightly shifted toward 8°, and there was no change in the peak position at 10° for p‐CT (A‐M), which was immersed in different solvents (1 mol %); however, the intensity of 2θ at 10° was not similar for all the samples. Among the solvents used for the sorption studies at 1 mol %, p‐CT (A‐M) could sorb more p‐CT and CB than p‐X, toluene, and chloroform. The solvent sorption isotherm was the Langmuir sorption mechanism. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 3439–3446, 2004     

Pressure and temperature dependence of the gas‐transport properties of dense poly[2,6‐toluene‐2,2‐bis(3,4‐dicarboxylphenyl)hexafluoropropane diimide] membranes

The gas‐transport properties of poly[2,6‐toluene‐2,2‐bis(3,4‐dicarboxylphenyl)hexafluoropropane diimide] (6FDA‐2,6‐DAT) have been investigated. The sorption behavior of dense 6FDA‐2,6‐DAT membranes is well described by the dual‐mode sorption model and has certain relationships with the critical temperatures of the penetrants. The solubility coefficient decreases with an increase in either the pressure or temperature. The temperature dependence of the diffusivity coefficient increases with an increase in the penetrant size, as the order of the activation energy for the diffusion jump is CH₄ > N₂ > O₂ > CO₂. Also, the average diffusion coefficient increases with increasing pressure for all the gases tested. As a combined contribution from sorption and diffusion, permeability decreases with increases in the pressure and the kinetic diameter of the penetrant molecules. Even up to 32.7 atm, no plasticization phenomenon can be observed on flat dense 6FDA‐2,6‐DAT membranes from their permeability–pressure curves. However, just as for other gases, the absolute value of the heat of sorption of CO₂ decreases with increasing pressure at a low‐pressure range, but the trend changes when the feed pressure is greater than 10 atm. This implies that CO₂‐induced plasticization may occur and reduce the positive enthalpy required to create a site into which a penetrant can be sorbed. Therefore, a better diagnosis of the inherent threshold pressure for the plasticization of a glassy polymer membrane may involve examining the absolute value of the heat of sorption as a function of pressure and identifying the turning point at which the gradient of the absolute value of the heat of sorption against pressure turns from a negative value to a positive one. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 354–364, 2004     

Photodegradation of a herbicide derivative, 2,4-dichlorophenoxy acetic acid in aqueous suspensions of titanium dioxide

The photocatalytic degradation of a herbicide derivative, 2,4-dichlorophenoxy acetic acid (2,4-D, 1), has been investigated in aqueous suspensions of titanium dioxide. The degradation was studied by monitoring the change in substrate concentration employing UV spectroscopic analysis and decrease in Total Organic Carbon (TOC) content as a function of irradiation time in the presence of UV light source. The degradation kinetics was investigated under a variety of conditions, such as different types of TiO₂, pH, catalyst and substrate concentrations. Higher photonic efficiencies were observed with Degussa P25 as compared with other photocatalysts. The degradation products were analysed by GC-MS and probable pathways for the formation of different products were proposed.     

RuH2和RuN2电子组态与光谱性质的从头计算

用量子化学从头算方法在B3LYP/6 311G 的水平上 ,研究了RuH2 和RuN2 可能的电子组态和光谱性质 .结果表明 ,RuH2 的3 B2 和5Σ-态对应于静电作用的物理吸附态 .RuN2 的一重态和三重态的计算结果跟钌单晶面上的实验值相接近 .而RuN2 在C∞v对称性时 ,五重态5Σ-的计算频率比实验值稍低 .在C2v对称性时 ,五重态的计算频率值则更低 ,3 B2 和5A1态不能稳定存在     

(Nd_(1-x)Er_x)_2Co_(15.5)V_(1.5)的结构转变与磁性

利用电弧熔炼制备了 (Nd1 xErx) 2 Co1 5 5V1 5(x=0— 1 0 )化合物样品 .通过x射线衍射分析和磁性测量研究了Er替代Nd2 Co1 5 5V1 5中的Nd时对化合物结构和磁性的影响 .研究结果表明 ,低Er含量 (x <0 4 ) ,化合物为Th2 Zn1 7型结构 ;高Er含量时 (x >0 5 ) ,化合物转变为Th2 Ni1 7结构 ;Er含量为x =0 4和 0 5时 ,两种结构共存 .两种结构的晶胞参数a ,c和晶胞体积V随着Er含量的增加都呈现递减的趋势 .随着Er含量的增加 ,(Nd1 xErx) 2 Co1 5 5V1 5化合物的居里温度和饱和磁化强度都单调下降 .(Nd1 xErx) 2 Co1 5 5V1 5化合物的室温各向异性由低Er含量时的易锥型转变为高Er含量时的易轴型 .x =0— 0 5的化合物在温度升高时发生自旋重取向转变 ,自旋重取向温度Tsr随Er含量的增加而减小