聚丙烯基纳米碳纤维复合材料结晶行为研究

采用示差扫描量热法(DSC)研究了纳米碳纤维对PP／CNF复合材料中PP结晶行为的影响。结果表明：纳米碳纤雏可提高PP的结晶温度，但略降低其结晶速率和结晶度。提高纳米碳纤雏含量或减小纳米碳纤雏直径，PP结晶行为的上述变化更为明显，但结晶速率随纳米碳纤维含量出现先减小后增大的趋势。     

溶剂热还原合成Cr2O3纳米管(英)

Cr₂O₃ nanotubes with diameters of 80 nm and lengths of 550 nm were synthesized in a solvothermal reduction system at 180 ℃. The acetyl acetone (AcAc) and ethylene glycol (EG) were used as the chelate agent and the reductant respectively in the system. An intermediate compound-Cr(Ⅲ)(C₅H₇O₂)₃ was formed to force Cr₂O₃to crystallize along one direction.     

氧化铝/碳纳米管复合材料的制备及表征

采用聚乙烯醇对碳纳米管表面进行改性，通过化学沉淀法将Al(OH)₃均匀沉积在碳纳米管表面，然后在氮气气氛下于500 ℃煅烧2 h，制备出氧化铝/碳纳米管复合材料。采用TEM、TG、DTA、XRD、IR、氮吸附脱附(比表面积及孔结构分析)等对氧化铝/碳纳米管复合材料进行表征，结果表明:未经聚乙烯醇改性的碳纳米管，氧化铝与碳纳米管相互分离;经聚乙烯醇改性的碳纳米管，氧化铝与碳纳米管结合良好。经聚乙烯醇改性的碳纳米管表面均匀覆盖一层聚乙烯醇膜，通过聚乙烯醇的吸附作用， Al(OH)₃沉积在碳纳米管表面形成一层连续的覆盖层。     

铁(Ⅲ)-邻菲罗啉溶液体系的光化学还原 Ⅱ.气相色谱法研究光化反应机理

关于Fe(Ⅲ)-邻菲罗啉(phen)溶液的光化学还原现象的记载可追溯到十九世纪末。     

无纺布上的偕胺肟基团鳌合物的氧化还原反应的研究

 采用各种分析方法系统研究了含偕胺肟基因维尼无纺布与Ａｎ³⁺进行氧化还原反应时的化学结构变化、氧化还原与鳌合吸附的关系以及还原产物的结晶结构和形态．结果表明，含偕胺肟基无纺布与Ａｕ³⁺反应时，开始主要是偕胺肟基被氧化成为酰胺基．此外，有部分偕胺基因被氧化成为羧基．Ａｎ³⁺被还原的同时生成约相等当量的氢离子．反应后期或反应温度高时，氢离子生成量增大．实验结果还表明，在反应起始阶段，Ａｕ³⁺与偕胺肟基因会发生鳌合作用．还原生咸的单质Ａｎ形成“玫瑰花”状的小晶粒粘附于无纺布纤维表面．     

Preparation of Nanoelectrode Ensembles by Assembly of Nano—Silver Colloid on Gold Surface

A novel method for preparing silver nanoelectrode ensembles(SNEEs) and gold nanoelectrode ensembles (GNEEs) has been developed. Silver colloid particles were first absorbed to the gold electrode surface to form a monolayer silver colloid. N-hexadecyl nercaptan was then assembled on the electrode to form a thoil monolayer on which hydrophilic ions cannot be transfered. The SNEEs was prepared by removing thiol from silver colloid surface through applying and AC voltage with increasing frequency at 0.20V(vs.SCE). Finally,GNEEs was obtained by immersing a SNEEs into 6 mol/L HNO3 to remove the silver colloid particles. By comparison with other methods such as template method ect., this method enjoys some advantages of lower resistance, same diameter,easy preparation,controllable size and density.     

铅在铂电极上的还原电位溶出分析法

研究了以亚铁氰化钾为还原剂铅在铂电极上的还原电位溶出法；讨论了电极的预处理、阳极富集和随后的还原电位溶出及铅测定的干扰。     

还原温度对超细K－Co－Mo催化剂合成低碳醇性能的影响

 用溶胶－凝胶法合成了K－Co－Mo催化剂．样品经不同温度还原后，用于低碳醇的合成．XRD和HRTEM结果表明，样品是超细粒子，粒子尺寸为2～5nm．考察了催化剂的还原温度和反应条件对催化剂性能的影响．实验结果表明，还原温度对催化剂的活性有较大的影响，最佳还原温度为500℃．最佳反应温度范围为310～330℃．升高压力和空速可以提高醇的收率和选择性．在空速14400h－1，压力6．0MPa和温度310℃的条件下，醇的选择性为55．8％，收率为520．0g／（kg·h），MeOH／C2＋OH为0．27．催化剂稳定性良好，在200h的寿命实验中，活性基本不变．与文献中催化剂相比，超细K－Co－Mo催化剂对合成醇具有较高的活性和选择性，尤其是对C2＋OH的合成明显高于其他合成醇催化剂体系．     

碲氢化钠还原亚胺的方法

本文报道一种还原亚胺的新方法。取代的芳基和脂肪基亚胺可以在较温和的条件下被碲氢化钠顺利地还原为相应的仲胺。