环糊精-六次甲基四胺超分子络合物电化学研究及应用

在0.05 mol/L KCl底液中,β-环糊精(β-CD)-六次甲基四胺超分子络合物在2.5次微分极谱仪上于-0.78V(vs.SCE)处产生吸附还原波,峰形对称且稳定,其峰电流与六次甲基四胺浓度在4.0×10-4-1.0×10～mol/L之间呈良好线性关系;检出限为1.5×10-4mol/L。应用该法测定了有机工业产品六次甲基四胺,并与传统方法进行了比较,结果令人满意。对超分子络合物电化学性质及分子识别机理进行了探讨。     

SrTi0.9M0.1O3-δ钙钛矿型氧化物催化剂甲烷氧化偶联反应性能的研究

The structure and catalytic properties of SrTi_0.9M_0.1O_3-δ (M=Mg，Al， Zr) perovskite-type catalysts for ox-idative coupling of methane (OCM) have been studied by using X-ray diffraction (XRD)，X-ray photoelectron spectroscopy (XPS) and temperature-programmed desorption of oxygen(O₂-TPD) methods. It has been shown that doping the cations of lower valence (e.g. Mg²⁺， Al³⁺) to the B site of SrTi_0.9M_0.1O_3-δ perovskite-type catalysts results in the higher content of adsorbed oxygen species on the surface of catalysts and thus higher C₂-selectivity for OCM reaction. It is suggested that the oxygen vacancies of SrTi_0.9M_0.1O_3-δ (M=Mg， Al， Zr) perovskite-type catalysts are the sites responsible for oxygen activation， and the adsorbed oxygen species on the surface of SrTi_0.9M_0.1O_3-δ catalysts are the main active species for OCM reaction.     

The Synthesis of Bis（carboxyalkylmethyl） Diselenides by Selenium Transfer Reaction of Aryl Selenoamides

Aryl selenoamides react smoothly with a-haloacetic acid in various alcohol to givecorresponding bis(carboxyalkylmethyl) diselenides in good yields.     

MMI作为铜的盐酸酸洗缓蚀剂作用机理的研究

用失重法研究了N-甲基-2-巯基咪唑（MMI）在5％盐酸中对铜的酸洗缓蚀性能.探讨了温度和MMI浓度对缓蚀效果的影响，从中得出了MMI在铜表面的吸附等温式，计算了吸附热及MMI的加入对铜在盐酸中腐蚀反应活化能的影响，进而探讨了MMI对铜缓蚀作用的机理.结果表明， 30 ℃下，在5％盐酸中，当MMI的浓度在3 mmol•L－1和8 mmol•L－1之间时,缓蚀率随MMI浓度的增加而迅速增加，当浓度达到8 mmol•L－1时，缓蚀率趋于定值，而当浓度小于3 mmol•L－1时， MMI的加入会加速铜的腐蚀；吸附在铜表面的MMI分子间的作用力整体表现为引力； MMI在铜表面的吸附是吸热反应； MMI的加入降低了铜的腐蚀反应活化能.     

溴酸钾氧化亮绿SF催化光度法测定痕量亚硝酸根

本文基于亚硝酸根对溴酸钾氧化亮绿ＳＦ而使其褪色所起的催化作用，建立了高灵敏度催化吸光光度法测定痕量亚硝酸根的新方法，测定范围为０．０５－２０ｎｇ／ｍｌ，用于不同水样中亚硝酸根的测定，获得了满意结果。     

硫酸溶液中Ag+离子对Mn2+离子阳极氧化的催化作用

Anodic oxidation of Mn2+ and Ag+ ions and anodic oxidation of Mn2+ ion on platinum electrode in H2SO4 solution catalyzed by Ag+ ion are studied by using RRDE and triangle voltammetry techniques. Mn2+ ion is oxidized on the anode surface with adsorped OH group to form a certain compound containing Mn3+, which causes Mn2+difficult to be oxidized directly on anode. Near the potential of oxygen evolution from H2O decomposition, Ag+ ion is oxidized to form Ag2+ ion. This is the main reaction on anode because of its reversability. At higher potential silver oxide is formed on the anode. The oxide catalyzes the decomposition of H2O strongly. The anodic oxidation of Mn2+ion catalyzed by Ag+ takes place and Ag2+ ion and silver oxide are no longer the product of Ag+ anodic oxidation when Mn2+ exists in solution at the potential for Ag+ anodic oxidation. It is confirmed that the catalysis reaction is homogeneous and very fast.     

双金属氰化物配合物的制备、表征及催化性能

 制备了基于钴氰化锌的双金属氰化物配合物（DMC）催化剂，并\r\n用元素分析、X射线衍射和红外光谱等手段进行了表征，考察了催化剂\r\n的结构与组成对其催化活性的影响以及该催化体系催化环氧烷烃开环聚\r\n合的特点．结果表明，含ZnCl2和叔丁醇的非晶态DMC催化剂具有最高的\r\n催化活性．该催化体系使聚合物的分子量可控，不饱和度很低（＜14μ\r\neq／g），逐步聚合所得到的聚合物的分子量分布较窄（Mn／Mw＜1．4\r\n8）．13CNMR分析结果表明，甲基氧丙环均聚物的链结构具有无规立构\r\n的特点，且链节分布几乎都为头－尾方式．IR分析结果表明，甲基氧丙\r\n环－环氧乙烷共聚物的链结构是无规分布的．     

碳纳米管添加剂对质子交换膜燃料电池低铂载量膜电极性能的影响研究

以碳纳米管（CNT）作为低铂载量膜电极（CCM）催化层（0.1 mg_Pt·cm^-2）添加剂，研究了CNT的添加方式对催化层微观结构以及膜电极性能的影响.结果表明，与常规低铂载量催化层相比，在其表面喷涂一层CNT或将CNT均匀分散到Pt/C催化层中均有利于提升低铂载量膜电极的输出性能，在70℃和100%相对湿度条件下最高输出功率比常规低铂载量膜电极的0.522 W·cm^-2分别提升了22.4%和60.0%，并且均匀分散添加方式优于分层添加方式.其原因在于分层添加CNT后改善了低铂催化层和气体扩散层之间的接触界面，降低了催化层与扩散层间的接触电阻，而均匀分散添加方式除了可降低界面接触电阻外，还显著改善了低铂催化层中的气体传输，大幅提升了Pt催化剂的利用效率，使得膜电极电化学反应电阻明显降低.进一步对均匀分散添加方式中CNT的载量进行优化，表明CNT添加量为37.5 μg·cm^-2时电池输出性能最佳，70℃和100%相对湿度条件下的最大输出功率达到0.91 W·cm^-2.本研究工作表明，将CNT均匀分散添加到催化层中是一种有效提升低铂载量膜电极性能的方法.     

DFT法研究离子液中EMIM+催化丁烯双键异构反应机理(II)

用密度泛函理论(DFT)在B3LYP/6-31G(d, p)的计算水平上研究了离子液中1-乙基-3-甲基咪唑阳离子(EMIM⁺)的4-H和5-H原子催化丁烯双键异构反应的可能途径，优化了反应体系的平衡态和过渡态的几何构型，分析了反应过程中键参数的变化，通过振动分析对平衡态和过渡态进行了验证. 计算结果表明, 离子液中的EMIM⁺首先通过4-H和5-H原子吸附丁烯, 进而催化丁烯的双键异构反应, EMIM⁺的4-H和5-H催化1-丁烯异构为2-丁烯的正反应活化能分别为204.2和207.3 kJ•mol^-1，逆反应活化能约为220.9和223.8 kJ•mol^-1， 反应为基元反应.