Crystallization and melting behaviors of polystyrene-b-poly(ethylene-co-butene) block copolymers

Non-isothermal and isothermal crystallization behaviors of polystyrene-b-poly(ethylene-co-butene) (PSt-b-PEB) block copolymers with different compositions and chain lengths were investigated by differential scanning calorimetry (DSC). The results show that crystallization of PEB block is strongly dependent on the composition. Crystallization temperature (T_c), melting temperature (T_m) and fusion enthalpy (ΔH_f) increase rapidly with PEB volume fraction (V_E) for block copolymers with V_E below 50%, but there is little change when PEB block becomes the major component. Glass transition temperature (T_g) of the PSt block and order-disorder transition temperature (T_ODT) of block copolymers also have a weak effect. The isothermal crystallization kinetics results show that Avrami exponent (n) was strongly dependent on the composition and crystallization temperature. For the block copolymers with V_E below 38.7 vol%, the values of n vary between 0.9 and 1.3, indicating that crystallization is confined. For the PSt-b-PEB block copolymers with V_E higher than 50%, fractionated crystallization behavior is usually observed. A two-step isothermal crystallization procedure is applied to these block copolymers. It is found that breakout crystallization occurs at higher T_c, but confined at lower T_c. Two overlapped melting peaks are observed for the block copolymers with fractionated crystallization behavior after two-step crystallization, and only the higher melting peak corresponding to breakout crystallization can be used to derive equilibrium melting temperature.     

不同嵌段比的PEG-b-PDMAEMA共聚物在水溶液中的自聚集行为

采用氢核磁共振(¹H-NMR)、动态光散射(DLS)及透射电子显微镜(TEM)对聚乙二醇-嵌段-聚甲基丙烯酸N,N-二甲氨基乙酯(PEG-b-PDMAEMA)三种具有不同PEG/PDMAEMA嵌段比的PEG-b-PDMAEMA共聚物在水溶液中的自聚集行为进行了研究. 研究表明, 两嵌段比例是影响聚合物胶束化过程的关键因素: 只有当其中聚乙二醇含量较低(质量分数低于33%)时, 聚合物才具有其pH/温度敏感胶束化特性. 此外, 共聚物溶液随温度胶束化过程与共聚物嵌段比大小密切相关. PEG-b-PDMAEMA这种不同于传统双亲性嵌段共聚物(DHBCs)在选择性溶剂中独特的胶束化行为, 是由聚合物溶液体系中各种基团之间的氢键作用决定的.     

Surface patterns of block copolymers in thin layers after vapor treatment

A systematic study of formation of surface patterns in block copolymer thin layers after their exposure to solvent vapors was performed. The studied effect involves layers of thickness approximately equal to the ordering size of polymers - about 45 nm. Experiments were performed on three styrene - methacrylate derivative block copolymers, synthesized by living anionic polymerization: poly(4-octylstyrene)-block-poly(butyl methacrylate), poly(4-fluorostyrene)-block-poly(butyl methacrylate) and poly(p-octylstyrene)-block-poly(methyl methacrylate). The polymers were exposed to vapors of chloroform, 1,4-dioxane, hexane, acetone and tetrahydrofuran.     

Surface structure of thin asymmetric PS-b-PMMA diblock copolymers investigated by atomic force microscopy

Asymmetric poly(styrene-b-methyl methacrylate) (PS-b-PMMA) diblock copolymers of molecular weight M_n = 29,700 g mol⁻¹ (M_PS = 9300 g mol⁻¹M_PMMA = 20,100 g mol⁻¹, PD = 1.15, χ_PS = 0.323, χ_PMMA = 0.677) and M_n = 63,900 g mol⁻¹ (M_PS = 50,500 g mol⁻¹, M_PMMA = 13,400 g mol⁻¹, PD = 1.18, χ_PS = 0.790, χ_PMMA = 0.210) were prepared via reversible addition-fragmentation chain transfer (RAFT) polymerization. Atomic force microscopy (AFM) was used to investigate the surface structure of thin films, prepared by spin-coating the diblock copolymers on a silicon substrate. We show that the nanostructure of the diblock copolymer depends on the molecular weight and volume fraction of the diblock copolymers. We observed a perpendicular lamellar structure for the high molar mass sample and a hexagonal-packed cylindrical patterning for the lower molar mass one. Small-angle X-ray scattering investigation of these samples without annealing did not reveal any ordered structure. Annealing of PS-b-PMMA samples at 160 °C for 24 h led to a change in surface structure.     

