Thermal Emulsion Polymerization without any Conventional Initiators and Emulsifiers

Stable poly(styrene-co-sodium styrene sulfonate) (P(St-NaSS) nanoparticles with broader size distribution were synthesized by thermal emulsion polymerization without any conventional initiators and emulsifiers. The obtained polymer nanoparticles have higher ξ potential, and the particle sizes have broad distribution. The stability of polymer particles originated from the addition of small amounts of ionic comonomer, NaSS, which can act as an emulsifier in somewhat. The monomer conversion could reach up to about 28 wt% in 48 h, and did not increase by further polymerization when higher polymerization temperature (120 ℃) was employed. This polymerization system may be give some further understand for mechanism of emulsion polymerization.     

(EnH2)2Ge2S6的合成与结构表征

用溶剂热方法制备了(EnH2)2Ge2S6单晶.单晶X射线衍射分析结果表明,(EnH2)2Ge2S6属单斜晶系,P2(1)/n空间群,晶胞参数a=0.67125(5)nm,b=1.12290(4)nm,c=1.07518(4)nm,β=92.288(2)°,Z=2.利用DSC及TG分析研究了其热稳定性,结果表明,该化合物在200℃以下能够稳定存在.     

含热致液晶性共聚酯的聚砜共混物

将一种含萘环的热致液晶性共聚酯与聚砜树脂熔融共混并挤塑成条。毛细管流变性测试表明，这一共聚酯降低了共混物的表观粘度，甚至低于其本身的粘度。共混物受剪切作用形成了各向异性的微纤增强结构，并具有皮芯结构，在液晶聚俣物含量低到２％与０．５％的样条中仍有共聚酯微纤形成。共聚酯微纤提高了聚砜的力学性能，含２０％共聚酯共混物挤塑条的位伸模量为聚砜树脂的二倍半。     

稀土高氯酸盐-谷氨酸配合物[Pr2(L-α-Glu)2(ClO4)(H2O)7](ClO4)3•4H2O的低温热容和热化学研究

合成了一种稀土高氯酸盐-谷氨酸配合物. 经TG/DTG、化学和元素分析、FTIR及与相关文献对比, 确定其组成为[Pr₂(L-α-Glu)₂(ClO₄)(H₂O)₇](ClO₄)₃•4H₂O, 纯度为99.0%以上. 利用显微熔点仪分析发现其没有熔点. 在78～370 K温区, 用精密绝热量热仪测量其低温热容, 在285～306 K温区发现一明显吸热峰, 归结为固-固相变过程. 通过相变温区三次重复热容测量, 得到相变温度T_tr、相变焓Δ_trH_m和相变熵Δ_trS_m分别为(297.158±0.280) K, (12.338±0.016) kJ•mol^－1和(41.520±0.156) J•K^－1•mol^－1. 用最小二乘法将非相变温区的热容对温度进行拟合, 得到了热容随温度变化的两个多项式方程. 用此方程进行数值积分, 得到每隔5 K的舒平热容值和相对于273.15 K的热力学函数值. 根据TG/DTG结果, 推测了该配合物的热分解机理. 依据Hess定律, 选择1 mol•dm^－3盐酸为量热溶剂, 利用等温环境溶解-反应量热计, 测定了该配合物的标准摩尔生成焓为: Δ_fH_m⁰＝－(7223.1±2.4) kJ•mol^－1.     

水热改性对NiMo/γ-Al2O3加氢脱氮催化剂结构及性能的影响

The influence of hydrothermal modification on the structure and hydrodenitrogenation (HDN) activity of NiMo/γ-Al₂O₃catalyst was studied in the range 140～180 ℃. The experimental results indicated that the hydrodenitrogenation reaction rate of pyridine was accelerated using the NiMo/γ-Al₂O₃catalyst synthesized via hydrothermal route due to the change of the structure, the increase of the amount of Mo and Ni and the rise of the specific surface area. The change of the structure of catalysts was enhanced at higher hydrothermal temperature, producing NiMo/γ-Al₂O₃catalyst with better HDN activity.     

