Microwave‐assisted synthesis and characterization of biodegradable block copolyesters based on poly(3‐hydroxyalkanoate)s and poly(D,L‐lactide)

Microwave (MW)‐assisted ring‐opening polymerization (ROP) provides a rapid and straightforward method for engineering a wide array of well‐defined poly(3‐hydroxyalkanoate)‐b‐poly(D,L ‐lactide) (PHA‐b‐PLA) diblock copolymers. On MW irradiation, the bulk ROP of D,L ‐lactide (LA) could be efficiently triggered by a series of monohydroxylated PHA‐based macroinitiators previously produced via acid‐catalyzed methanolysis of corresponding native PHAs, thus affording diblock copolyesters with tunable compositions. The dependence of LA polymerization on temperature, macroinitiator structure, irradiation time, and [LA]₀/[PHA]₀ molar ratio was carefully investigated. It turned out that initiator efficiency values close to 1 associated with conversions ranging from 50 to 85% were obtained only after 5 min at 115 °C. A kinetic investigation of the MW‐assisted ROP of LA gave evidence of its “living”/controlled character under the experimental conditions selected. Structural analyses and thermal properties of biodegradable diblock copolyesters were also performed. © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2012     

溶剂去除速度对于溶剂退火薄膜相形貌的影响

以聚苯乙烯-聚4-乙烯基吡啶(PS-b-P4VP)嵌段共聚物作为研究对象,采用DMF作为退火溶剂,以原子力显微镜(AFM)和透射电子显微镜(TEM)为表征手段,研究了溶剂退火后期溶胀薄膜中溶剂的去除速度对于薄膜相形貌的影响,发现通过改变溶剂去除速度可以有效的调控薄膜中的形貌.当薄膜厚度为35 nm时,DMF的快速挥发会导致薄膜中形成以PS为分散相的反转柱状相结构,当降低溶剂的挥发速度时,薄膜中形成了以PS为分散相的环状形貌,当进一步减缓挥发速度时,薄膜中将形成台阶状的片层结构;然而当薄膜厚度为55 nm时,溶剂退火后期薄膜中形成的是以P4VP为分散相的正常柱状相结构,在相同溶剂去除速度条件下薄膜相形貌变化较小.     

Direct synthesis of Poly(Ԑ-Caprolactone)-block-poly (glycidyl methacrylate) copolymer and its usage as a potential nano micelles carrier for hydrophobic drugs

Ring-opening (ROP) and enzymatic copolymerization (ECP) are among the most widely used approaches for synthesizing copolymers of polycaprolactone (PCL). It involves multiple-step reactions and the utilization of enzymes that make the process a lot more complicated, time consuming, and expensive. Atom transfer radical polymerization (ATRP) has been adopted to synthesize a novel amphiphilic copolymer in our study. The study presents a method to eliminate the ROP/ECP multiple steps in monomer polymerization thus making the process simpler and smoother. The synthesis of cationic polymer micelles copolymer of PCL-PGMA (polycaprolactone grafted poly glycidyl methacrylate) was carried out using direct functionalization of hydroxy group in crude PCL to achieve a higher degree of functionalization, i.e., 12.8% for macroinitiator. FTIR and ¹H-NMR confirmed the successful synthesis of the copolymer with better control over the molecular weight with a PDI (1.84). DSC and XRD results showed the reduction of crystallinity by 86.81%, making copolymer more compatible for drug delivery application. The synthesized copolymer was further converted to nano-micelles drug carrier having an average size of 96.08 ± 21.22 nm. The drug encapsulation efficiency achieved was 60.0 ± 1.7%, and nano-micelles rendered a slow and controlled release of naproxen with long-term storage stability.     

Getting to the bottom morphology of block copolymer thin films

We demonstrate a general approach for attaining the bottom morphology of block copolymer(BCP) thin films. In our former measurements on PS-b-PMMA films, surface morphology maps of the BCP films revealed distinct ordering regimes where the cylinders orient predominantly perpendicular or parallel to the interface and an ‘intermediate' regime where these morphologies coexist. However, this earlier work did not explore the bottom morphology of BCP thin films. In this study, we investigated the block copolymer morphology near the solid substrate in the cast block copolymer film having a perpendicular cylinder morphology on the surface.     

Synthesis and enrichment of a macromolecular surface modifier PP-b-PVP for polypropylene

Polypropylene-block-poly(vinylpyrrolidone) copolymer was synthesized through the esterification of dicarboxyl-terminated polypropylene with monohydroxyl-terminated poly(vinylpyrrolidone) and used as a macromolecular surface modifier to improve the surface hydrophilicity of PP. The results of ATR-FTIR and contact angles measurements indicated that PP-b-PVP could diffuse preferably onto the surface by the inducement of high energy interface and lower the water contact angle of polypropylene. Lower loading and lower molecular weight of PP and PVP segment would result in higher surface selective enrichment.     