Novel random poly(propylene isophthalate/adipate) copolyesters: Synthesis and characterization

Poly(propylene adipate) (PPA) and poly(propylene isophthalate/adipate) (PPI-PPA) random copolymers of various compositions were synthesized in bulk and characterized in terms of chemical structure and molecular weight. Furthermore, the thermal behavior was examined by thermogravimetric analysis and differential scanning calorimetry. All the polymers showed a good thermal stability. At room temperature they appeared as semicrystalline materials, except the copolymers containing 20 and 30 mol% of PI units: the main effect of copolymerization was a lowering in the amount of crystallinity and a decrease of melting temperature with respect to homopolymers. The crystalline phase of PPI and PPA was evidenced at high content of propylene isophthalate or propylene adipate units, respectively. Amorphous samples were obtained after melt quenching and an increment of T_g as the content of PI units is increased was observed. This behavior was explained as due to the stiff phenylene groups in the polymeric chain. The Wood equation was found to describe well T_g-composition data. Lastly, the presence of a rigid-amorphous phase was evidenced in the copolymers, differently from PPA homopolymer.     

Concentrated reverse micelles in a random graft block copolymer system: structure and in-situ synthesis of silver nanoparticles

The structure and rheological properties of a poly(dimethylsiloxane)-graft-poly(oxyethylene) copolymer at high concentrations in block-selective solvents were studied by small-angle X-ray scattering (SAXS) and rheometry. Analysis of SAXS data indicates that quasispherical, reverse micellar aggregates (with no ordered packing) are present in concentrated solutions of the copolymer in nonpolar solvents, and that upon addition of water, the size of such aggregates increases due to the solubilization inside the micellar cores. The viscosity of concentrated polymer solutions increases exponentially as water is added, and finally, viscoelastic, gel-like behavior is found in the vicinity of the phase separation limit. It was found that small silver nanoparticles with an average diameter of ≈3 nm can be synthesized inside the copolymer aggregates without the need of a reducing agent; namely, particles embedded in a viscoelastic matrix are obtained. The synthesis seems to follow first-order kinetics. Electronic supplementary material Supplementary material is available in the online version of this article at and is accessible for authorized users.     

Non-ionic amphiphilic block copolymers by RAFT-polymerization and their self-organization

Water-soluble, amphiphilic diblock copolymers were synthesized by reversible addition fragmentation chain transfer polymerization. They consist of poly(butyl acrylate) as hydrophobic block with a low glass transition temperature and three different nonionic water-soluble blocks, namely, the classical hydrophilic block poly(dimethylacrylamide), the strongly hydrophilic poly(acryloyloxyethyl methylsulfoxide), and the thermally sensitive poly(N-acryloylpyrrolidine). Aqueous micellar solutions of the block copolymers were prepared and characterized by static and dynamic light scattering analysis (DLS and SLS). No critical micelle concentration could be detected. The micellization was thermodynamically favored, although kinetically slow, exhibiting a marked dependence on the preparation conditions. The polymers formed micelles with a hydrodynamic diameter from 20 to 100 nm, which were stable upon dilution. The micellar size was correlated with the composition of the block copolymers and their overall molar mass. The micelles formed with the two most hydrophilic blocks were particularly stable upon temperature cycles, whereas the thermally sensitive poly(N-acryloylpyrrolidine) block showed a temperature-induced precipitation. According to combined SLS and DLS analysis, the micelles exhibited an elongated shape such as rods or worms. It should be noted that the block copolymers with the most hydrophilic poly(sulfoxide) block formed inverse micelles in certain organic solvents.     

The use of the DPE radical polymerization method for the synthesis of chromophore-labelled polymers and block copolymers

Two analogues of diphenylethene carrying phenanthrene (1-(9-phenanthryl)-1-phenylethene (PPE)) and anthracene (1-(2-anthryl)-1-phenylethene (APE)) units were used in radical polymerization of styrene (St) and methyl methacrylate (MMA) at 80 °C using AIBN as initiator. Because of the nature of the polymerization, the resulting polymers possess the corresponding chromophoric groups. Using the methodology of a DPE system, these labelled polymers were further used for the synthesis of block copolymers. In this way poly(methyl methacrylate)-b-poly(styrene) and poly(methyl methacrylate)-b-poly(acrylonitrile) with molar masses of 60,000-90,000 g/mol were synthesized. Incorporation of the chromophoric groups into both homo- and block copolymers was confirmed by spectral measurements.     

Dynamic light scattering and cryogenic transmission electron microscopy investigations on metallo-supramolecular aqueous micelles: evidence of secondary aggregation

Metallo-supramolecular diblock copolymers consisting of a polystyrene (PS) block connected to a poly(ethylene oxide) (PEO) block by a bis(terpyridine)ruthenium complex (PS₂₀-[Ru]-PEO _y ) were used to prepare aqueous micelles. The length of the PS block was kept constant, while two PEOs of different molecular weight were used. The resulting hydrated micelles and aggregates were characterized by a combination of cryogenic transmission electron microscopy (cryo-TEM) and dynamic light scattering measurements. The results were compared to those obtained for a covalent counterpart (PS₂₂-b-PEO₇₀). Cryogenic transmission electron microscopy allowed visualization of the PS core of the micelles. Moreover, the aggregates result from clustering of individual micelles.