钙钛矿型La_((1 x)/2)Sr_((1-x)/2)Co_(1-x)Cu_xO_3催化CO氧化活性与表征

研究了钙钛矿型LaSrCoCu_xO_3催化剂对CO氧化反应的催化活性及其表面氧的催化作用．结果表明，x＝0．4的催化剂对CO氧化具有最高催化活性，常压及本实验条件下CO完全氧化的最低温度为168℃；催化剂均为氧缺陷化合物，吸附于表面晶格氧缺陷上的吸附氧是CO氧化反应的活性氧物种；并发现催化剂中存在有非常价态的C04 ，认为CO氧化反应是通过吸附氧调变Co3 和Co4 价态而进行．     

光谱复杂的稀土基体中稀土杂质ICP光谱测定的一些问题

ICP激发光源以其独特的功能使ICP/AES技术在稀土分析中的应用日益广泛,在一定程度上取代了经典的直流电弧光谱法,但应指出,由于常规雾化器的低雾化效率(≤5％)和试样的高倍稀释,ICP/AES技术的实际检测能力的改善并不明显,本文用ICP光谱法测定了     

Crystal Structure of Organometallic Complex [Zn（pom）2I2]

ＣｒｙｓｔａｌＳｔｒｕｃｔｕｒｅｏｆＯｒｇａｎｏｍｅｔａｌｌｉｃＣｏｍｐｌｅｘＺｎ（ｐｏｍ）_２Ｉ_２］ＤｏｎｇＭｅｉ－Ｂｉｎ；ＬｉＳｏｎｇ－Ｘｉａｎ；ＺｈａｎｇＨａｎ－Ｈｕｉ（ＤｅｐａｒｔｍｅｎｔｏｆＣｈｅｍｉｓｔｒｙ，ＦｕｚｈｏｕＵｎｉｖｅｒｓｄｙ...     

手性恶唑硼烷结构与还原苯基乙基甲酮的对映选择性研究

本文以苯基乙基甲酮为还原底物, 研究了原地(in situ)制备的在3、4、5位具有不同取代基的手性1,3,2-恶唑硼烷催化剂的结构与不对称催化效应关系。研究结果表明, 在不对称催化硼烷还原反应中(CBS方法)、产物的构型和对映选择性主要受手性恶唑硼烷的4位取代基控制。     

含吡咯烷酮基丙烯酸酯类单体的合成及聚合

轻度交联的聚甲基丙烯酸2-羟乙酯(HEMA)是众所周知的医用水凝胶,即所谓的“Hvdron”。但其吸水率一般在59%(EWC为37%),并不尽人意。近年来,为了提高这类水凝胶的亲水性及生物相容性,常用一些亲水性的烯类单体进行表面改性或通过共聚以达到此目的,N-乙烯基吡咯烷酮是较为常用的这类单体之一。本文合成了含吡咯烷酮基丙烯酸酯类的单体,即丙烯酸2-N-吡咯烷酮基乙酯(PyEA),甲基丙烯酸2-N-吡咯烷酮基乙醋(PyEMA),并研究了这两种单体在甲基丙烯酸二甲氨乙酯(DMAEMA)与过硫酸钾(KPS)所组成的氧化还原引发体系下的聚合。     

Ru/Mn-Ce/TiO2催化剂催化湿式氧化丁二酸的反应活性和动力学研究

在二氧化钛载体中通过掺杂Ru，Mn，Ce制备了一系列用于催化湿式氧化的催化剂，利用XRD，TEM，BET等手段对催化剂进行了表征．在反应温度T=210～270℃，氧分压Po2=2．1MPa条件下，在间歇式高压反应釜中对丁二酸进行了降解实验．催化剂在反应中有很高的催化活性．催化剂在30min内对丁二酸降解的COD去除率为54．4～98．3％．Ru及Mn，Ce的氧化物对催化活性都有促进作用．建立了丁二酸催化湿式氧化的一级分段动力学模型．基于COD的一段及二段反应的活化能分别为43．74kJ／mol和54．28kJ／mol．     

A Novel Cu-Mo／ZSM-5 Catalyst for NOx Catalytic Reduction with Ammonia

The Cu-Mo/ZSM-5 catalysts with different Cu/Mo ratios were prepared by wet impregnation method, and their catalytic performance for selective catalytic reduction of NOx was studied. The results showed that Cu-Mo/ZSM-5 is a very effective catalyst for NOx catalytic reduction with ammonia, especially when Cu/Mo molar ratio is about 1.5. It not only exhibited the extremely high catalytic activity, but also showed good stability for 02. The bulk phase structure of Cu-Mo/ZSM-5 catalysts was determined by XRD technique, and the results indicated that there is a maximum dispersion for Cu species when Cu/Mo molar ratio is 1.5, and an interaction between Cu and Mo along with HZSM-5 may be present in Cu-Mo/ZSM-5, which may possibly result in a special structure favorable for the catalytic reduction of NOx over Cu-Mo/ZSM-5 catalyst.     

水热法合成Ce0.67Zr0.33O0.2固溶体研究

采用两种不同前驱体通过水热法合成了Ce0.67Zr0.33O0.2固溶体,并通过XRD,BET,TPR等手段考察了样品的相结构,比表面及还原特性.结果表明,在180℃,12 h的水热条件下,以共沉淀产物为前驱体所制得的Ce0.67Zr0.33O0.2固溶体比表面积较高,但存在一定程度的相分离;以凝胶产物为前驱体制得的Ce0.67Zr0.33O0.2固溶体结构更完整,具有良好的还原特性及热稳定性.     

化学光谱法测定5N氧化钆中14个稀土杂质元素

报道了化学光谱法测定５Ｎ高纯氧化钆中１４个稀土杂质元素，在Ｐ５０７萃淋树脂色层柱上分离氧化钆中稀土杂质元素，分别采用定量分离Ｌａ－Ｓｍ及Ｔｂ－Ｌｕ＋Ｙ和部份分离Ｅｕ的方法，并相应地采用碳粉吸附法和碳粉粉末法进行光谱测定。分离时间为３．５ｈ，测定下限为１．２μｇ／ｇ（ＲＥ）。