聚3-甲基噻吩及聚3-己基噻吩修饰钛酸盐纳米管的光电化学性能研究

采用水热法制备了钛酸盐纳米管, 并将钛酸盐纳米管制备成纳米结构电极进行光电化学研究. 钛酸盐纳米管产生阳极光电流, 具有n-型半导体特性. 结果表明, 聚3-甲基噻吩[poly(3-methylthiophene), PMeT]、聚3-己基噻吩[poly(3-hexylthiophene), P3HT]修饰钛酸盐纳米管后产生的光电流均较纯钛酸盐纳米管的光电流高, 且使产生光电流的波长向长波区移动. 钛酸盐纳米管/PMeT、钛酸盐纳米管/P3HT的光电转换效率分别达11.40%, 0.91%(未校正光子损失). 钛酸盐纳米管/PMeT的光电转换效率较钛酸盐纳米管/P3HT的光电转换效率高10.5%. 钛酸盐纳米管/PMeT、钛酸盐纳米管/P3HT中存在p-n异质结, 在一定条件下p-n异质结的存在有利于光生电子/空穴的分离.     

CuCl2掺杂聚苯胺催化合成苯甲醛1,2-丙二醇缩醛

缩醛是一类重要化合物,具有原料来源丰富、生产工艺简单、化学性质稳定等优点,近20年来作为新型香料在日用香精和食品香精中均有广泛应用[1-2]。根据酸催化机理,Lewis酸可增强羰基碳的正电性,有利亲核试剂的进攻。研究表明,不少无机盐都是这类反应的高效、高选择性的催化剂,又因为无机盐价廉、易得等优点,所以用其作为催化剂具有更加重要的实际意义。聚苯胺(PAn)以其独特的掺杂现象及良好的稳定性为催化载体的选择提供了新的途径[3-4]。若以PAn为载体,将具有催化活性的路易斯酸掺杂其中,可降低路易斯酸的流失量,并克服其易潮解、腐蚀设备…     

还原氮化温度对氮化铌纳米管组成、结构与电化学性能影响研究

以铌箔为基底,用阳极氧化法结合氨气还原氮化法制备出氮化铌纳米管,利用X射线衍射仪(XRD)、X射线光电子能谱(XPS)和扫描电镜(SEM)等结构表征手段和循环伏安法(CV)、充放电(GCD)和交流阻抗法(EIS)等电化学测试手段研究了还原氮化温度对纳米管的物相、形貌以及电化学性能的影响.结果表明,还原氮化后出现了氮化铌物相,以氧氮化铌固溶体形式存在,当还原氮化温度为700℃时,氮化铌纳米管阵列结构均匀,纳米管的孔内径约为35 nm,管壁厚度约为12 nm,纳米管长度约为1.5μm,样品中内在阻抗和电荷转移电阻较小,在电流密度为0.1 mA/cm2时,其比电容为400μF/cm2.     

PbSe/TiO2同轴异质结纳米管的制备及光催化性能

通过溶液法合成了PbSe/TiO2复合纳米管,并对其进行了微观形貌、晶体结构等的表征。结果表明,制得的样品是由PbSe和TiO2两种材料构成的复合材料,致密、均匀的TiO2薄膜包覆在PbSe纳米管表面。以氙灯为模拟光源,通过对甲基橙的降解研究了PbSe/TiO2复合纳米管的光催化性能。结果显示,PbSe与TiO2之间形成的异质结使PbSe/TiO2复合纳米管具有较高的光催化性能,比纯PbSe纳米管的催化降解率提高了约4.5倍。另外,对PbSe/TiO2复合纳米管光催化稳定性也进行了研究。     

聚苯胺／聚乙烯醇导电复合膜的制备及性质研究

用较简单的化学氧化现场吸附聚合法（ｉｎ－ｓｉｔｕｐｏｌｙｍｅｒｉｚａｔｉｏｎ）制得了聚苯胺（ＰＡｎ）／聚乙烯醇（ＰＶＡ）导电复合膜．该膜具有较好的导电性和机械性能；其电导率可达５．８ｓ／ｃｍ，拉伸强度达１３ＭＰａ，断裂伸长率为１１０％左右．本文讨论了制备的各种条件对复合膜导电性能及力学性能的影响、稳定性及电化学活性；并采用循环伏安曲线、扫描电镜（ＳＥＭ）、ＦＴＩＲ谱及元素分析对该复合膜的结构和性能进行了表征．     

