Storage-Reduction of NOx over Combined Catalysts of Pt/Ba/Al2O3-Mn/Ba/Al2O3： Carbon Monoxide as Reductant

Storage-reduction of NOx by carbon monoxide was investigated over combined catalysts of Mn/Ba/Al2O3-Pt/Ba/Al2O3. Combination of Mn/Ba/Al2O3 and Pt/Ba/Al2O3 catalysts in different ways showed excellent NOx storage-reduction performance and the content of Pt could be reduced by 50%. Not only the addition of 5Mn/15Ba/Al2O3 to lPt/15Ba/Al2O3 could improve its storage ability, but also enhance the NOx conversion consequently. NOx conversion over the combined catalysts (the combined catalysts I and II) was increased under dynamic lean-rich burn conditions, the maximum NOx conversion increased from 69.4% to respectively 78.8% and 75.7% over two combined catalysts.     

BaFeO3-x与Cu-ZSM-5耦合催化剂的NOx储存还原性能

为替代传统的贵金属基NO_x储存还原（NSR）催化剂,本文设计并制备了不含贵金属的BaFeO_3-x+Cu-ZSM-5 耦合催化剂,用于催化消除稀燃发动机尾气中的NO_x. 在稀燃阶段,NO在BaFeO_3-x催化剂上发生了氧化和储存反应;在富燃阶段,从BaFeO_3-x催化剂中脱附出来未能消除的NO_x被置于其后的Cu-ZSM-5催化剂进一步催化消除. 实验结果表明,BaFeO_3-x+Cu-ZSM-5 耦合催化剂的工作温度窗口被拓宽到250-400 ℃,同时NO_x消除性能得到了显著提高：NO_x转化率最高可达98%,N₂选择性接近100%.     

负载型Au-Pd双金属催化剂的制备及其对CO氧化的催化活性

采用改性的等体积浸渍法制备了SiO2负载的Au-Pd双金属催化剂,考察了催化剂的焙烧温度对CO氧化反应活性的影响.与623,723和773K的条件下焙烧的催化剂相比,673K焙烧的催化剂具有良好的催化CO氧化活性,CO完全转化温度低于398K.应用N2物理吸附、X射线衍射、程序升温还原、CO程序升温脱附及X射线光电子能谱等技术对催化剂进行了表征.结果表明,673K焙烧的催化剂具有最大的比表面积和最小的孔径,存在Au0,Pd0和PdO相,AuxPdy合金相很少;而773K焙烧的催化剂上除了含有Au0,Pd0和PdO相外,还存在明显的AuxPdy合金相.具有大比表面积,小孔径,Au0,Pd0和PdO多相共存的催化剂可使CO的吸附量增加,催化活性提高;而AuxPdy合金相的生成并不能提高催化剂的催化活性.     

Cu掺杂对LaMnO3催化剂的结构和催化氧化性能的影响

采用非晶态多核配合的方法合成了La1-xCuxMnO3(x=0、0.05、0.1、0.2、0.3、0.4、0.5)系列催化剂, 并用X射线衍射(XRD)、透射电镜(TEM)、比表面测定仪(BET)等手段对催化剂的微观结构进行了表征. 研究了Cu掺杂对钙钛矿结构及其对CO催化氧化发光性能及催化氧化CO、CH4性能的影响规律. 结果表明, 当x≤0.1 时, Cu掺杂仍可形成单相的钙钛矿结构; 当x>0.1时, 过量掺杂的Cu以CuO杂相存在. Cu掺杂可改善La1-xCuxMnO3催化剂对CO和CH4的催化氧化活性. 经700 ℃焙烧3 h制备的La0.9Cu0.1MnO3催化剂具有最高CO催化氧化活性(T100%=170 ℃), 该结果与CO催化氧化发光结果一致.而La0.95Cu0.05MnO3催化剂对CH4的催化氧化活性最高(T95%=705 ℃).     

