Doping in the Mixed Layer to Achieve High Brightness and Efficiency Organic Light Emitting Devices

Doping in the mixed layer was introduced to fabricate high brightness and high efficiency organic light emitting devices.In these devices,a copper phthalocyanine(CuPc) film acts as the buffer layer,a naphthylphenybiphenyl amine (NPB) film as the hole transport layer and a tris(8-hydroxyquinolinolate) aluminium (Alq3) film as the electron transport layer.The luminescent layer consists of the mixture of NPB,Alq3( to be called the mixed layer),and an emitting dopant 5,6,11,12-petraphenylnaphthacene (rubrene),where the concentration of NPB declined and the concentration of Alq3 was increased gradually in the deposition process.Adopting this doping mixed layer,the device exhibits the maximum emission of 49300cd/m^2 at 35V and the maximum efficiency of 7.96cd/A at 10.5V,which have been improved by two times in comparison with conventional doped devices.We attribute this improvement to the effective confinement of carriers in the mixed layer,which leads to the increase of the recombination efficiency of carriers.     

溶剂效应对聚喹啉铝发光特性的影响

研究了非共轭聚喹啉铝（Palq)在氯仿和乙醇不同极性的溶剂下所获得的薄膜的吸收和发光光谱。由于溶剂性的不同，聚喹啉铝链在氯仿和乙醇溶液中表现出不同的聚集状态。当各种溶液分别旋涂成膜时，溶液中的聚喹啉铝的聚集态仍部分地保存下来，导致不同聚喹啉铝薄膜的电子结构状态的差别。结果，聚喹啉铝的薄膜表现出不同的发光特性。实验表明，在制作聚合物器件中，溶剂的选择对共轭聚合物的发光特性有着重要的影响。     

改性Y沸石上苯与二异丙苯烷基转移反应活性及结炭失活的研究Ⅰ.沸石的钠含量和硅铝比对表面酸性的影响

用调节交换液ｐＨ值、高温水蒸气处理和不同浓度磷酸溶液等三种不同的改性方法对国产Ｙ型沸石进行了改性处理，运用ＴＰＤ、红外光谱、ＸＲＤ、原子吸收光谱测试了催化剂的物理性质，考察了不同改性方法对催化剂中的钠含量及骨架硅铝比的影响，以及由此造成对催化剂表面酸性质的影响。实验结果表明，这三种改性方法均能将沸石中深层次的钠交换下来。钠的减少主要产生的是Ｂｒｏｎｓｔｅｄ酸中心，而当Ｎａ２Ｏ含量低于０．２‰时，产生的又主要是强Ｂｒｏｎｓｔｅｄ酸中心。其中，高温水蒸气处理不仅影响钠的含量，而且影响硅铝比。催化剂酸性质是钠含量和硅铝比两个相反因素结合作用的结果。此外，实验结果还发现高温水蒸气处理一方面影响Ｂｒｏｎｓｔｅｄ酸量，一方面又能降低Ｂｒｏｎｓｔｅｄ酸强度。而磷酸改性只能同时改变各种强度的Ｂｒｏｎｓｔｅｄ酸量，对酸强度则没有影响。     

Deposition of Er：A12O3 Films and Photoluminescence Characteristics

Er^3 -doped Al2O3 films were deposited on silicon substrates by reactive closed-field unbalanced magnetron sput-tering. The process parameters, such as target bias voltage, substrate bias voltage, O2 gas flows, sputtering gas pressure, were studied. The 1.53μm photoluminescence characteristics from Er^3 were measured. The relations among the PL peak intensity, annealing temperatures, and pump power were experimentally investigated.     

Li-Al模拟靶件内中子注量率分布计算

为确保Li-Al模拟靶件辐照实验顺利实现，需要从理论上了解靶件内的中子注量率。     

MR/PVA薄膜的SP和PP偏振存储特性的比较

用两正交偏振光(SP)和两P偏振光(PP)作为记录光(λ=532nm)，记录光的功率均为5mW，用He—Ne激光器632．8nm红光作为读出光，分别得到两种记录条件下甲基红掺杂聚乙烯醇薄膜(MR／PVA)样品的光栅生长曲线．发现用两P偏振光作为记录光时，光栅生长曲线分为快、慢2个过程；两正交偏振光作为记录光时，光栅生长曲线只有一个过程，前者的慢过程和后者过程的响应时间近于相同．     

Eu3+掺杂铌酸盐玻璃的光谱性质

研究了Eu^3 掺杂铌磷与铌硅系列玻璃的发射光谱，声子边带谱及^5D0能级寿命，计算了样品的强度参数。随着Nb2O5浓度的增加，Eu-O键强增大，共价性增强，Eu^3 的局域环境对称性降低，电－声子耦合增强，^5D0能级的无辐射过程加快，寿命变短，温度猝灭加剧。研究了从77－690K铌磷与铌硅系列玻璃中Eu^3 离子在488nm激光激发下的变温荧光发射特性，求出了温度猝灭速率。分析了发光强度增强与减弱的原因，即热布居与无辐射过程随温度的变化关系，研究了谱线宽度与峰值位置随温度的变化关系。