Preparation, structures and photoluminescent enhancement effect of PbWO4–TiO2 composite nanofilms

A novel route for preparing PbWO₄–TiO₂ nanofilms on a glass substrate is firstly proposed. The collodion is used as a dispersant and film-forming agent. The nanofilms are characterized through SEM, XRD, TG/DTA, PL and IR, respectively. The results of XRD indicate PbWO₄ particles with tetragonal scheelite structure and TiO₂ particles with Anatase phase, and SEM shows they are well dispersed in the substrate. Compared with nanoparticles, when TiO₂ nanoparticles are added in 5% ratio, the PL intensities at 395 nm of PbWO₄ nanofilms are enhanced obviously. IR spectrum reveals a large absorption band between 750 and 870 cm⁻¹, which is the W–O stretching vibration in WO₄ tetrahedron.     

Tribological Behavior of Multiply-Alkylated Cyclopentanes (MACs)-Cu Nanoparticles Composite Thin Film

Multiply-alkylated cyclopentanes (MACs) composite thin films containing Cu nanoparticles are fabricated on the octadecyltrichlorosilane (OTS)-modified substrate by a spin-coating technique. The thickness, wetting behavior, and nanoscale morphologies of the films are characterized by means of ellipsometry, contact angle measurement, and atomic force microscope (AFM). The friction and wear behaviors of the thin films sliding against Si₃N₄ ball are examined on a UMT-2MT tribometer in a ball-on-disk contact mode. The worn surfaces of the OTS-MAC-Cu composite film and the counterpart Si₃N₄ balls are investigated with a scanning electron microscope. Water contact angle on OTS-MAC-Cu composite film is higher than that of OTS-MAC film. OTS-MAC-Cu composite film exhibits higher load-carrying capacity and better friction reduction and antiwear behavior as compared with OTS-MAC film. This may be attributed to the load-carrying and self-repairing property of the Cu nanoparticles in the composite film and the formation of a transfer layer composed of OTS, MAC, and Cu on the rubbing surface of the counterpart ball.     

Infrared absorption spectra and structure of TiO2-SiO2 composites

The composites xTiO₂-(1−x)SiO₂ (x = 0.1, 0.5, 0.9) were obtained by coprecipitation from solutions of alkoxides: tetraethoxysilane (TEOS) and titanium tetraisopropoxide (TIPT). Intermolecular interaction of the components of the composite is apparent in the IR absorption spectra in the 928–952 cm⁻¹ region, and is connected with bending vibrations of the Si-O-Ti bond. Translated from Zhurnal Prikladnoi Spektroskopii, Vol. 75, No. 5, pp. 724–728, September–October, 2008.     

Preparation of nano-hydroxyapatite/poly(<Emphasis Type="SmallCaps">l</Emphasis>-lactide) biocomposite microspheres

Nano-hydroxyapatite (HA)/poly(l-lactide) (PLLA) composite microspheres with relatively uniform size distribution were prepared by a solid-in-oil-in-water (s/o/w) emusion solvent evaporation method. The encapsulation of the HA nanopaticles in microshperes was significantly improved by grafting PLLA on the surface of the HA nanoparticles (p-HA) during emulsion process. This procedure gave a possibility to obtain p-HA/PLLA composite microspheres with uniform morphology and the encapsulated p-HA nanoparticle loading reached up to 40 wt% (33 wt% of pure HA) in the p-HA/PLLA composite microspheres. The microstructure of composite microspheres from core-shell to single phase changed with the variation of p-HA to PLLA ratios. p-HA/PLLA composite microspheres with the diameter range of 2–3 μm were obtained. The entrapment efficiency of p-HA in microspheres could high up to 90 wt% and that of HA was only 13 wt%. Surface and bulk characterizations of the composite microspheres were performed by measurements such as wide angle X-ray diffraction (WAXD), thermal gravimetric analysis (TGA), environmental scanning electron microscope (ESEM) and transmission electron microscopy (TEM).     

三氧化二铝-聚苯乙烯复合微球的制备

以Al2O3-PS复合材料为原料,采用乳液微封装法制备出掺杂Al2O3的PS空心微球。三相溶液分别是两个水相：蒸馏水（W1相）、5wt%PVA水溶液（W2相）和3wt%Al2O3-PS溶液（O相,苯和三氯甲烷混合物作溶剂）。所得微球表面粗糙度低于50nm。     

Relation between interfacial shear strength and compressive strength of carbon fiber/epoxy resin composite strands

The mechanism with which the fiber-matrix interfacial strength exerts its influence on the compressive strength of fiber reinforced composites has been studied by measuring the axial compressive strength of carbon fiber/epoxy resin unidirectional composite strands having different levels of interfacial shear strength. The composite strands are used for experiments in order to investigate the compressive strength which is not affected by the delamination taking place at a weak interlayer of the laminated composites. The interfacial strength is varied by applying various degrees of liquid-phase surface treatment to the fibers. The efficiency of the compressive strength of the fibers utilized in the strength of the composite strands is estimated by measuring the compressive strength of the single carbon filaments with a micro-compression test. The compressive strength of the composite strands does not increase monotonically with increasing interfacial shear strength but showes lower values at higher interfacial shear strengths. With increasing interfacial shear strength, the suppression of the interfacial failure in the misaligned fiber region increases the compressive strength, while at higher interfacial shear strengths, the enhancement of the crack sensitivity decreases the compressive strength.     

Li-defect interactions in electron-irradiated n-type silicon by EPR measurements

Single crystal silicon, both with and without oxygen, has been diffused with lithium to concentrations ～10¹⁷/cm², irradiated with 1 to 1.5 MeV electrons, and the ensuing defects studies by EPR measurements. The presence of oxygen strongly affects the properties of these defects. Measurements have indicated the presence of two new defects which involve Li-one in O-containing material and one in O-free material. The defects are observed in their electron-filled state, and indicate a net electron spinof ½. The defect spectra disappear (with time) at room temperature, and can be explained by the formation of other Li-involved defects which lie deeper in the energy bandgap and are not visible by EPR. Electron irradiation at 40 °K followed by annealing at higher temperatures show that both EPR defects described above begin to form at about 200 °K and begin to decrease at about 275 °K-just as does the 250 °K reverse annealing observed generally for n-type Si. Based on these data, and the work of others, it is suggested that both defects form as a result of the motion of Si interstitials which produce a (Li-O-interstitial) complex in O-containing Si, and a (Li-interstitial) complex in O-free Si.     

平均折射率为零的光子晶体中缺陷模频率特性的实验研究

利用传输线技术制备了左手材料,将左手材料与正常材料交替排列组合成平均折射率为零的一维光子晶体.该光子晶体在特定频段具有光子带隙,带隙不随晶格尺度和入射角的变化而改变.通过掺杂技术破坏光子晶体的周期性,可在禁带中引入缺陷模,这种结构的光子晶体可用于实现滤波器小型化和超强耦合.研究表明,通过调节缺陷的厚度可以控制缺陷模的频率,这为调节频率提供了一种方法.实验与仿真结果相符. 关键词： 左手材料 复合左右手传输线 光子晶体     

TRANSIENT ANALYSIS OF COMPOSITE PLATES BY A LOCAL RADIAL BASIS FUNCTIONS-FINITE DIFFERENCE TECHIQUE

The use of local numerical schemes,such as finite differences produces much better conditioned matrices than global collocation radial basis functions methods.However,finite difference schemes are limi...