β型聚丙烯注塑件的分层结构与力学性能

用X-射线衍射仪研究了不加和加成核剂形成不同晶型的三种聚丙烯注塑件的分层结晶结构,获得各层结晶度和β晶型含量(k_β)随皮芯距离的分布规律,测定了试件弯曲、拉伸和冲击性能。发现,纯等规聚丙烯试件主要含α晶型,皮层的结晶度和k_β低于芯层。加有α成核剂的试件仅含有α晶型,皮层的结晶度也低于芯层。加有β成核剂的试件主要含β晶型,皮层的结晶度和k_β值高于芯层。纯聚丙烯试件和β型为主的试件的分层结构中存在α晶和β晶间的转变。与α型聚丙烯相比,β型聚丙烯有较低的屈服强度,却有较高的抗张强度,显示很高的拉伸韧性和延展性,可明显提高室温以及玻璃化温度以下的低温抗冲击性能。     

CONVERSION OF METHANE AND CARBON DIOXIDE TO AROMATICS OVER CHROMIUM-BASED CATALYSTS:SELECTIVITY AND YIELD OF MAIN PRODUCTS

在８４０℃，０．５ＭＰａ，ＣＨ４／ＣＯ２摩尔比为１．４，接触时间（Ｗ／Ｆ）为０．７９ｈ·ｇ·Ｌ－ｌ的条件下，甲烷和二氧化碳在７．５ｗｔ％Ｃｒ／５．０ｗｔ％Ｎａ／ＳｉＯ２催化剂上共活化得到了４．８％的Ｃ２选择性，４８．７％的芳烃选择性及１．９％的芳烃收率。在钠修饰的铬基催化剂上，成功地一步实现了ＣＨ４和ＣＯ２转化为乙烯及中间物乙烯聚合为芳烃的过程     

阳离子交换树脂的有机催化进展

综述了聚苯乙烯型磺酸树脂、全氟磺酸树脂Nafion及崭新的Nafion／siO_2复 合催化剂在有机合成中应用的最新进展．     

Synthesis and Characterization of ZSM-5/β Co-Crystalline Zeolite

ZSM-5/β co-crystalline zeolites with different content of ZSM-5 have been synthesized by adding different amount of ZSM-5 to the synthetic system of β zeolite with NaAlO2, silica sol as the source of aluminum and silica, respectively, and TEA as the template under controlled condition of the synthesis. The ZSM-5/β co-crystalline zeolite was studied by XRD, SEM, BET and NH3-TPD. The reaction activity of toluene alkylation was investigated with a mixture of toluene-methanol as the feedstock in a pulse micro-reactor over the ZSM-5/β co-crystalline zeolite. It is found that ZSM-5/β co-crystalline zeolite has two kinds of zeolite structure including ZSM-5 and β zeolite, not in the form of a physical mixture. The pore structure of ZSM-5/β co-crystalline zeolites is different from that for β zeolite, ZSM-5 and their physical mixture. In addition, the peaks of both high and low temperature desorption of ammonia over the ZSM-5/β co-crystalline zeolite shift 23 ℃ to lower temperatures and the acid amount of its strong acid is 3% more than the physical mixture. So the ZSM-5/β co-crystalline zeolite produces the highest content of xylene, which is 10.4% higher than the physical mixture. And the ZSM-5/β co-crystalline zeolite has better selectivity for toluene alkylation and weaker de-methylation than β zeolite, ZSM-5 and their physical mixture.     

基于小波变换模极大法的聚乙烯催化剂表面分形分析

运用分形和小波相结合的方法研究负载型聚乙烯催化剂(简称催化剂)表面形态. 采用小波变换模极大(WTMM)法提取了催化剂表面多尺度边缘(细节)图像, 用分形和多重分形方法研究了各尺度边缘图像中边缘点的分布情况, 并用基于小波变换模极大的多重分形谱法讨论了催化剂边缘点奇异强度的分布状况. 研究结果表明, 催化剂的较小尺度边缘图像的分维和多重分形谱可以与催化剂的表面形态和活性进行较好的关联; 高活性催化剂的基于WTMM的多重分形谱的奇异强度跨度更宽, 拥有较多具有较高奇异强度的奇异点. 基于小波和分形对催化剂表面形态的研究, 发挥了小波和分形各自的优点, 为研究物体表面形态提供了思路.     

Ag/ZrO2催化剂上的1,2-丙二醇选择性气相氧化反应

采用浸渍法制备了一系列Ag/ZrO₂催化剂, 考察了Ag/ZrO₂催化剂对1,2-丙二醇选择性氧化合成丙酮醛反应的催化性能. 实验结果表明: 在原料气配比为V(N₂)∶V(O₂)＝300∶19, n(O₂)/n(alcohol)＝1.2, 反应物液时空速为3.2 g/(g•h), 反应温度为673 K时, 1,2-丙二醇选择性氧化合成丙酮醛反应的转化率为95.7%, 选择性为55.3%, 高于传统电解银催化剂. UV-Vis DRS和XPS的研究结果表明: 在Ag/ZrO₂催化剂上存在大量的Ag^＋和Ag_n^δ＋有利于促进催化活性的提高.