Two‐stage copolycondensation of preformed oligomers with bisphenols by tosyl chloride/dimethylformamide/pyridine from distributions of resulting oligomers determined by a combination of gel permeation chromatography and NMR

A two‐stage co‐oligomerization of the oligomers initially formed from an equimolar mixture of isophthalic acid (IPA) and terephthalic acid (TPA) and 2,2‐bis(4‐hydroxyphenyl)propane (BPA, 50 mol %) with bisphenols (BPs, 20 mol %) was carried out using a tosyl chloride/dimethylformamide/pyridine condensing agent. The distributions of the resulting oligomers (n_x‐mers), which were quenched with methanol, were determined by a combination of gel permeation chromatography (GPC) and NMR. These distributions (presented by molar percentage) were conveniently calculated with the equation n_x (mol %) = n_x (% mol by GPC) × n₀ (mol % by NMR)/n₀ (% mol by GPC), where n_x (% mol) = n_x (wt % by GPC)/its molecular weight. The results showed the distributions of the preformed IPA/TPA‐BPA oligomers to be in fairly good accord with those obtained directly from GPC and to be supported by the NMR results. The calculation was applied to the co‐oligomers prepared up to a reaction of 0.7, at which there was an increase in the number of higher oligomers indivisible by GPC and the distributions could no longer be determined by molar percentage. The calculated distributions are discussed in relation to the results of copolycondensation. The sequence distributions in the resulting co‐oligomers, which were also examined by NMR, are compared with those in the copolymers. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 44–51, 2004     

Polymerization of 1,3‐dienes with functional groups. III. Free‐radical polymerization of N,N‐diethyl‐2‐methylene‐3‐butenamide

Free‐radical homo‐ and copolymerization behavior of N,N‐diethyl‐2‐methylene‐3‐butenamide (DEA) was investigated. When the monomer was heated in bulk at 60 °C for 25 h without initiator, rubbery, solid gel was formed by the thermal polymerization. No such reaction was observed when the polymerization was carried out in 2 mol/L of benzene solution with with 1 mol % of azobisisobutyronitrile (AIBN) as an initiator. The polymerization rate (R_p) equation was R_p ∝ [DEA]^1.1[AIBN]^0.51, and the overall activation energy of polymerization was calculated 84.1 kJ/mol. The microstructure of the resulting polymer was exclusively a 1,4‐structure where both 1,4‐E and 1,4‐Z structures were included. From the product analysis of the telomerization with tert‐butylmercaptan as a telogen, the modes of monomer addition were estimated to be both 1,4‐ and 4,1‐addition. The copolymerizations of this monomer with styrene and/or chloroprene as comonomers were also carried out in benzene solution at 60 °C. In the copolymerization with styrene, the monomer reactivity ratios obtained were r₁ = 5.83 and r₂ = 0.05, and the Q and e values were Q = 8.4 and e = 0.33, respectively. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 999–1007, 2004     

Structure and properties of the mesophase of syndiotactic polystyrene. VIII. Solvent sorption behavior of syndiotactic polystyrene/p‐chlorotoluene mesophase membranes

A crystalline δ form of a syndiotactic polystyrene (sPS) membrane was prepared from a solution of sPS (1 wt %) and p‐chlorotoluene (p‐CT) by a solution‐casting method. The mesophase (δ empty form) of sPS was obtained by the extraction of the guest solvent from the δ form of sPS by a stepwise solvent‐extraction method. The sPS/p‐CT mesophase membrane [p‐CT (A‐M)] was used for the sorption of 1 mol % p‐CT for different times and for the sorption of different concentrations of p‐CT, chlorobenzene (CB), p‐xylene (p‐X), toluene, and chloroform for 48 h. The presence of solvents in the sPS membrane was confirmed by IR analysis. A thermal study revealed that the sorption amount of 1 mol % p‐CT increased with increasing immersion time, and the sorption amounts of different solvents increased with increasing solvent concentration. Differential scanning calorimetry results showed that the desorption peak temperature increased as the amount of the solvent increased in the clathrated sPS membrane. Wide‐angle X‐ray diffraction results showed that 2θ at 8.25° was slightly shifted toward 8°, and there was no change in the peak position at 10° for p‐CT (A‐M), which was immersed in different solvents (1 mol %); however, the intensity of 2θ at 10° was not similar for all the samples. Among the solvents used for the sorption studies at 1 mol %, p‐CT (A‐M) could sorb more p‐CT and CB than p‐X, toluene, and chloroform. The solvent sorption isotherm was the Langmuir sorption mechanism. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 3439–3446, 2004     

Toughness mechanism in polypropylene composites: Polypropylene toughened with elastomer and calcium carbonate

