聚丙烯基纳米碳纤维复合材料结晶行为研究

采用示差扫描量热法(DSC)研究了纳米碳纤维对PP／CNF复合材料中PP结晶行为的影响。结果表明：纳米碳纤雏可提高PP的结晶温度，但略降低其结晶速率和结晶度。提高纳米碳纤雏含量或减小纳米碳纤雏直径，PP结晶行为的上述变化更为明显，但结晶速率随纳米碳纤维含量出现先减小后增大的趋势。     

稀土添加剂对烃类水蒸汽重整镍催化剂性能的影响——水蒸汽吸附的TPD研究

用程序升温脱附技术,研究了添加稀土的烃类水蒸汽重整催化剂(Ni/α-Al_2O_3)对水蒸汽的吸附性能,同未加稀土的镍催化剂作了对比。结果表明,加有稀土的镍催化剂对水蒸汽的吸附能力主要是稀土的贡献。还原态催化剂对水蒸汽的吸附量比相应的氧化态多1.4倍。发现催化剂对水蒸汽的吸附能力不仅取决于浸渍方式,而且同稀土含量有关。当稀土含量较多时,催化剂表面上呈现出三个能量不同的吸附位。稀土含量少于1.3%时。对提高催化剂吸附水蒸汽的能力已作用不大。含稀土的镍催化剂吸附水蒸汽的能力大,正是其抗结炭性能耐硫性能好的原因。     

Preparation of Nanoelectrode Ensembles by Assembly of Nano—Silver Colloid on Gold Surface

A novel method for preparing silver nanoelectrode ensembles(SNEEs) and gold nanoelectrode ensembles (GNEEs) has been developed. Silver colloid particles were first absorbed to the gold electrode surface to form a monolayer silver colloid. N-hexadecyl nercaptan was then assembled on the electrode to form a thoil monolayer on which hydrophilic ions cannot be transfered. The SNEEs was prepared by removing thiol from silver colloid surface through applying and AC voltage with increasing frequency at 0.20V(vs.SCE). Finally,GNEEs was obtained by immersing a SNEEs into 6 mol/L HNO3 to remove the silver colloid particles. By comparison with other methods such as template method ect., this method enjoys some advantages of lower resistance, same diameter,easy preparation,controllable size and density.     

结合电生孔技术的抗体-纳米TiO2靶向光敏杀癌细胞

报道了用免疫、电生孔和纳米TiO₂光催化组合技术进行杀伤结肠癌LoVo细胞的研究. 先把结合LoVo细胞表面CEA抗原的单克隆抗CEA抗体吸附在纳米TiO₂微粒表面, 抗体-纳米TiO₂复合微粒就会自动吸附到LoVo细胞的表面, 然后用电脉冲法使LoVo癌细胞的细胞膜上产生小孔, 促使纳米TiO₂微粒进入癌细胞内部. 最后在紫外光照射下使TiO₂纳米粒子在癌细胞内部发生光催化氧化作用, 杀伤癌细胞. 结果表明, 这种组合技术具有很高的杀癌细胞能力. 在仅含3.12 μg/mL抗体-纳米TiO₂的细胞培养液内和强度为4 mW/cm²的紫外光照射下, 可在30 min内将所有LoVo癌细胞杀死. 这种技术对LoVo癌细胞的杀伤力远高于对不表达CEA抗原的人正常TE353.sk细胞的杀伤力, 显示了组合技术杀癌细胞的高选择性. 因此, 这种组合技术有望成为治疗癌症的新方法, 值得进一步探索.     

纳米碳酸锌的制备和热分解动力学参数的测定

Nanosized zinc carbonate was prepared in the droplet of nano-reactor based on microemusion. The influences of the concentration of the surfactant and reactant on the diameter of nanoparticles were studied and the kinetic pa-rameters of thermal decomposition reaction were determined. It can be shown from experimental results， the di-ameter of the droplet in the microemulsion which have dissolved reactant zinc nitrate and sal volatile is between 4.9nm and 7.7nm， 6.2nm and 12.4nm， respectively. Nanosized zinc carbonate prepared by the method of mi-croemusion has shown good dispersion， narrow distribution and light agglomeration. The particle size of nanosized zinc carbonate is between 5nm and 40nm， and its kinetic parameters of thermal decomposition reaction-activation energy E and reaction order n are 110kJ·mol^-1 and 0.9， respectively.     

纳米氧化铜的制备及常温脱硫效能研究

采用硝酸铜为原料、氢氧化钠溶液为沉淀剂、使用体积比为1∶1的乙醇-水溶液为分散剂的直接沉淀法制备，通过改变工艺条件得到了三种纳米氧化铜产品，平均粒径分别为25.63，10.74和7.57 nm。采用TG-DTA、FIR、XRD和TEM等对纳米氧化铜进行表征。对产品的常温脱硫活性进行了穿透试验，并与已开发的其他常温精脱硫产品进行了比较，结果表明纳米氧化铜应用于H₂S脱硫，可在常温条件下具有优异的脱硫活性，对H₂S的脱除精度可以达到0.05 mg·m^-3以下。经过优选，产品在3 000 h^-1空速下穿透硫容达到25.3%，高于同类型的其他脱硫剂产品。     

镍 钴 钯 铁2—（二苯基膦基）吡啶配合物的合成及其催化羰基化反应

众所周知,铑催化剂是醇类羰基化的有效催化剂,但是铑价格昂贵且对设备有腐蚀性,因此,寻找出对醇类羰基化催化活性好的非贵金属催化剂,对醇类羰化的工业化有十分重要的意义。 本文在温和条件下,合成了四种含有相同配体(Ph_2PPy)不同金属的有机配合物(金属基分别为Ni、Co、Pd、Fe),并探索了它们对乙醇羰基化反应的催化活性。     

方波伏安法测定镍铜合金中的镍含量

在0.01mol·L-1的氨水-氯化铵缓冲溶液(pH 9.3)中,镍(Ⅱ)于-1.25V(vs.SCE)出现一灵敏的方波伏安峰。镍(Ⅱ)浓度在1.5×10-6～1.0×10-4mol·L-1与伏安峰高呈线性关系,线性方程为ip(μA)=2.1870+0.6328c(μmol·L-1),相关系数为0.9991。方法的标准偏差为0.7％。该法应用于镍铜合金样品中镍的测定,结果满意。