一种新型侧链液晶聚合物的喇曼光谱研究

The Raman scattering on a novel liquid crystal side chain polymer, poly-2,5-bis (p-meth-oxybenzoyloxy) styrene, has been performed. We observed that the characteristic Raman sp-ctra of the vinyl group in the monomer changed much deeply in the polymer, especially for the Raman line correponding to the C=C of the vinyl group which disappeared completly in the polymer. Contrast with that, the Raman spetra of the rest group did not present any substantial difference between the monomer and the polymer. These experimental facts show-ed that the vinyl group of the monomer was tranfered to the polymeric backbone while the chemical structure of the mesogenic unit in the monomer remained after the polymerization,and also conformed that it was successful in the synthesis of a liquid crystal side chain plymer without a flexible spacer between the mesomorphic unit and the molecular main chain.     

水相湿法改性纳米碳酸钙表面性质的研究

用特定的表面改性剂在水相中对纳米碳酸钙的悬浮液进行了湿法改性。红外光谱和热失重分析证明,改性剂与碳酸钙之间以化学键结合;沉降体积和接触角的测定结果说明改性粒子在液体石蜡中的润湿性和疏水性得到了提高;透射电子显微镜照片显示改性粒子在液体石蜡中有更好的分散性;体系粘度实验表明改性粒子与液体石蜡之间有较好的相容性。     

Synthesis of polypiperazine-amide thin-film membrane on PPESK hollow fiber UF membrane

A new interfacial polymerization (IP) procedure is developed in order to synthesize polypiperazine-amide thin-film membrane on the inner surface of poly(phthalazinone ether sulfone ketone) (PPESK) hollow fiber ultrafiltration (UF) membrane.A hollow fiber composite membrane with good performance was prepared and studied by FT-IR and scanning electron microscopy.     

表面包覆改性对纳米CeO2分散性的影响

了改善纳米CeO2在Zn-Al类共晶合金中的分散性,采用超声液相包覆法对纳米CeO2进行表面活性剂表面包覆改性,并用AES测定了包覆层的厚度,用TEM研究了CeO2的团聚状况,用TGA分析了有机物包覆层的炭化温度范围,最后用FE-SEM观察了CeO2在复合材料中的分散情况。结果表明,包覆在纳米CeO2表面的厚度约为20 nm的表面活性剂层提高了微粒的分散性,而且该包覆层在495℃时已经炭化。热力学计算的结果也表明,炭化层能与氧化膜反应,该反应提高了CeO2与基体间的润湿性,并使其均匀分布在基体合金中。     

硼酸酯偶联剂的合成与表征

通过分子结构设计，合成了一种氮一硼内配位结构的硼酸酯偶联剂，解决了硼酸酯水解稳定性差的问题，同时分子结构中含有氨基、丁氧基等活性基团。用傅立叶变换红外光谱对硼酸酯进行了结构表征，讨论了原料配比、合成工艺等对硼酸酯收率及反应速率的影响，并通过实验确定了最佳配方及工艺。对硼酸酯的物理性能、溶解性、水解稳定性及对硼酸铝晶须的表面处理效果进行了表征。结果表明：合成的硼酸酯偶联剂由于具有氮-硼内配位作用，表现出优良的水解稳定性，并且硼酸酯偶联剂对硼酸铝晶须具有良好的表面改性效果。     

无机层状复合氢氧化物中顺铂-DNA模型分子的选择性插入

药物分子的选择性包裹和控制释放是药物研究领域中具有挑战性的研究方向。本文研究表明:顺铂-DNA模型分子cis-[Pt(NH₃)₂(5′-GMP)₂](5′-GMP 5′-单磷酸鸟苷)可插入无机层状复合氢氧化物[Zn_0.68Al_0.32(OH)₂](NO₃)_0.32·mH₂O。但另一种层状复合氢氧化物[LiAl₂(OH)₆]Cl·H₂O由于其阳离子层中正电荷密度较高、阳离子层与层间阴离子之间静电作用较强,因而顺铂-DNA模型分子不能通过离子交换方式插入其层间。光谱数据证实插入层间的顺铂-DNA模型分子结构不变。这可能为铂-DNA分子的传递提供新的方法。     

Fe-Ni-B-O纳米合金的合成及其催化制氢性能的研究

Preparation and catalytic performance of Fe-Ni-B-O nano-alloy having crystal-palpus structure has been studied. Black powder was synthesized by reducing mixture solution of Fe²⁺, Ni²⁺ with KBH₄ as reducing agent and polyethylene glycol as dispersant. Fe-Ni-B-O nano-alloy of crystal-palpus structure was obtained after hydrogen reduction of black powder. TEM shows that crystal-palpus length is 200～400 nm, diameter is 2～4 nm. The analytic results indicate that the total content of Fe and Ni is 86.6%, B is 5.08%. The alloy exhibits excellent catalytic performance. Hydrogen generation rate can approach 100% especially when pH is 8.     

在位分散聚合聚甲基丙烯酸甲酯/二氧化硅纳米复合材料研究

应用在位分散聚合方法制备了分散相粒径介于１３０ｎｍ左右的聚甲基丙烯酸甲酯／二氧化硅ＰＭＭＡ／ＳｉＯ２纳米复合材料，并利用ＳＥＭ，ＤＭＡ，ＴＧＡ等手段研究了该体系的性能．结果表明，经表面处理的ＳｉＯ２无机填料在复合材料基体中分散均匀，界面粘结好．ＳｉＯ２填充粒子的用量对基体的热稳定性，动态力学行为，光学行为以及拉伸强度，弹性模量，断裂伸长率等力学性能都有较大影响     

钙钛矿型La_((1 x)/2)Sr_((1-x)/2)Co_(1-x)Cu_xO_3催化CO氧化活性与表征

研究了钙钛矿型LaSrCoCu_xO_3催化剂对CO氧化反应的催化活性及其表面氧的催化作用．结果表明，x＝0．4的催化剂对CO氧化具有最高催化活性，常压及本实验条件下CO完全氧化的最低温度为168℃；催化剂均为氧缺陷化合物，吸附于表面晶格氧缺陷上的吸附氧是CO氧化反应的活性氧物种；并发现催化剂中存在有非常价态的C04 ，认为CO氧化反应是通过吸附氧调变Co3 和Co4 价态而进行．     

导电性聚西佛碱的研究：Ⅰ含硫聚西佛碱的合成,性能及表征

采用对氯苯甲醛和联苯二胺为原料,合成了4,4′-二氯代苄叉联苯胺,发现该化合物具有热致液晶性。利用所合成的二氯代化合物与硫化钠在醋酸锂催化下缩取得得到了含硫聚西佛碱探讨了高分子量含硫聚西佛碱的合成方法。测出该含硫聚西佛碱具有3.4×10~(-11)S/cm本征导电率。使用红外光谱、元素分析等方法表征了所合成的聚合物。