膦化聚2,6—二甲基1,4—苯醚负载钯催化剂的表征及其催化性能

报道了四种不同P/Pd摩尔比的膦化聚2,6-二甲基1,4-苯醚负载把催化剂的加氢和异构化性能;通过XPS、电镜和远红外对催化剂进行了表征;并考察了溶剂和温度对催化剂活性的影响.     

PREPARATION AND CHARACTERIZATION OF SHISH-KEBAB TYPE LIQUID CRYSTALLINE POLY（p-PHENYLENEVINYLENE）

Novel shish-kebab type liquid crystalline poly（p-phenylenevinylene） derivatives were synthesized by Stille coupling reaction from 2,5-bis[（4-n-alkoxyl）benzoyloxy]1,4-dibromobenzene （monomer l） and 1,2-bis（tributylstannyl） ethylene （monomer 2）. The polymers with alkoxy groups are soluble in common organic solvents and exhibit blue fluorescence. Both the cast film and the annealed film have large red-shifts in fluorescence spectra and show yellow fluorescence. The polymers with CN and NO2 groups show poor solubility and green fluorescence. All the polymers possess liquid crystalline smectic phases. The melting point （Tm） of the polymers decreases when the length of the alkoxy tails of the mesogenic units increases. The polymers are easily aligned under a magnetic field of 10 Tesla. It is found that the conjugated backbone and LC side chain are aligned perpendicular and parallel to the magnetic field, respectively. The polymers show optical dichroism in fluorescence spectra, suggesting that they are available for advance materials with linear optical polarization.     

聚-γ-N-(β-丁硫基乙基)胺丙基硅氧烷钯络合物的合成及其催化性能的研究

报导了聚－γ－Ｎ－（β－丁硫基乙基）胺丙基硅氧烷和氯化钯的反应，得到固载在二氧化硅上的聚－γ－Ｎ－（β－丁硫基乙基）胺丙基硅氧烷钯络合物，并用ＸＰＳ研究其结构．选用硝基苯、烯丙基环氧丙基醚、烯丙基苯基醚、丙烯腈、烯丙基苯、苯乙烯、环己烯及丁烯等８种底物进行催化加氢，以评价其催化活性．结果表明，该催化剂催化效果良好，并且有很好的稳定性．     

Synthesis and Crystal Structure of 3,3,6,6-Tetramethyl-N-hydroxy-9-ethyl-1,8-dioxo-1,2,3,4,5,6,7,8,9,10-decahydroacridine

1 INTRODUCTION 1,4-Dihydropyridines (1,4-DHPs) are well-knowncompounds because of their pharmacological pro-perty as calcium channel modulators[1, . The che- 2]mical modifications, such as the introduction of dif-ferent substituents[3, or heteroatoms[5], of the DHP 4]ring have allowed the expansion of researches onthe structure-activity relationship to gain new in-sights into the molecular interactions at the receptorlevel. In fact, it is well established th…     

聚偏氟乙烯取向薄膜的结晶形态

本文用小角激光散射法研究了聚偏氟乙烯薄膜在拉伸取向过程中晶体形态及结构的变化。拉伸使球晶形变为椭球,同时伴随着局部熔融与重结晶过程,散射图案由原来的四叶瓣发展为八叶瓣。红外测量及X-射线衍射分析表明,拉伸引起分子链构象改变,使晶型发生了转变。     

微波辐照下无皂阳离子聚(St-MMA)高分子纳米粒子的制备和表征

讨论了微波辐照下 ,以丙酮 水为分散介质 ,利用阳离子型自由基引发剂偶氮二异丁基脒盐酸盐(AIBA)引发苯乙烯 (St)和甲基丙烯酸甲酯 (MMA)共聚 ,合成出表面带正电荷的P(St MMA)共聚物纳米粒子 ,考察了丙酮用量、单体和引发剂浓度对纳米粒子粒径、粒径分布和乳液稳定性的影响 .结果表明 ,丙酮 水的体积比由 0增加到 1 2 6∶1时 ,粒子的平均水化半径从 12 2 2 1nm降低到 2 4 6 8nm ,粒径分布变宽 ,乳液抗电解质稳定性逐渐增强 ;增加引发剂和共聚单体MMA的浓度 ,粒子的水化半径逐渐减小 ,粒径分散系数增大 .     

FTIR-ATR技术研究聚氨酯类文物保护材料的光降解

Polyurethanes are one kind of relic protection materials commonly used. During artificial photo-ageing, three polyurethanes, HDI-based polyurethane, MDI-based polyurethane and TDI-based polyurethane, have been considered to undergo UV radiation. Photochemical degradation of the polyurethanes has been monitored by means of Fourier transform infrared spectroscopy with attenuated total reflection accessory （FTIR-ATR）. It was proved that the mechanism of the photochemical degradation of polyurethanes might be the scissions of carbamate （urethane） groups and the re-reactions of radical groups formed in the scission reactions. From the experiment results HDI-based polyurethane, an aliphatic diisocyanate, could be considered to be more suitably used as relic protection materials among these three polyurethanes for its ageing products with less color.     

疏水缔合型增稠剂聚(丙烯酰胺-丙烯酸高级酯)的合成及增稠性能研究

采用沉淀聚合法合成了聚（丙烯酰胺－丙烯酸十四酯），聚（丙烯酰胺－丙烯酸十六酯）和聚（丙烯酰胺－丙烯酸十八酯），重点讨论了共聚物中疏水基团数量及疏水基团链长对增稠性能的影响。采用凯达尔定氮法和动态热分析（DMTA）测定了共聚物的组成及玻璃化温度。     

乙烯-甲基丙烯酸共聚物离聚体在聚对苯二甲酸乙二酯中的相分离行为

聚对苯二甲酸乙二酯(PET)结晶速度很慢,通常加入成核剂来提高结晶速度。从专利文献来看,以离子聚合物为成核剂的例子也是很多的。离子聚合物与小分子成核剂的显著差别是:离子聚合物有一个很长的碳氢主链,其侧基为酸基,酸基被部分或全部地中和成盐。很明显,离子聚合物不象小分子成核剂那样能很好地分散在PET基体中,而是以独立的相存在。作为PET体系系列研究的继续,本文报道了离子聚合物Surlyn在PET中的相分离行为。     

TiO2与ZnO复合纳米结构电极的光电化学研究

利用尿素加压共沉淀法以Ti(SO4)2与Zn(NO3)2为原料制备了TiO2-ZnO复合纳米粒子, 其纳米结构电极的光电化学研究结果表明, 反应物摩尔比为3∶1, 于530 ℃煅烧制备的复合纳米结构电极的光电转换效率最高. 对吸附染料RuL2(SCN)2∶2TBA的纳米结构TiO2和各种复合纳米粒子的纳米结构电极进行光电研究的结果表明, 染料对各纳米结构电极都起到了敏化作用, 其中也是由反应物摩尔比为3∶1, 于530 ℃煅烧制备的纳米结构电极的光电转换效率最高. 对聚3-甲基噻吩修饰的纳米结构TiO2和摩尔比为3∶1, 于530 ℃煅烧的复合纳米粒子构成的纳米结构电极进行光电性能研究, 结果表明, 聚3-甲基噻吩与半导体纳米粒子之间存在p-n结, 在一定条件下p-n结的存在有利于光生电子/空穴的分离, 从而提高了光电转化效率.