触头用银合金粉末的氧化性能和氧化后的组织结构

通过热重实验和扫描电子显微等方法，研究了４种触头用银合金粉末的氧化性能及氧化后的组织结构。发现Ａｇ－Ｓｎ－ＲＥ合金粉末氧化以后，在粉末表层形成一层纯银层，其组织结构理想；它的氧化性能最好，适于制备触头材料。Ａｇ－Ｓｎ－ＲＥ合金粉末的优良氧化性能与其氧化后理想的组织结构有关。稀土元素可以降低合金粉末的氧化温度，其它影响作用有待于进一步研究。     

Ω型分子筛脱铝的核磁共振研究

在不同投料比（ＳｉＯ２／Ａｌ２Ｏ３＝１３．８，１９及２１）条件下，合成了三种Ω型分子筛原粉．对投料比为１３．８的原粉样品进行了四种不同方式的脱铝处理，即水热、ＳｉＣｌ４、ＥＤＴＡ和（ＮＨ４）２ＳｉＦ６处理，而形成了系列脱铝Ω型分子筛样品．对原粉及其脱铝样品进行了２９Ｓｉ和２７ＡｌＭＡＳＮＭＲ测试，确定出样品骨架硅铝比和铝在两种晶体学不等价Ｔ位上的占据比率，以探索四种脱铝方法的效果．实验结果与分析表明：在所有样品中，铝原子的占据具有择优Ｂ位的倾向；且铝在ＴＡ与ＴＢ位上的占据比率与合成条件有关；四种处理方式对Ω型分子筛的脱铝效果不尽相同．     

ICP-AES法测定硅铝钡钙合金

硅铝钡钙合金是炼钢常用的复合脱氧剂[1] ,它具有较强的脱氧能力和使夹杂物变质的能力 ,同时还能脱硫[2 ] 。硅铝钡钙合金目前既无国家标准分析方法 ,又无较成熟的化学分析方法 ,本文研究了用ＩＣＰ发射光谱仪测定硅铝钡钙合金的方法。本法采用基准物质配制标准系列绘制工作曲线 ,并用回收试验和试样精密度试验来证实方法的可靠性。1　试验部分1.1　仪器与试剂美国ＰＥ公司的ＯＰＴＩＭＡ330 0型全谱直读电感耦合等离子体发射光谱仪铝、钡、锶、锰、钙、磷、铁标准溶液 :用光谱纯金属氧化物或基准物质分别配置成 1ｍｇ·ｍｌ-1的储备液 ,使…     

Study of Manganese Promoter on a Precipitated Iron-Based Catalyst for Fischer-Tropsch Synthesis

The effects of Manganese(Mn)incorporation on a precipitated iron-based Fischer-Tropsch synthesis(FTS)catalyst were investigated using N_2 physical adsorption,air differential thermal analysis (DTA),H_2 temperature-programmed reduction(TPR),and M(?)ssbauer spectroscopy.The FTS perfor- mances of the catalysts were tested in a slurry phase reactor.The characterization results indicated that Mn increased the surface area of the catalyst,and improved the dispersion ofα-Fe_2O_3 and reduced its crystallite size as a result of the high dispersion effect of Mn and the Fe-Mn interaction.The Fe-Mn inter- action also suppressed the reduction ofα-Fe_2O_3 to Fe_3O_4,stabilized the FeO phase,and(or)decreased the carburization degree of the catalysts in the H_2 and syngas reduction processes.In addition,incorporated Mn decreased the initial catalyst activity,but improved the catalyst stability because Mn restrained the reoxidation of iron carbides to Fe_3O_4,and improved further carburization of the catalysts.Manganese suppressed the formation of CH_4 and increased the selectivity to light olefins(C_(2-4)~=),but it had little effect on the selectivities to heavy(C_(5 )) hydrocarbons.All these results indicated that the strong Fe-Mn interaction suppressed the chemisorptive effect of the Mn as an electronic promoter,to some extent,in the precipitated iron-manganese catalyst system.     

