La1-xNdxSrCoO4催化剂的合成及其催化性能

采用聚丙烯胺溶胶-凝胶法制备了类钙钛矿La1-xNDxSrCoO4(x=0.1～0.9)复合氧化物催化剂,考察了其对CO和C3H8的催化氧化活性,并运用XRD、IR和TPR等手段对催化剂进行了表征.结果表明,所制备的样品均具有K2NiF4型结构,适量Nd2O3的加入增加了LaSrCoO4的催化活性,使LaSrCoO4催化剂粒度变小、晶格畸变率变大及与氧的结合能力减弱,从而有利于CO和C3H8氧化活性的提高.     

硼砂与氯化铵合成hBN反应机理的研究

 研究了以硼砂、氯化铵为原料在氨气气氛下合成hBN 的反应机理。指出氯化铵在反应中的主要作用是与硼砂反应形成可阻止硼砂颗粒团聚的高熔点膜层；而氨气的主要作用就是提供大量参与反应的NH₃分子，增加了反应几率；新生成的hBN则进一步隔离高度熔融的硼砂团粒，防止玻璃相的生成。     

Investigation of chemical decomposition of CCl4 on TiO2 near room temperature

Dissociative adsorption of CCl₄ on TiO₂ at 35 °C has been studied by Fourier-transform infrared spectroscopy, X-ray photoelectron spectroscopy, and electron spin resonance. CCl₄ decompose to form CO, CO₂, and CO₃ on the surface, at such a low temperature, in which CO₂ formation is not from CO oxidation on TiO₂, but CO₃ can be produced by CO and CO₂ adsorption. The Cl generated from CCl₄ decomposition is left on the surface and bonded to titanium ions. Mineralization of CCl₄ on TiO₂ involves the lattice oxygens. Thermodynamical driving force and possible reaction routes for CO and CO₂ formation in the CCl₄ decomposition on TiO₂ are discussed.     

Dielectric and conduction mechanism studies of PVA-orthophosphoric acid polymer electrolyte

Polyvinyl alcohol (PVA)-based proton conducting polymer electrolytes have been prepared by the solution cast technique. The conductivity is observed to increase from 10⁻⁹ to 10⁻⁴ S cm⁻¹ as a result of orthophosphoric acid (H₃PO₄) addition. The plot of conductivity vs temperature shows that a phase transition occurred at 343 K in the sample PVA-33 wt% H₃PO₄. The β-relaxation peak is observed at 313 K. The glass transition temperature of PVA-33 wt% H₃PO₄ is 343 K. Orthophosphoric acid seems to play a dual role, i.e., as a proton source and as a plasticizer. The ac conductivity σ _ac = Aω ^s was also calculated in the temperature range from 303 to 353 K. The conduction mechanism was inferred by plotting the graph of s vs T from which the conduction mechanism for sample PVA-17 wt% H₃PO₄ was inferred to occur by way of the overlapping large polaron tunneling (OLPT) model and the conduction mechanism for the sample PVA-33 wt% H₃PO₄ by way of the correlated barrier height (CBH) model.     

Synthesis and cyclization of 1-arylalk-1-ene-3,5-diynylamines

An investigation of the reaction of 1-lithio-1,3-diynes, generated in situ, with nitriles has been carried out. In the case of aromatic nitriles 1-arylalk-1-ene-3,5-diynylamines are formed, which undergo dimerization and cyclization on isolation, giving 3-(alka-1,3-diynyl)-4-(alk-2-ynyl)-2,6-diarylpyridines. The effect of the nature of the substituent in the benzonitrile molecule on the selectivity of the reaction and the yield of the products has been determined. A scheme is proposed for the conversions and the structures of the intermediates have been established. __________ Translated from Khimiya Geterotsiklicheskikh Soedinenii, No. 5, pp. 701–710, May, 2006.     

Microwave synthesis of magnetic Fe3O4 nanoparticles used as a precursor of nanocomposites and ferrofluids

Methods to synthesize magnetic Fe₃O₄ nanoparticles and to modify the surface of particles are presented in the present investigation. Fe₃O₄ magnetic nanoparticles were prepared by the co-precipitation of Fe³⁺ and Fe²⁺, NH₃·H₂O was used as the precipitating agent to adjust the pH value, and the aging of Fe₃O₄ magnetic nanoparticles was accelerated by microwave (MW) irradiation. The obtained Fe₃O₄ magnetic nanoparticles were characterized by Fourier transform infrared spectroscopy (FT-IR), transmission electron microscopy (TEM), X-ray powder diffraction (XRD) and vibrating sample magnetometer (VSM). The average size of Fe₃O₄ crystallites was found to be around 8–9 nm. Thereafter, the surface of Fe₃O₄ magnetic nanoparticles was modified by stearic acid. The resultant sample was characterized by FT-IR, scanning electron microscopy (SEM), XRD, lipophilic degree (LD) and sedimentation test. The FT-IR results indicated that a covalent bond was formed by chemical reaction between the hydroxyl groups on the surface of Fe₃O₄ nanoparticles and carboxyl groups of stearic acid, which changed the polarity of Fe₃O₄ nanoparticles. The dispersion of Fe₃O₄ in organic solvent was greatly improved. Effects of reaction time, reaction temperature and concentration of stearic acid on particle surface modification were investigated. In addition, Fe₃O₄/polystyrene (PS) nanocomposite was synthesized by adding surface modified Fe₃O₄ magnetic nanoparticles into styrene monomer, followed by the radical polymerization. The obtained nanocomposite was tested by thermogravimetry (TG), differential scanning calorimetry (DSC) and XRD. Results revealed that the thermal stability of PS was not significantly changed after adding Fe₃O₄ nanoparticles. The Fe₃O₄ magnetic fluid was characterized using UV–vis spectrophotometer, Gouy magnetic balance and laser particle-size analyzer. The testing results showed that the magnetic fluid had excellent stability, and had susceptibility of 4.46×10⁻⁸ and saturated magnetization of 6.56 emu/g. In addition, the mean size d (0.99) of magnetic Fe₃O₄ nanoparticles in the fluid was 36.19 nm.