稀土纳米复合氧化物RE2O3：Eu（RE=Y，Gd）的制备及特性

以甘氨酸辅助的燃烧法和非晶态稀土DTPA配合物前驱体热分解法制备了Y2O3:Eu和Gd2O3:Eu纳米材料。X射线衍射表明燃烧法和配合物前驱体热分解法制备的纳米Y2O3：Eu均为立方相,而GdO3:Eu纳米材料则随制备条件不同可得到立方相或单斜相两种产物,发射光谱证实了这一结论。通过透射电子显微镜、扫描电子显微镜对不同方法制备的纳米材料的尺寸、形貌也进行了表征。     

Ca2Y8（SiO4）6O2：RE（RE=Eu,Tb）发光薄膜的制备及发光性能的研究

采用溶胶－凝胶法制备了稀土离子掺杂（Eu^3 ,Tb^3 )的氧磷灰石三元稀土硅酸盐Ca2Y8(SiO4)6O2发光薄膜。通过X射线衍射（XRD）,红外光谱（IR）,扫描电镜（SEM）等方法对薄膜的组成、结构、颗粒尺寸、形貌及厚度进行了研究,通过发光光谱对薄膜的发光性质进行了分析。XRD结果表明700℃时薄膜尚处于非晶态,800℃时已开始有Ca2Y8(SiO4)6O2的物相形成,1000℃时结晶已完全。这一点和红外光谱的结果相符。发光光谱测试表明Ca2Y8(SiO4)6O2:Eu^3 薄膜显示了很强的红光发射,并以Eu^3＋的^5D0-^7F2(616nm)超灵敏跃迁为最强一组。Ca2Y8(SiO4)6O2:Tb^3 的发射光谱由蓝光发射和绿光发射两部分组成,前者对应于^5D3-^7FJ,后者对应于^5D4-^7FJ(J=6,5,4,3),且以^5D4-^7F5(544nm)绿光发射为最强。     

Ce1—xM′xCa0.2O1.8—0.4x（M=Y,La和Gd）的水热合成及离子导电性质研究

采用水热法合成了系列双掺杂的萤石结构Ce1-xLnxCa0.2O1.8-0.4x固溶体,并研究了3种稀土离子对固溶体导电性的影响,发现掺杂离子半径接近Ce^4 时,体系电导率增大而活化能降低,同时发现水热合成的Ce1-xLnxCa0.2O1.8-0.4x样品的平均粒度按着掺入离子Y^3 ,Gd^3 ,La^3 的顺序逐渐减小,分别为32,20和15nm,这种变化是由于Y^3 半径比La^3 和G ^3 更接近Ce^4 ,因而在水热合成过程中, 掺Y^3 的体系更有利于晶粒的生长,得到的晶体粒度较大。     

多检测GPC/SEC技术在高分子表征中的应用—聚(α-甲基苯乙烯-异戊二烯)二嵌段共聚物的溶液性质

采用体积排斥色谱法 (SEC) /示差折光指数 (RI) /直角激光光散射 (RALLS) /示差粘度 (DV )三检测联用技术 ,在THF为溶剂、2 5℃的条件下表征了聚 (α 甲基苯乙烯 异戊二烯 ) (PαMS PI)二嵌段共聚物 ;计算得到了PαMS PI分子的无扰尺寸A为 0 .0 778nm·mol1/ 2 ·g-1/ 2 ;根据PαMS PI与PS分子的无扰尺寸A ,比较了两者在 2 5℃、THF溶剂体系中的链柔性程度 ,证明在此体系中PαMS PI与PS的链柔性程度相当 ;验证了PαMS PI符合普适标定规律     