以水滑石及类水滑石为前体的Mg/Al、Co/Al及Co/Mg/Al混合氧化物的合成、表征和异丙醇催化性能

以共沉淀法合成的水滑石(HT)和类水滑石(HTLc)为前体制备了镁铝、钴铝、钴镁铝混合氧化物，采用了BET、XRD、TG-DTA、TPR、FTIR和微量量热吸附及异丙醇催化反应进行了研究。结果表明：以HT和HTLc为前体制备的混合氧化物，其比表面积较大、并随着钴含量的增加而降低。在HT中引入Co²⁺离子后，由于Co²⁺离子的氧化还原属性，削弱了水滑石层对阴离子的键合能力，从而使其热分解温度及热稳定性降低，导至焙烧后生成的混合氧化物的比表面积比不含钴的2Mg/Al混合氧化物的低。在TPR过程中，镁铝混合氧化物不被还原，而含钴的混合氧化物的还原是经由Co³⁺ → Co²⁺ → Co⁰的过程。混合氧化物表面含有酸性位和碱性位，并随着钴含量的变化而得到调变。含钴氧化物样品的表面以L酸为主和含有很少量的B酸。异丙醇催化反应生成丙酮的选择性最高，表明样品表面的氧化还原位是主要的，随着钴的加入及含量的增大，异丙醇催化反应的转化率也是增大的。     

Tween-20与牛血清白蛋白的相互作用

通过表面张力和等温滴定量热方法，研究了非离子表面活性剂Tween-20与牛血清白蛋白(BSA)的相互作用. 结果表明，BSA与Tween-20的相互作用较弱，当Tween-20浓度增大时，能将吸附于表面上的BSA分子取代. BSA/Tween-20混合体系的性质随温度的变化趋势与单一非离子型表面活性剂相似. BSA浓度在3.7×10^-5～11.1×10^-5 kg•L^-1范围内，Tween-20的cmc不随BSA浓度的变化而变化. 当Tween-20的含量一定时，Tween-20与BSA相互作用过程的热效应也与BSA 的浓度无关. BSA/Tween-20混合体系的热力学参数表明， BSA的存在使Tween-20的cmc减小，体系的熵变增大.     

Et2NH2[Nd(S2CNEt2)4]的晶体结构和生成反应焓变

在干燥氮气气氛下,以无水乙醇为溶剂,制备了低水合氯化钕与二乙氨基荒酸二乙铵(D-DDC)配合物,确定其组成为Et2NH2[Nd(S2CNEt2)4].单晶结构分析表明,配合物中4个二乙氨基荒酸根各通过2个硫原子与钕离子成键形成八配位十二面体阴离子,并与二乙铵阳离子形成缔合型分子.晶体属单斜晶系,空间群P21/n,a=1.37517(14)nm,b=2.1146(2)nm,c=1.44641(15)nm,β=102.028(2)°,Z=4.用微量热法测定了298.15K下水合氯化钕和D-DDC在无水乙醇中的溶解焓及二乙氨基荒酸钕液相生成反应焓变分别为(-17.89±0.096),(50.280±0.151)和(-10.116±0.065)kJ/mol,求得固相生成反应焓变.     

微量热法研究γ-Mo2N催化剂表面氢的微分吸附热

Differential heats of H 2 adsorption on γ-Mo2N catalysts were studied by using microcalorimetry. Samples with high and medium surface areas (90 and 17 m2•g -1 ) present a homogeneous energetic distribution of surface sites, which corresponds with the preferential orientation of their (200) planes. Molybdenum nitride with low surface area (8 m2•g -1 ) displays a heterogeneous energetic distribution of H 2 adsorption sites. The higher initial differential heat of hydrogen adsorption observed for the low surface Mo nitride was attributed to species adsorbed on surface sites associated with the (111) plane.     

大庆渣油族组分非等温热反应的研究

采用动态热重分析法在升温速率为６．２Ｋ·ｍｉｎ￣（－１）及惰性气流量１００ｃｍ￣３·ｍｉｎ￣（－１）的条件下，对大庆渣油族组分的热转化行为进行了考察，获得了族组分的热转化速率峰值、速率峰值处的反应温度、转化率和剧裂分解温度区间等动力学基本数据以及各族组分的生焦性能。数据分析表明，族组分的热反应活性顺序为：饱和分＞胶质＞芳香分＞沥青质。在大庆渣油族组分热转化的两个温区内，采用分段一级动力学模型较好地拟合了实验数据，确定了各族组分在两个温区内的热反应动力学参数。