Ti—Si沸石表面吸附物种的TPSR—TPD研究

氯丙烯在不同催化剂表面上吸附的ＴＰＤ结果表明在ＴＳ－１上有三重附峰，而在ＴｉＯ２／Ｓｉｌｉｃａｌｉｔｅ上仅有单峰，Ｈ２Ｏ２或分子Ｏ２在催化剂表面吸附后，在脱附物种中可用质谱检测到原子Ｏ（１６）物种；说明Ｈ２Ｏ２或分子Ｏ２在样品表面存在解离吸附；并发现解离子分子Ｏ２的活性很低，ＴＳ－１能同时吸附内烯和Ｈ２Ｏ２，而在ＳｉＯ２／Ｓｉｌｉｃａｌｉｔｅ表面的吸附却与吸附顺序有关，环氧化活性顺序如下：ＴＳ－１     

A Two-Dimensional Photonic Crystal Slab Mirror with Silicon on Insulator for Wavelength 1.3μm

A concrete two-dimensional photonic crystal slab with triangular lattice used as a mirror for the light at wavelength 1.3μm with a silicon-on-insulator （SOI） substrate is designed by the three-dimensional plane wave expansion method. For TE-like modes, the bandgap in the Г-K direction is from 1087nm to 1559nm. The central wavelength in the bandgap is about 1.3μm, hence the incident light at wavelength 1.3μm will be strongly reflected. Experimentally, such a photonic crystal slab is fabricated on an SOI substrate by the combination of EBL and ICP etching. The measurement of its transmission characteristics shows the bandgap edge in a longer wavelength is about 1540 nm. The little discrepancy between the experimental data and the theoretical values is mainly due to the size discrepancy of the fabricated air holes.     

ZK—4、NaANaHS3种沸石的铝化

用高温气－固相置换法对ZK－4、NaANaHS3种沸石进行铝化。组成分析、尾气分析、X射线衍射、晶体形貌分析、红外光谱和^29Si高分辨魔角固体核磁结果表明，3种低硅铝比沸石铝化后骨架可能存在Al-O-Al键。     

圆形振动膜ZnO压电微传声器的研制

本文介绍了一种新型圆形振动膜ZnO压电微传声器的制备，并对传声器制备的工艺过程进行了较为详细的描述。圆形振动膜的压电传卢器与以前方形振动膜结构设计相比，较大幅度提高了传声器的灵敏度和成品率，灵敏度达到-70dB（相对于1V／Pa），成品率达到80％。     

纳米级氧化铁的合成及其对六价铬的吸附性能研究

采用溶胶-凝胶法合成了纳米氧化铁,研究了合成条件,并采用TEM对产品进行了表征,测得产品的平均粒径为20-30nm.研究了纳米级氧化铁对Cr（Ⅵ）的吸附.在pH=3.0,吸附比为3.5×10-6:1×10-2（g/g）时,平均吸附效率为95.98％,最大吸附量为398.3μg Cr（Ⅵ）/g.采用2mol/LNaOH可完全洗脱纳米氧化铁所吸附的Cr（Ⅵ）,测定了回收后的纳米氧化铁对Cr（Ⅵ）的吸附效率,结果表明纳米级氧化铁可循环使用,这将为环境污水中Cr（Ⅵ）的治理及研究纳米材料的吸附行为提供参考.     

含稀土锰系氧化物的磁性和氧吸附性

比磁化率(x)和顺磁共振谱数据测定表明,含9种不同稀土的复合锰系氧化物Ln_(0.7)Sr_(0.3)MnO_3(Ln=Ce、Pr、Nd、Sm、Gd、Tb、Dy、Ho和Er)均为顺磁性物质,而La_(0.7)Sr_(0.3)MNO_3具有铁磁性。在200℃,80mT外磁场下,上述样品的氧吸附量(M)均有不同程度的提高。将比磁化率(x)~(2/3)与比表面(As)的乘积对氧吸附量变化值(ΔM)作图,得到以f电子数=7为分界的两分组线性图,并对此进行了讨论。