混合配体的铜(Ⅱ)配合［Cu(C2H4O2N)(C12H8N2)(H2O)］.ClO4.2.5H2O的合成、性质及晶体结构

本文对甘氨酸、1,10 -邻菲咯啉铜 ( )固体配合物进行了合成和表征 ,并利用 X射线分析研究了其晶体结构     

复盐K3Na(SO4)2的热化学研究

钾芒硝是一种成因复杂的复盐[1～ 3 ] ,并且由于钾芒硝Ｋ3 Ｎａ(ＳＯ4 ) 2 与硫酸钾石 [Ｋ3 Ｎａ(ＳＯ4 ) 2 或Ｎａ2 ＳＯ4 ·3Ｋ2 ＳＯ4 ]的化学组成相同 ,未能确定二者是否属于同一种复盐[4 ,5] 。我们合成了复盐Ｋ3 Ｎａ(ＳＯ4 )2[3 ] ,用溶解量热法测定了Ｋ3 Ｎａ(ＳＯ4 )2 和反应物 [Ｎａ2 ＳＯ4 (ｓ) +Ｋ2 ＳＯ4 (ｓ) ]的溶解焓 ,通过设计热化学循环计算出复盐的标准生成焓 ,为我们了解钾芒硝和硫酸钾石是否为同一复盐 ,并为进一步研究其成因和组成提供参考。1　实验部分1 1　试剂与仪器Ｋ2 ＳＯ4 (ｓ)和Ｎａ2 ＳＯ4 (ｓ)为Ａ .Ｒ .…     

Synthesis and characterization of gallium-based perovskitetype dense membrane with oxygen semipermeability

La0.15Sr0.85Ga0.3Fe0.7O3-δ(LSGFO) and La0.15Sr0.85Co0.3Fe0.7O3-δ(LSCFO) mixed oxygen-ion and electron conducting oxides were synthesized by using a combined EDTA and citrate complexing method, and the corresponding dense membranes were fabricated. The properties of the oxide powders and membranes were characterized with combined SEM, XRD, H2-TPR, O2-TPD techniques, mechanical strength and oxygen permeation measurement. The results showed that LSGFO had much higher thermochemical stability than LSCFO due to the higher valence stability of Ga3+. After the temperature-programmed reduction by 5% H2 in Ar from 20℃to 1020℃, the basic perovskite structure of LSGFO was successfully preserved. LSGFO also favors the oxygen vacancy formation better than LSCFO. Oxygen permeation measurement demonstrated that LSGFO had higher oxygen permeation flux than LSCFO, but they had similar activation energy for oxygen transportation, with a value of 110 and 117 kJ ?mol~(-1), respectively. The difference in oxygen permeation f     

N,N(-双(邻甲苯基)-3,6-二甲基-1,4-二氢-S-四嗪-1,4-二甲酰胺的晶体结构

邻甲苯基异腈酸酯与3,6-二甲基-1,6-二氢-S-四嗪在催化剂4-二甲胺基吡啶存在下反应,生成标题化合物( C20H22N6O2, Mr = 378.43 )。经X-射线单晶结构分析表明此晶体属单斜晶系,P21/c空间群,a = 11.151(4),b = 15.318(2),c = 11.352(2)?,β=103.85(2)°,V = 1882.7? 3,Z = 4,μ= 0.093mm-1,Dc = 1.413g/cm3,F(000) = 800。结果表明,该化合物的两个酰胺基处于S-四嗪环的1,4位,而四嗪环本身呈船式构象。     

环丙烷衍生物在CD3OD离子体系中的H/D交换反应

研究了环丙烷衍物生物在CD3OD离子体系中的H/D交换反应产物离子[M 1]^*,[M 2]^ 和[M 3]^*的碰撞诱民碎裂(CID)反应特征,实验结果表明这些产物离子是由反应物与试剂离子之间生H/D交换反应生成的,获得了环丙烷衍生物结构中活泼氢位置及其数量的信息.     

罗丹明B—I3^—离子缔合物共振散射测定环境水样中的铬（Ⅵ）和铬（Ⅲ）

研究在磷酸介质中,罗丹明B与I3^-的离子缔合物的共振散射光谱。确定了散射光强度与溶液中Cr(VI)浓度的关系。提出了共振散射测定Cr(VI)的新方法,方法的检出限为2．2ug/L,线性范围为10．0－500ug/L,结合离子交换分离法,用于环境水样中铬的形态分析,结果满意。