Preparation of Small Particle Sized ZnAl-Hydrotalcite-Like Compounds by Ultrasonic Crystallization

Ultrasonic technology has been intensively studied recently due to its special features. In this paper, an ultrasonic crystallization method was introduced for the preparation of ZnAl-Hydrotalcite-Like compounds (ZnAl-HTLcs). Samples with high crystallinity, small particle size and narrow particle size distribution were obtained and fully characterized using conventional techniques of XRD, FT-IR and TGDTA. The results prove that both ultrasonic frequency and ultrasonic power have effects on the sizes of the product particles. By varying the ultrasonic power from 250 W to 88 W, with the ultrasonic frequency fixed at 59 kHz, the median particle size of the samples increased from 0.37 μm to 0.82 μm. By altering the hydrothermal treatment time from 1 h to 5 h at 110℃, the median particle size of ZnAl-HTLcs synthesized via ultrasonic crystallization increased from 0.88 μm to 1.11 μm.     

水杨醛乙酰腙席夫碱作为Al3+荧光探针分子的理论研究

用密度泛函理论和含时密度泛函理论研究了实验上合成的一种基于水杨醛席夫碱的Al~(3+)荧光探针的性质.通过优化探针分子及其与Al~(3+)形成的配合物可能存在的异构体的几何结构,并模拟各异构体的电子吸收光谱,找到了最可能存在的异构体.最后模拟了它们的荧光光谱,进一步验证了前面推测的异构体的正确性,加深了人们对这一探测过程的认识.     

现场表面拉曼光谱研究Fe-Mo合金诱导共沉积

现场表面拉曼光谱结果显示，在0．2mol·L-1Na2MoO4,pH＝4．0的溶液中，电位正于0．5V（vsSCE）时只观察到多钼酸盐的拉曼峰（940、880和450cm-1）．负于-0．5V时，出现中心位于730cm-1的宽峰．同时电极表面有蓝色膜生成．表明混合氧化态（MO（Ⅳ），MO（Ⅴ））氧化膜的形成．730cm-1的峰在-1．9V时仍然存在，说明氧化膜没有被进一步还原．在钼酸钠溶液中同时含有0．1mol·L-1FeSO4和0．2mol·L-1柠檬酸时，中间态氧化膜的拉曼峰的中心移到740cm-1．且峰强度随着电位从-1．3V负移到-1．9V而逐渐减弱并最终消失．电极表面沉积层呈银白色，说明由于Fe2 的存在，钼的中间态氧化膜的结构发生了变化，能够被进一步还原形成Fe－Mo合金，表现出诱导共沉积的特征．     

5—（4‘—溴—2’—羧基苯偶氮）罗丹宁与铜（Ⅱ）的显色反应及其应用

本报道了新显色剂５－（４’－溴－２’－羧基苯偶氮）罗丹宁的合成及在水溶液中的离解常数Ｋ１和Ｋ２，研究了该显色剂与铜（Ⅱ）的显色反应，在弱酸性时，试剂与铜（Ⅱ）形成摩尔比２：１的络合物，摩尔吸光系数为８．９×１０＾４Ｌ．ｍｏｌ＾－１．ｃｍ＾－１。当铜的浓度在０～２．７ｍｇ／Ｌ的范围内符合比耳定律。用分光光度法测定了合金中铜的含量。     

ICP-AES法测定锌阳极中的铝、镉、铁、铜、铅

通过分析高频功率、雾化压力、辅助气流量和泵速等试验条件，建立了ICP-AES法测定锌阳极中铝、镉、铁、铜、铅的方法。用该方法测定锌阳极中的铝、镉、铁、铜、铅，其RSD分别为0.17%、0.63%、2.7%、5.2%、2.5%，回收率分别为99.3%-101.2%，99.3%-100.3%、97.1%-102.2%、97.8%-102.9%。对锌阳极试样进行测定，该方法的测定结果与GB4951-85方法的测定结果基本一致。