最有效的相容剂是两嵌段还是多嵌段聚合物？

采用Monte Carlo模拟方法研究了多嵌段聚合物在A／B／嵌段聚合物三组份体系作为相容剂使用的有效性．占总体积19％的A组份在体系中为分散相．模拟结果显示了两嵌段和多嵌段聚合物在界面上的聚集行为,以及如何影响这个不相容体系的相形为．两嵌段聚合物趋于直立在相界面上,而多嵌段聚合物更容易横跨在相界面上并占据较大的界面积．从而导致多嵌段聚合物更有效的阻止体系相分离的发生．     

离子辐照引起的金属／绝缘体界面混合与相变研究

载能离子穿过固体界面引起界面原子迁移使界面原子混合和物质成分变化，从而导致界面发生材料相变。简要介绍了载能离子辐照引起金属／绝缘体界面混合效应及相变现象的主要实验研究进展、低能离子和高能离子辐照引起金属／绝缘体界面现象差异，并对离子辐照引起界面混合及相变的机制进行了初步探讨。When penetrating an interface between two kind of solids, energetic ions can induce atomic diffusion at both sides of the interface and then result in intermixing, atom re-distribution or composition change, as well as phase transformation. Main progress on the study of intermixing and phase change at metal/insulator interface induced by energetic ion irradiations, the difference of phenomena occurred at metal/insulator interfaces induced by high-and low-energy ions were briefly reviewed. Furthermore, the possible mechanisms related to intermixing and phase change at metal/insulator interface produced by energetic ion irradiations were also discussed in short words.     

表面活性剂对均相沉淀法制备单晶Ce2O(CO3)2￠H2O微粉形貌及 形成机理的影响

在尿素及硝酸铈的混合溶液中分别加入表面活性剂CTAB、 PEG19000、OP-10,利用均相沉淀法合成了不同形貌的CeO2超细前驱体Ce2O(COa)2·H2O,采用X射线衍射及透射电子显微镜等测试手段,对产品的物相和形貌进行了表征．实验结果表明,所得产品均为斜方晶系的单晶Ce2O(CO3)2·H2O,且表面活性剂的加入使晶体的晶化程度明显提高;添加不同的表面活性剂得到不同形貌尺寸的产物: 阳离子型表面活性剂CTAB对Ce2O(CO3)2·H2O晶体的形貌影响不大,所得产物尺寸变小,且分散性得到一定的改善;非离子型表面活性剂对所得产物的形貌影响显著．加入PEG19000和OP-10分别得到了形状排列有序的、尺寸较均匀的、较规则无团聚的微米棒及具有紧密结合中心的发散状的花样微粒．不同形貌前驱体的形成与晶粒形成生长机理的改变有关．     

化合物半导体-绝缘体界面的界面态(续)

 三、界面态连续体的动态响应和分布多年来的大量研究结果表明把界面态处理为局域在半导体界面平面处的经典理论完全不能够解释化合物半导体-绝缘体界面的行为特点,从而使人们逐渐认识到界面态的空间分布特征.图3为半导体界面的能带结构示意图.在实际的I-S界面上,界面态是在绝缘体-半导体界面附近,在能量上和空间上的连续分布体(如图中点所示). 这里以n型半导体为例,通过绝缘体中的界面态对电子的捕获和发射过程说明界面态动态响应的特点.由于势垒△Ec的存在,空间分布的界面态与电子的作用只能依介量子力学的隧道效应得以进行.     

电沉积n—CdSe在多硫溶液界面上的电荷转移机理

通过测定平带电位,澄清了OH~-离子在CdSe电极上的吸附情况,发现在S、S~(2-)、OH~-溶液中S~(2-)离子优先吸附,结合旋转环盘电极测量,证明n-CdSe电极在多硫溶液界面上的电荷转移过程。     

E*-酉范畴逆半群的结构

本文通过定义本原逆半群在集合上的部分作用及其整体化,给出了E*-酉范畴逆半群的结构．     

In Situ Observation of Skeletal Shape Transition during BaB2O4 Crystal Growth in High-Temperature Solution

The transition from a fiat solid-liquid interface to a skeletal shape during BaB2O4 （BBO） single crystal growth in Li2B4O7 flux is observed in real time by an optical high-temperature in-situ observation system. The movement of crystal step is also investigated. The observation results demonstrate that the steps propagate along and parallel to the fiat interface when the crystal size is small. Nevertheless, they will ‘bend＇ close to the face centre if the crystal size becomes greater. Atomic force microscopy reveals that more deposition places near the face centre give rise to the bending of advancing steps and thus the formation of a vicinal interface structure. Measurements of step velocity show that the velocity keeps nearly constant at different moments for one specific step, whereas the step on a newly formed layer advanced faster than that on a previously formed one when the crystal size is larger than 210μm or so. Thus interracial morphological instability occurs and a skeletal interface is obtained.     

采用热处理方法提高MEH-PPV单层聚合物有机发光二极管发光性能的研究

对以MEH－PPV为发光层的单层聚合物有机发光二极管（OLED）器件在最佳条件下进行真空热处理，并用金相显微镜观察施加电压后器件的阴极表面形貌。发现处理后的器件阴极表面的气泡及黑斑明显减少。器件的发光性能显著提高。与未经处理的器件相比，最大相对发光强度提高了一个数量级、启亮电压降低了2．0V，半寿命提高了12．7倍。初步分析表明热处理方法提高器件发光性能的主要原因在于有效地减少了器件在工作过程中由于焦耳热产生的某些气体，从而减少阴极表面气泡及黑斑的出现，另一方面，热处理方法也增强了有机发光层与阴极接触界面的结合力，提高电子注入水平。