SALS,WAXS and mechanical properties of heat‐treated thermotropic polymers

The influence of heat treatment on the texture, microstructure and tensile mechanical properties of extruded thin films of a series of high‐performance thermotropic liquid crystal polymers (LCPs) was investigated. LCPs based on random units of hydroxybenzoic acid (B), hydroxynaphthoic acid (N), terephthalic acid (TA) and biphenol (BP) were kindly supplied by the former Hoechst Celanese Corp as 50 µm thick extruded tapes. The LCPs, denoted B‐N, COTBP and RD1000, have B and N as common comonomers and vary the other comonomers. Thus, this study also enables the investigation of the influence of monomer composition on microstructure and mechanical properties. Heat treatments were carried out at temperatures close to the solid‐to‐nematic transition (T_s→n) for periods up to 5 h, under dry air conditions. The thermal treatment produced either two endotherms or a small increase of T_s→n (B‐N and RD1000), or increased significantly T_s→n (COTBP). Moreover, when heat treatment was carried out approximately 40°C below the respective T_s→n, the mechanical Young's modulus, E, along the extrusion axis, increased for all LCPs. Strikingly, for COTBP, E increased over 100% relative to the as‐extruded film. The results also showed that the optimum treatment time for improving the Young modulus, under dry air atmosphere, was between 3 and 4 h. Wide‐angle X‐ray scattering showed a significant sharpening of crystalline reflections and concentration of the 002 meridional reflection as a result of thermal treatment, suggesting the elimination of defects and a better alignment of the molecular chains along the extrusion axis. This would explain the increase in tensile modulus. Copyright © 2013 John Wiley & Sons, Ltd.     

STRUCTURAL CHARACTERIZATION OF POLY(ϵ-CAPROLACTONE) AND POLY(ϵ-CAPROLACTONE-b-ISOBUTYLENE-b-ϵ-CAPROLACTONE) BLOCK COPOLYMERS BY MALDI-TOF MASS SPECTROMETRY

Poly(?-caprolactone)(PC1) and PC1-polyisobutylene-PC1 (PC1-PIB-PC1) block copolymers were synthesized in anhydrous toluene by in situ conversion of 2-methyl-1-propanol (2M1P) and α,ω-dihydroxy PIB, respectively, to the corresponding aluminum alkoxide by reaction with a stoichiometric amount of triethylaluminum (TEA) followed by the addition of e-caprolactone. Structural characterization of 2M1P-initiated PCl by gel permeation chromatography (GPC) and matrix-assisted laser desorption ionization–time of flight (MALDI-TOF) mass spectrometry (MS) demonstrated the presence of cyclic oligomers, which are produced by intramolecular transesterification reactions that become significant at high monomer conversions. A minor fraction of chains bearing carboxylic acid termini was also observed in the MALDI-TOF mass spectrum; however, carboxylic acid chain ends could not be detected by ¹³C NMR analysis. Thus, the likely origin of the carboxylic acid termini is fragmentation of the initiator residue from the chain end during MALDI-TOF analysis. For PCl-PIB-PCl block copolymers, two different α,ω-telechelic PIB diols were used as macroinitiators, one derived from allyl and one from isopropenyl terminated PIB. Terminal olefins were converted to primary alcohols via regioselective hydroboration followed by alkaline hydrogen peroxide oxidation. After reaction with ?-caprolactone, formation of a block copolymer was evidenced by a shift of the polymer peak to lower elution volume in GPC analysis. Block copolymers possessed molecular weight distributions ≤1.4, and molecular weights of the PCl blocks calculated from GPC were in excellent agreement with those found using MALDI-TOF MS. Structural analysis indicated that the PCl end blocks were severed from the crude block copolymer during MS analysis, for both allyl- and isopropenyl-derived materials. For allyl-derived materials the PCl blocks were found to predominantly carry a C₂ residue at the point of detachment of the PIB block; however, the isopropenyl-derived block copolymers showed a complex mixture of different residues suggesting a complex fragmentation mechanism during loss of the PIB block.     

Further Studies on the Anionic Copolymerization of Styrene and Glycidyl Methacrylate in Toluene

Sequential anionic copolymerization of styrene and glycidyl methacrylate (GMA) was performed with the protection of argon under normal pressure, where styrene, GMA, toluene, THF, n-butyllithium and a small amount of lithium chloride (LiCl) were used as first monomer, second monomer, solvent, polar reagent, initiator and additive, respectively. Polystyrene-b-poly(glycidyl methacrylate) diblock copolymers (PS-b-PGMA) with well-defined structure and narrow molecular weight distribution were prepared by the copolymerization reaction of poly(styryl)lithium with GMA under certain temperatures. The copolymers were characterized using gel permeation chromatography (GPC), ¹H-NMR, ¹³C-NMR, thin layer chromatography (TLC) and hydrochloric acid-dioxane argentimetric methods. The effects of additives, copolymerization temperature and THF dosage on the copolymerization were studied. No chain transfer reaction of anionic polymerization of styrene in toluene was observed. Slightly broader molecular weight distribution of PS-b-PGMA was observed with the increase the GMA repeat units. Using THF/toluene blend solvent could reduce the polydispersity index (M _w /M _n ) and dissolve the copolymer better than toluene alone. Lower temperature (< -40°C) and LiCl are required to prepare PS-b-PGMA with narrower molecular weight distribution.