Pt3Co核-Pt壳型纳米粒子的制备及磁性

Pt₃Co alloy nanoparticles were prepared by the reduction of H₂PtCl₆ and Co(OOCCH₃)₂ using NaBH₄ as a reducing agent. The Pt₃Co core-Pt shell nanoparticles (Pt₃Co@Pt) were synthesized using hydrogen absorption reduction and characterized by plasma-atomic emission spectrometry (ICP), transmission electron microscopy (TEM), X-ray diffraction (XRD) and SQUID magnetometer. The results show that average size of Pt₃Co@Pt nanoparticles is 3.6 nm with a standard deviation of 0.9 nm. Heating Pt₃Co nanoparticles in air at 700 ℃ for 1 h, Co in Pt₃Co nanoparticles was oxidized to Co₃O₄ and CoO; while no oxidation tendency was detected for Pt₃Co@Pt nanoparticles. The crystallize structure of Pt₃Co@Pt changed from the face centered cube (fcc) to the face centered tetragonal (fct) after the heating treatment. The coercivity of the heated Pt₃Co@Pt reached to 276 Oe at room temperature.     

纤维素基磁性聚偕胺肟树脂的研究——循环吸溴中吸附与还原能力的变化

研究了酸式纤维素基磁性聚偕胺肟树脂（ＡＭＡＯ）在循环吸溴过程中吸附容量和还原能力的变化，发现原树脂的吸溴初速和溴的还原率比再生树脂高一倍以上，但第一次和第二次再生树脂的吸附速度和还原效率几乎相同，暗示着树脂吸溴后基本结构已发生了彻底的变化．树脂在循环使用时吸溴容量变化不大而溴的还原量却显著降低，表明ＡＭＡＯ作为吸溴剂有较高的实用价值．     

探针反应和FTIR法研究Pt与L型沸石的相互作用

探针反应和ＦＴＩＲ法研究Ｐｔ与Ｌ型沸石的相互作用董家禄,朱建华,须沁华,张婕,刘大壮（南京大学化学系,南京,２１０００８）（郑州工学院化工系,郑州,４５０００２）关键词Ｐｔ／Ｌ沸石,沸石催化剂,异丙醇分解反应,Ｐｔ－载体相互作用Ｐｔ的分散度和电子状态...     

具有非正规自旋态的氮氧自由基桥联双镍配合物的合成,…

合成了４种氮氧自由基桥联的五氟丙酸镍双核配合物［Ｎｉ（ｐｒｐｒ）２］２ＮＩＴＲ．ｎＨ２Ｏ对该配合物进行了元素分析和热重－热分析，测定了红外光谱、紫外－可见光谱、电子顺磁共振和摩尔导，讨论了配合物的结构，测量了［Ｎｉ（ｐｆｐｒ）２］ＺＮＩＴｐｈＣｌ．４Ｈ２Ｏ和［Ｎｉ（ｐｆｐｒ）２］ＺＮＩＴＰｈＯＭｅ．４Ｈ２Ｏ的变温磁化率（４－３００Ｋ），表明配合物具有非正规自旋态的Ｎｉ（Ⅱ）－Ｃｕ（Ⅱ）三核体系的地     

纳米磁性液体对多元多相体系结晶特性的影响

以HCFC141b气体水合物结晶生成体系为对象,通过实验研究了磁场作用下纳米磁性液体对多元多相体系结晶生成特性的影响.重点研究了互不相容的水相与HCFC141b液相间、水相与气相(水蒸汽与HCFC141b蒸气)间的质量传递现象.结果发现,在旋转磁场作用下,纳米磁性液体能显著增强相间的质量传递和热量传递,使得结晶生成性能包括生成温度、生成速率等得到很大的提高.     

由Mg-Fe(Ⅱ)-Fe(Ⅲ)LDH层状前体制备MgFe2O4尖晶石的研究

提出了一种由层状前体合成单一晶相镁铁尖晶石的新方法，首先对Mg-Fe(Ⅱ)- Fe(Ⅲ)水滑石的制备进行了系统研究，成功合成了Mg^2+/Fe^2+/Fe^3+摩尔比分别 为1／2／1，4／5／3，2／1／1的系列水滑石层状前体，结果表明在以上三种投料 比下均可制备出晶型较好的水滑石层状前体，并探讨了合成条件对晶体结构的影响 规律。在此基础上，利用X射线衍射、振动样品磁强计和穆斯堡尔谱等手段研究了 层状前体焙烧产物的结构、组成、磁性及微观信息，研究表明当 Mg^2+/Fe^2+/Fe^3+投料摩尔比为2／1／1时，焙烧层状前体可得到晶相单一的尖晶 石型铁氧体。     

R2Fe17CNx的结构和磁性

采用适当的热处理,使碳原子和氮原子先后进入到R_2Fe(17)的结构中去。利用X射线折射和磁测量技术研究了R_2Fe_(17)CN_x的晶体结构和内禀磁性。碳、氮的加入使晶胞体和膨胀、居里温度升高、饱和磁矩增大,并加强了稀土晶位的轴各向异性。     

Formation of SnO2 Nanoparticles on External Surface of NaY Zeolite

Tin dioxide nanoparticles of 5 nm in size were prepared on NaY zeolite external surface by impregnation of SnCl2 solution and subsequent calcination at 623 K. A SnO2-NaY based chemical sensor for detecting H2 was demonstrated.     

利用DPN技术直接构建磁性纳米图形

在纳米尺度下构建有序的磁性模板和图形是当前的研究热点之一 [1,2 ] .这种模板在生物样品的分离[1] 、磁电子学研究和信息存储 [2 ] 等领域具有重要意义 .目前 ,光刻 [3] 、微触点印刷 [4 ] 和自组装 [5] 等多项技术已被用来构建各种纳米模板 .1 999年 ,美国西北大学 Mirkin小组 [6 ]发明的 Dip- pen纳米刻蚀技术 (简称 DPN技术 )更在可控组装方面显示出巨大优越性 .这项技术是在一定驱动力作用下 ,使吸附在原子力显微镜 ( AFM)针尖上的分子“墨水”逐渐转移到基底表面上 ,实现纳米模板的可控构建 .与传统技术相比 ,DPN技术可在纳米尺…     

一种新型共生沸石(T-L)的合成与表征

在Na₂O-K₂O-Al₂O₃-SiO₂-H₂O体系中水热合成了一种新型的共生沸石, 它由L型沸石生长在T型沸石的一端而形成, 称之为T-L型沸石. 通过XRD, SEM, TEM, EDX, IR等手段对其进行了初步的表征. SEM相片表明这种沸石具有特殊的铆钉状外形; 在TEM相片上可以清楚地看到L型沸石的大孔道, 此孔道与L型沸石的表面垂直. 通过EDX的数据计算发现共生沸石的两相有不同的骨架硅铝比: T型沸石部分Si/Al＝3.71, L型沸石部分Si/Al＝3.41. 在该样品中B酸大于L酸.