活化条件对活性碳纳米管比表面积的影响

以KOH为活化剂, 研究了多壁碳纳米管在制备活性碳纳米管过程中四个重要影响因素: 活化剂用量、活化温度、活化时间和活化过程中保护气体的流速对所得活性碳纳米管BET比表面积的影响并解释了原因. 研究表明上述四个因素都会对活性碳纳米管的比表面积产生较大的影响, 其中活化剂用量的影响最大, 在研究范围内可引起比表面积增大约241 m²•g^-1. 在这四个影响因素中除活性碳纳米管的比表面积随活化温度的增加而不断增加外, 其他三个影响因素的变化都会使活性碳纳米管的比表面积出现最大值, 而且四个影响因素的改变, 都不改变活性碳纳米管的孔洞主要是中孔和大孔的特点.     

ELECTRORHEOLOGICAL PROPERTIES OF POLYANILINE/PUMICE COMPOSITE SUSPENSIONS

Electrorheological （ER） properties of polyaniline （PAni）, pumice and polyaniline/pumice composites （PAPC） were investigated. Polyaniline and PAni/pumice composite were prepared by oxidative polymerization. PAni/pumice particlesbased ER suspensions were prepared in silicone oil （SO）, and their ER behavior was investigated as a function of shear rate, electric field strength, concentration and temperature. Sedimentation stabilities of suspensions were determined. It has been found that ER activity of all the suspensions increases with increasing electric field strength, concentration and decreasing shear rate. It has shown that the suspensions have a typical shear thinning non-Newtonian viscoelastic behavior. Yield stress of composite suspensions increased linearly with increasing applied electric field strength and with concentrations of the particles. The effect of high temperature on ER activity of purrfice/silicone oil systems was also investigated.     

原位聚合沉积聚苯胺薄膜及其电致变色性能

采用原位聚合的方法,以水溶性高分子聚乙烯吡咯烷酮(PVP)为空间稳定剂,直接在玻璃基体表面聚合沉积导电聚苯胺(PANI)薄膜。用扫描电镜(SEM)、紫外可见光谱(UV-Vis)、四探针电导率测试仪和热重分析仪(TG)对聚苯胺膜结构及性能进行了表征。采用循环伏安法测试了薄膜的电致变色性。结果表明:盐酸掺杂聚苯胺薄膜呈翠绿色,薄膜厚115 nm,表面电导率为4.6×10-3S/cm。电致变色实验中聚苯胺电极电位在-6~ 6 V循环变化时,薄膜颜色在黄绿和蓝绿间可逆变化。电致变色前后聚苯胺薄膜的紫外可见吸收光谱表明,随着电极电位的降低,极化子峰发生红移,说明聚苯胺分子链中醌式结构单元被还原,聚苯胺薄膜质子化程度提高。     

导电聚苯胺/钙基膨润土复合材料的制备

采用插层聚合法制备了导电聚苯胺/钙基膨润土、聚苯胺/有机化膨润土复合材料.以电导率为考核指标,通过正交设计优化了苯胺的加入量、反应温度和反应时间等参数.结果表明,苯胺的加入量影响较显著,反应温度对聚苯胺/有机化膨润土复合材料影响较聚苯胺/钙基膨润土体系明显,反应时间的延长,有利于聚苯胺/有机化膨润土复合材料电导率的提高.聚苯胺/钙基膨润土复合材料制备的最佳工艺条件为:苯胺加入量为70%,反应温度为0℃,反应时间为6 h;聚苯胺/有机化膨润土复合材料制备的最佳工艺条件为:苯胺加入量为70%,反应温度为室温,反应时间为8 h.利用红外光谱(FT-IR)、X射线衍射(XRD)和四探针技术表征了材料的组成、结构和性能.结果表明:膨润土经有机化后,晶面间距增大较多;苯胺单体与钙基膨润土插层聚合后,膨润土晶面间距增大不多;苯胺单体与有机化膨润土复合后,破坏了膨润土的晶格结构,形成了混杂复合体系,电导率达10-3S.cm-1.