Polypropylene (PP) was modified with elastomer or CaCO₃ particles of two different sizes (1 μm and 50 nm) in various volume fractions. The dispersion morphology and mechanical properties of the two systems were investigated as functions of the particle size and volume fraction of the modifier. The brittle‐to‐tough transition occurred when the matrix ligament thickness was less than the critical ligament thickness, which was about 0.1 μm for the PP used here, being independent of the type of modifier. At the same matrix ligament thickness, the improvement of the toughness was obviously higher with the elastomer rather than with CaCO₃, but adding CaCO₃ increased the modulus of PP. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 1656–1662, 2004     

(Nd_(1-x)Er_x)_2Co_(15.5)V_(1.5)的结构转变与磁性

利用电弧熔炼制备了 (Nd1 xErx) 2 Co1 5 5V1 5(x=0— 1 0 )化合物样品 .通过x射线衍射分析和磁性测量研究了Er替代Nd2 Co1 5 5V1 5中的Nd时对化合物结构和磁性的影响 .研究结果表明 ,低Er含量 (x <0 4 ) ,化合物为Th2 Zn1 7型结构 ;高Er含量时 (x >0 5 ) ,化合物转变为Th2 Ni1 7结构 ;Er含量为x =0 4和 0 5时 ,两种结构共存 .两种结构的晶胞参数a ,c和晶胞体积V随着Er含量的增加都呈现递减的趋势 .随着Er含量的增加 ,(Nd1 xErx) 2 Co1 5 5V1 5化合物的居里温度和饱和磁化强度都单调下降 .(Nd1 xErx) 2 Co1 5 5V1 5化合物的室温各向异性由低Er含量时的易锥型转变为高Er含量时的易轴型 .x =0— 0 5的化合物在温度升高时发生自旋重取向转变 ,自旋重取向温度Tsr随Er含量的增加而减小     

类钙钛矿化合物Ca(Mn2 Cu1)Mn4 O12的磁性与磁电阻效应

利用固相反应法制备了名义成分为Ca(Mn2 Cu1 )Mn4 O1 2 的类钙钛矿锰氧化物 .x射线衍射表明 ,为了获得较为致密的样品和减小杂相含量 ,可以采用高温烧结再在 10 73K长时间空气中退火的制备方法 .样品在低温下同时存在铁磁相和反铁磁相 ,由于反铁磁相的存在导致样品在 4 5K时的磁化强度显著降低 ,并在 8T的高磁场下仍未达到饱和 .样品呈半导体导电性质 ,在 85K和 6T磁场下磁电阻比的最大值可达 - 4 6 % .     

波段三维ESR成像系统的研制（Ⅴ）——灵敏度与分辨率实验及系统总性能指标

实验确定了自行研制的L波段三维电子自旋共振成像（3D-ESRI）系统的检测灵敏度及成像分辨率指标. 用Tempo水溶液模型测量灵敏度结果表明： 样品体积为10 mm, 高30 mm，测量浓度1×10^-4 mol/L水溶液的信噪比为S/N=4∶1；加梯度磁场后，样品浓度需>5×10^-4 mol/L，样品体积为19 mm, 高30 mm时，获得的投影谱的信噪比可满足图像重建的需要. 用DPPH固体样品确定的成像分辨率结果<1 mm. 文中还对ESRI系统的
各项总体性能做了归纳总结.     

Cr3+：MgAl2O4晶体EPR参量及其电子精细光谱的研究

考虑了SS(Spin-Spin)作用和SOO(Spin-Other-Orbit)作用，采用完全对角化方法，结合自旋Hamiltonian理论，研究了Cr³⁺∶MgAl₂O₄晶体EPR参量及其吸收光谱，理论与实验符合甚好. 在此基础上，进一步研究了⁴A₂(3d³)离子EPR参量的微观起源. 研究表明，EPR参量起源于四种微观机制：(1) SO(Spin-Orbit) 耦合机制；(2) SS耦合机制；(3)SOO耦合机制；(4) SO～SS～SOO总联合作用机制. 在这些机制中，SO机制是最主要的.     

旋光性与电光效应交互作用及其对旋光晶体电光Q开关的影响

研究了晶体的旋光性与电光效应的交互作用、以及此交互作用对 旋光晶体电光Q开关的影响. 关键词： 旋光性 电光效应 电光Q开关 3Ga₅SiO₁₄晶体')" href="#">La₃Ga₅SiO₁₄晶体     

Yb:FAP和Yb:C_3S_2-FAP晶体光谱的温度特性和选择激发

报导了Yb :FAP和Yb :C3S2 _FAP晶体在不同温度下的吸收光谱和荧光光谱实验结果 ,研究发现由于电子_声子近共振耦合作用 ,Yb :FAP和Yb :C3S2 _FAP晶体均存在有明显的振动谱 ,Yb :FAP晶体的零声子线在低温下还劈裂为相差 10cm- 1 的两条线 .采用激光选择激发技术研究了Yb3 离子在FAP和C3S2 _FAP晶体中的格位特征 ,结果表明Yb3 离子在这两种基质中都只占据Ca(Ⅱ )格位 ,但由于CaF2 的挥发 ,导致了Ca(Ⅱ )格位的局部畸变 .